Relationships between molecular weighth properties and physical properties of Petkim hdpe homopolymer petilen yy so464 and determination of its ideal...
Başlık çevirisi mevcut değil.
- Tez No: 50585
- Danışmanlar: PROF.DR. HÜSEYİN ANIL
- Tez Türü: Doktora
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Fiziksel özellikler, Polietilen, Polimerler, Physical properties, Polyethylene, Polymers
- Yıl: 1996
- Dil: İngilizce
- Üniversite: Ege Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ABSTRACT Purpose of this study is to determine the relationships between molecular weight properties and physical properties of PETKİM HDPE homopolymer PETİLEN YY S0464, and using these relationships and melt flow rate range defined for PETİLEN YY S0464 to determine its ideal molecular weight and physical properties. ABSTRAKT Bu çalışma, PETKİM Petrokimya Holding A.Ş. Aliağa Yüksek Yoğunluklu Polietilen Fabrikası'nda üretilmekte olan, yüksek yoğunluklu polietilen homopolimeri PETİLEN YY S0464 türünün molekül ağırlığı özellikleriyle fiziksel özellikleri arasındaki ilişkisini belirlemek, bu ilişkileri ve söz konusu tür için tanımlanmış olan erime akış hızı aralığını dikkate alarak, ideal molekül ağırlığı ve fiziksel özelliklerini tesbit etmek amacıyla yapılmıştır. II
Özet (Çeviri)
SUMMARY Purpose of this study is to determine the relationships between molecular weight properties and physical properties of PETKIM HDPE homopolymer PETILEN YY S0464 and its ideal molecular weight and physical properties. Two type HDPE homopolymers which had different molecular weights and physical properties produced in two reactors operated under the specified conditions were blended in the specified ratios (0%, 25%, 50%, 75%, 100%) to prepare seven samples. Seven sample molecular weight properties (Mg^/M^ Mz/Mw, Mz+1, Mp, Mn, %, Mz, Mv, dispersity, intrinsic viscosity) were determined by using gel permeation chromatography and their physical properties (Melt flow rate, density, Izod impact strength, Olsen stiffness, tensile strength at yield point, tensile strength and elongation at break point, Nonnewtonian index, environmental stress cracking resistance, melting point, Vicat softening point) were determined according to ASTM. Then, to determine relationships between above mentioned properties, graphics were prepared. Using these graphics and melt flow rate range defined for PETILEN YY S0464, ideal molecular weight properties and physical properties for PETILEN YY S0464 were determined. 74
Benzer Tezler
- Biyolojik degradasyondan kağıt hamuru endüstrisinde yararlanma
Başlık çevirisi yok
M. KEMAL YALINKILIÇ
Doktora
Türkçe
1990
Ormancılık ve Orman MühendisliğiKaradeniz Teknik ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAHİN BOSTANCI
- Yeni bir inşaat malzemesi olarak geotekstiller
Geotextiles as a new construction material
Y.OKAN CİNDEMİR
Yüksek Lisans
Türkçe
1997
İnşaat Mühendisliğiİstanbul Teknik ÜniversitesiGeoteknik Mühendisliği Ana Bilim Dalı
PROF. DR. REMZİ ÜLKER
- Değişik yükleme durumlarında polipropilen gerilme gevşemesine bağlı olarak viskoelastik davranışının incelenmesi
Başlık çevirisi yok
SEMİH ATAÇ
Yüksek Lisans
Türkçe
1998
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. SELMA AKKURT
- Gördes klinoptilolit rezervinin NH4+ değişimi ve CO2 adsorbsiyonu yardımıyla karakterizasyonu
Başlık çevirisi yok
MAYK MIGIRDİÇ DİNDİSYAN
- Hemodiyaliz amaçlı poliakrilonitril membranlar hazırlanması
Preparation of polyacrylonitrile membranes for hemodialysis application
GAMZE BEHMENYAR
Yüksek Lisans
Türkçe
1997
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. BİRGÜL TANTEKİN (ERSOLMAZ)