Farklı kaplama teknikleri ile kaplanmış duşlu masa rollerinin yüksek sıcaklık aşınma korozyon davranışlarının incelenmesi
The investigation of high temperature wear corrosion behaviors of shower table rolls covered by different coating techniques
- Tez No: 501876
- Danışmanlar: YRD. DOÇ. DR. ALİ GÜNEN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Demir çelik endüstrisi, Iron steel industry
- Yıl: 2017
- Dil: Türkçe
- Üniversite: İskenderun Teknik Üniversitesi
- Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: İleri Metalurji ve Malzeme Teknolojileri Mühendisliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Demir çelik sektörü Türkiye ve bölgemiz (İskenderun-Payas-Osmaniye) açısından büyük önem arz etmektedir. Bu çalışmada demir çelik endüstrisindeki sıcak haddeleme kademesinin önemli bir kısmı olan duşlu masa rollerinin mevcut alev sprey kaplama hallerine alternatif olarak difüzyonel kaplama yöntemleri (TiC kaplama, borlama, boro-titanyumlama) ile kaplanabilirliği çalışılmıştır. Kaplama işlemi sonrası numuneler optik, SEM, EDS, XRD, tabaka kalınlığı, mikrosertlik ve yüzey pürüzlülüğü incelenerek elde edilen kaplamaların karakteristik özellikleri ortaya konmuştur. Ardından duşlu masa rollerinin çalışma koşulları gözönünde bulundurularak 4 farklı kaplama tabakası yüksek sıcaklık aşınma ve %3,5 NaCl çözeltisinde elektrokimyasal korozyon testine tabi tutulmuş ve yüzeylerin SEM ve EDS analizleri ile incelenerek birbirleriyle ve işlemsiz STKM-13A çeliği ile kıyaslanmıştır. Kaplama tekniklerine bağlı olarak ile 5- 1300 µm kaplama kalınlığı ve 851-3179 HV sertlik değerlerine sahip geniş bir aralıkta kaplama tabakaları elde edilmiştir. Yapılan kaplama işlemleri ile STKM-13A çeliğinin aşınma ve korozyon dirençlerinde iyileşme sağlanmıştır. Kaplanmış numuneler arasında en iyi aşınma direnci boro-titanyumlanmış numunede, en iyi korozyon direnci ise alev sprey ile kaplanmış numunede elde edilmiştir. Tez çalışması sonuçları göstermiştir ki: Duşlu masa rollerinin aşınma direnci ve korozyon dirençleri iyileştirilerek, takım ömrünün artırılması yoluyla demir çelik endüstrisinde ortaya çıkan haddeleme maliyetlerinin azaltılması ve işletmelerdeki plansız duruşların minimize edilmesinde katkı sağlayacağı öngörülmektedir.
Özet (Çeviri)
The iron and steel sector is of great importance in both Turkey and our province (Iskenderun-Payas-Osmaniye). In this study, it has been tried to coat the cooling bed roles, which is an important part of the hot rolling stage of the iron and steel industry, with diffusion coating methods (TiC coating, boron, boron-titanium) as an alternative to existing flame spray coatings. Samples after coating the optical properties, SEM, EDS, XRD, layer thickness, microhardness and surface roughness of the coatings have been determined. Then, considering the working conditions of shower table roles, 4 different coating layers were subjected to high temperature abrasion and electrochemical corrosion test in 3.5% NaCl solution, and the surfaces were examined by SEM and EDS analyzes and compared with each other and with untreated STKM-13A steel. Based used different coating techniques, a wide range of coating layers with a coating thickness of 5 - 1300 μm and hardness values of 851 - 3179 HV were obtained. Improvement of wear and corrosion resistance of STKM-13A steel has been achieved by the coating processes. The best wear resistance among the coated specimens was obtained with the boro-titanium specimen and the best corrosion resistance was obtained with the flame spray coated specimen. The results of the thesis study showed that: Improving the wear resistance and corrosion resistance of the external cooling roller is expected to increase the tool life and reduce the rolling costs of the iron and steel industry and minimize the unplanned stances in the enterprises.
Benzer Tezler
- Peo ve daldırma kaplama(dip coating) ile dubleks kaplanmış Cp-titanyumun korozyon davranışının incelenmesi
The investiagtion of corrosion behaviour of dublex coating on Cp-titanium by using combined plasma electrolytic oxidation and sol-gel dip coating methods
NESLİHAN BAŞTEPE
Yüksek Lisans
Türkçe
2022
Makine MühendisliğiAtatürk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. YAŞAR TOTİK
- ZnNiMo alaşımı kaplanmış bakır yüzeyine sentezlenen polianilin ve poli(o-Anisidin) homopolimer filmlerinin sentez koşullarının yanıt yüzey yöntemi ile optimizasyonu
The optimization of synthesis conditions of polyaniline and poly(o-Anisidine) homopolymer films synthesized on ZnNiMo alloy coated copper surface by response surface methodology
İBRAHİM FİLAZİ
Yüksek Lisans
Türkçe
2018
Polimer Bilim ve TeknolojisiHatay Mustafa Kemal ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. ALİ TUNCAY ÖZYILMAZ
- Termoreaktif difüzyon tekniği ile kaplanmış nitrasyon çeliğinin mekanik özelliklerinin araştırılması
Investigation of mechanical properties of nitriding steel coated with thermoreactive diffusion technique
MUZAFFER KARAGÖZ
Doktora
Türkçe
2021
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MUSTAFA ULUTAN
- Development of multifunctionally coated zinc oxide powders and evaluation of their solubility behavior and uv-filtering performance
Multifonksiyonel kaplanmış çinko oksit tozlarının geliştirilmesi ve çözünürlük davranışları ile uv-filtreleme performansının incelenmesi
HAKAN KAYA
Doktora
İngilizce
2026
KimyaEskişehir Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. YASEMİN ÇELİK
- Development of stretchable conductive fabric through different metals coating approach for e-textile applications
E-tekstil uygulamaları için farklı metal kaplama yaklaşımıyla uzayabilir iletken kumaş geliştirilmesi
ZUHAIB HASSAN
Doktora
İngilizce
2022
Tekstil ve Tekstil Mühendisliğiİstanbul Teknik ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. FATMA KALAOĞLU