Polikarbazol ve türevlerinin grafen ile nanokompozit sentezleri, karakterizasyonları ve kapasitör davranışları
Nanocomposite synthesis of polycarbazole and its derivatives with graphene, characterization and capacitor behaviours
- Tez No: 495029
- Danışmanlar: PROF. DR. MURAT ATEŞ
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Karbazol, iletken polimer, süperkapasitör, grafen, empedans spektroskopisi, nanokompozit, Carbazole, conducting polymers, supercapacitors, grahene, impedance spectroscopy, nanocomposites
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Namık Kemal Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tezin amaçları arasında Karbazol ve türevlerinin monomerlerinin (karbazol (Cz), metilkarbazol (MCz), vinilkarbazol (VCz)) Grafen (GN) ile kompozitleri ((PCz/GN, PCz/nanokil/GN), (PMCz/GN), (PCz/Zn/GN), (PVCz/nanokil/GN)) sentezlenmesidir. Elde edilen nanokompozitlerin karakterizasyonları DV, FTIR-ATR, SEM-EDX, EES gibi yöntemlerle gerçekleştirildi. İkili elektrot kullanılarak süperkapasitör hazırlandı. rGO/nanokil/PCz nanokompoziti için DV metoduna göre Csp= 187.78 F/g elde edilirken, rGO/PCz nanokompoziti için EES sonuçlarına göre spesifik kapasitans Csp= 256.10 F/g elde edilmiştir. PMCz/rGO nanokompoziti için Csp= 31.09 F/g DV metodu ile 0.1 V/s tarama hızında elde edilmiştir. rGO/nanokil/PVK nanokompoziti için 10 mV/s tarama hızında Csp= 168.64 F/g elde edilmiştir. rGO/Zn/PCz nanokompoziti için yine 10 mV/s tarama hızında Csp= 33.88 F/g elde edilmiştir. Ayrıca, galvanostatik yükleme/boşalma ölçümleri ve elektrokimyasal empedans spektroskopi metodlarıyla herbir nanokompozitin elektrkimyasal performans sonuçları karşılaştırılmıştır.
Özet (Çeviri)
The aim of this thesis is to synthesize carbazole based derivatives of monomers such as carbazole (Cz), methylcarbazole (MCz), vinylcarbazole (VCz), graphene (GN) and their nanocomposites (PCz/GN, PCz/nanoclay/GN, PMCz/GN, PCz/Zn/GN and PVK/nanoclay/GN were studied in thesis. The characterizations of obtained nanocomposites were taken by FTIR-ATR, SEM-EDX, and EIS. Two electrode systems were used for supercapacitor devices. As a result, according to CV method results of rGO/nanoclay/PCz, the highest Csp was obtained as Csp= 187.78 F/g and Csp= 256.10 F/g for EIS results. For PMCz/rGO nanocomposite, the Csp value was obtained as Csp= 31.09 F/g by CV method at 0.1 V/s. Moreover, for rGO/nanoclay/PVK nanocomposite, the highest Csp was obtained as Csp= 168.64 F/g at 10 mV/s. In addition, the highest Csp was obtained as Csp= 33.88 F/g at 10 mV/s. In addition, galvanostatic charge/discharge measurements and electrochemical impedance spectroscopic methods were compared as electrochemical performances of each nanocomposite materials.
Benzer Tezler
- The investigation of electrochemical and spectroelectrochemical behaviour of carbazole and some carbazole derivatives
Karbazol ve bazı karbazol türevlerinin, elektrokimyasal ve spektroelektrokimyasal davranışlarının incelemesi
HASSAN ELAMİN ELKHIDR ATTA
- Chemical and electrochemical polymerisation of substituted carbozoles in the presence of acrylamide
Sübstitüye karbozollerin akrilamid varlığında kimyasal ve elektrokimyasal polimerizasyonu
ÖZLEM YAVUZ
- Photochemical strategies for macromolecular syntheses
Makromoleküler sentezler için fotokimyasal yöntemler
ALİ GÖRKEM YILMAZ
- Polikarbazol/polipirolün kompozit materyallerinin elektrokimyasal eldesi ve karakterizasyonu
Electropolimerization and characterization of polypyrrole /polycarbazole composite materals
ELİF KAYASAN
- Polikarbazol/Kitosan iletken kompozitlerinin elektrokimyasal sentezi ve karakterizasyonu
Electrochemical synthesis and characterization of Polycarbazole/Chitosan conductive composites
VEYSEL POLAT