TiZr alaşımının toz metalurjisiyle üretimi ve biyouyumluluk özelliğinin incelenmesi
Investigation of biocompatibility property and production of TiZr alloys by powder metallurgy
- Tez No: 504339
- Danışmanlar: DOÇ. DR. MEHMET KAYA
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Ortopedi ve Travmatoloji, Metallurgical Engineering, Orthopedics and Traumatology
- Anahtar Kelimeler: Toz metalurjisi, geleneksel sinterleme, biyomalzeme, biyouyumluluk, Powder metallurgy, conventional sintering, biomaterial, biocompatibility
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Adıyaman Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, TiZr alaşımı toz metalurjisi (TM) yöntemlerinden geleneksel sinterleme ile farklı gözenek oranlarında üretildi. Üretilen numunelerin optik görüntüleri, SEM-EDX görüntü analizleri, XRD desen analizleri, basma dayanımları ve in vivo ortamda biyouyumlulukları incelendi. Üretim yapılırken, atomik olarak Ti-20Zr element tozları dönen bir kap içerisinde toz karışımlarının homojen olması için 12 saat süreyle karıştırıldı ve sonrasında gözenek oluşturmak için amonyum bikarbonat ile karıştırılarak farklı basınçlarda briketlendi. Briketlenen ham numuneler daha sonra farklı sıcaklıklarda iki saat süreyle argon gazı korumalı bir fırın içerisinde sinterlendi. Böylece % 3.17 ile % 40.40 aralığında gözenekliliğe sahip numuneler üretildi. Sinterleme sıcaklığı ve soğuk presleme basıncının artması ile gözenek oranlarının azaldığı görüldü. Üretilen numunelerin SEM-EDX ve XRD analizlerinde yapının α (hcp) fazıdan meydana geldiği, üretilen numunelerden gözenek oranının azalması ile basma dayanımlarının arttığı ve kemiğin basma dayanımından daha fazla olduğu belirlendi. İn vivo ortamda yapılan biyouyumluluk çalışmasında gözenek oranının artması ile yeni kemik ve fibröz doku oluşumunun iyi olduğu, ayrıca herhangi bir doku nekrozunun olmadığı anlaşıldı.
Özet (Çeviri)
In this study, TiZr alloy was produced as different porosities by conventional sintering from powder metallurgy (TM) methods. Optical images, SEM-EDX image analysis, XRD pattern analysis, compression strengths of produced samples and their biocompatibility in vivo were investigated. Ti-at%20Zr element pouders were mixed in a rotating vessel for 12 hours to obtain homogeneous mixtures before production. Later, powder mixture was mixed with ammonium bicorbonate to from pores structure, and then the mixture was briquette at different pressures.Finally the briquetted raw samples were sintered in an argon gas-protected oven at different temperatures for two hours. Thus, porous samples with porosity ranging from 3.17% to 40.40% were obtained. It was observed that the porosity decreases with increasing sintering temperature and cold pressing pressure. In the SEM-EDX and XRD analyzes of the produced samples, α (hcp) phase was seen and it was determined that compressive strength of samples increased with decreasing porosity, and also it was understood that the compressive strengthes of the produced samples were higher than that of bone. In the biocompatibility study performed in the in vivo environment, ıt was understood that the formation of new bone and fibrous tissue were good, and tissue necroses were not occurred.
Benzer Tezler
- Toz metalurjisi ile üretilen TZM alaşımlarının karakterizasyonu ve aşınma performansının incelenmesi
An investigation of characterization and wear performance of TZM alloys produced by powder metallurgy
HAKTAN SIRALI
Yüksek Lisans
Türkçe
2018
Mühendislik BilimleriKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
PROF. DR. DURSUN ÖZYÜREK
- TiC ve ZrC ilaveli TZM kompozitlerinin spark plazma sinterleme (SPS) yöntemi ile üretimi ve karakterizasyonu
Production and characterization of TZM based TiC or ZrC reinforced composites prepared by spark plasma sintering (SPS)
CANSİNEM TÜZEMEN
Yüksek Lisans
Türkçe
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLTEKİN GÖLLER
- Development of rare earth-free negative electrode materials for NiMH batteries
NiMH bataryalar için nadir toprak elementi içermeyen negatif elektrotların geliştirilmesi
EZGİ ONUR ŞAHİN
Yüksek Lisans
İngilizce
2016
EnerjiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. TAYFUR ÖZTÜRK
- Mekanik alaşımlama ve basınçsız sinterleme yöntemleri ile WNbMoVAlxCry (x, y = 0 – 1,0) refrakter yüksek entropi alaşımlarının sentezlenmesi ve ilişkin karakterizasyon çalışmaları
Synthesis and related characterization investigations of WNbMoVAlxCry (x, y = 0 – 1,0) refractory high entropy alloys by mechanical alloying and pressureless sintering methods
CEM ÇİÇEK
Yüksek Lisans
Türkçe
2022
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LUTFİ ÖVEÇOĞLU
- TZM alaşımının spark plazma sinterleme (SPS) yöntemi ile üretimi ve karakterizasyonu
Production and characterization of TZM alloys prepared by spark plasma sintering (SPS)
CAN BURAK DANIŞMAN
Yüksek Lisans
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLTEKİN GÖLLER