Restorasyon kalınlığının ve rezin simanın monolitik zirkonyumun renk ve translüsensliğine etkisinin incelenmesi
Investigation of effect of restoration thickness and cement on color and translucency of monolithic zirconia ceramics
- Tez No: 484908
- Danışmanlar: PROF. DR. FUNDA BAYINDIR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Monolitik zirkonya, renk, rezin siman, translüsensi, Akrilik reçineler, Dental porselen, Dental restorasyon, Dental çimentolar, Diş renk değişikliği, Kompozit reçineler, Reçineler-yapay, Zirkonyum, Çok renkli seramik, Color, monolithic zirconia, resin cement, translucency, Acrylic resins, Dental porcelain, Dental restoration, Dental cements, Tooth discoloration, Composite resins, Resins-synthetic, Zirconium, Multicolor ceramic
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç:Bu çalışmanın amacı, farklı rezin simanın ve farklı materyal kalınlıklarının monolitik zirkonyanın renk ve translüsensliğine etkisinin incelenmesidir. Materyal ve Metod: Monolitik zirkonya materyali olarak Katana High Translucent (Kuraray Noritake Dental, Kurashiki, Japonya) kullanılmıştır. 1 cm çapında, disk şeklinde, toplam 80 adet örnek üretilmiştir. Örnekler, 0,5 mm, 1 mm, 1,5 mm ve 2 mm olmak üzere dört farklı kalınlıklarda hazırlanmıştır. Örneklerin simantasyondan önce ve sonra renk ölçümleri spektrofotometre( SpectroShade MICRO; MHT Opic Research AG, Milan, İtalya) cihazı ile yapılmıştır. Örneklere şeffaf ve opak renkte self- etch adeziv rezin siman (Panavia V5, Kuraray Noritake dental, Kurashiki, Japonya) uygulanmıştır.Çalışmadan elde edilen veriler, tanımlayıcı istatistikler, korelasyon analizi, tek örneklem t testi, çift yönlü ANOVA ve Tukey testi ile değerlendirilmiştir. Bulgular: Monolitik zirkonyanın kalınlığının artmasıyla Translüsensi Parametresi (TP), L*, a*, b* değerleri artmış, TP değerleri azalmıştır ve bu değişimler istatistiksel olarak anlamlı bulunmuştur(p<0,001). Şeffaf ve opak siman grubunda, simantasyonla birlikte L*,a*,b* değerleri artmış, TP değerleri azalmıştır ve bu değişimler istatistiksel olarak anlamlı bulunmuştur(p<0,001). En fazla renk değişim, 0,5 mm kalınlığındaki örneklerde opak simanda görülürken,en az renk değişimi 2 mm kalınlığında şeffaf siman kullanılan örneklerde görülmüştür. Sonuç: Materyalin klaınlığı ve kullanılan simanın rengi monolitik zirkonyumun renk ve translüsensliğini etkilemektedir.
Özet (Çeviri)
Aim:The aim of this study was evaluation of the effects of different cemant shades and different material thicknesses on the color and translucency of monolithic zirconia. Material and Method: A monolithic zirconia materail, Katana High Translucent (Kuraray Noritake Dental, Kurashiki, Japan) was used n the present study. A total of 80 pecimens, 1 cm in diameter and sisc shape, were produced. Samples were prepared in four thicknesses: 0,5 mm, 1 mm, 1,5 mm and 2 mm. Color measurements of the samples prior to cementaion and after cementation were measured with a spectrophotometer(SPectroshade MICRO; MHT Optic Research AG,Milan, Italy). Self-etch adhesive resin cement (Panavia V5, Kuraray Noritake Dental, Kurashiki, Japan) was applied in clear shade and opaque shade. Despcriptive statistics, correlation analysis, one sample t test, two way ANOVA and Tukey test were used to evaluate the data obtained from the study. Results: Thickness of the material affected Translucency Parameter (TP), L*,a* and b* values. TP, L* and b* values decreased and a* values increased with increasing monolithic zirconia thickness and these changes were statistically significant (p<0,001). L*,a*,b* values were increased and TP values were decreased in both clear and opaque cement groups (p<0,001).The maximum color change was observed in opaque shade cement with a thickness of 0,5 mm; and the least color change was seen in clear shade cement with a thickness of 2 mm. Conclusion:The thickness of the material and cement shade affects color and translucency of the monolithic zirconium.
Benzer Tezler
- Monolitik zirkonya materyalinde kalınlığın, rengin ve simanın sonuç restorasyonun renk parametreleri üzerine etkisi
Effect of monolithic zirconia thickness and resin cementcolor on the color parameters of final restoration
AYLİN DOĞAN
Doktora
Türkçe
2019
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. CEMAL AYDIN
- Farklı rezin simanların tam seramik restorasyonların rengi üzerindeki etkisinin incelenmesi
Investigation of effect of different resin cements on the color of all ceramic restorations
SERTAÇ BAYRAK
Doktora
Türkçe
2018
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MUSTAFA KOCACIKLI
- Zirkonya ile güçlendirilmiş lityum silikat cam seramik kalınlığının ışıkla polimerize rezin simanın polimerizasyon dönüşüm derecesine etkisinin değerlendirilmesi
Evaluating the effect of zirconia reinforced lithium silicate glass ceramic thickness on the degree of conversion of LIGHT-cured resin cement
GÜLEN DAL
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiKütahya Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BANU ÇUKURLUÖZ BAYINDIR
- Farklı marka ve kalınlıktaki monolitik zirkonya materyalleri kullanılarak üretilmiş inley destekli köprülerin kırılma direncinin in vitro olarak incelenmesi
In vitro investigation of the breaking resistance of inley supported bridges produced by using monolithic zirconia materials in different brand and thickness
BURAK AĞAR
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FİLİZ KEYF
- Monolitik restorasyonlarda kalınlığın ve simanın final renk ve translusensi üzerine etkisi
The effect of thickness and luting cement on final shade andtranslucency on monolithic restorations
EMİNE GÜRSOY TÜRER
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SERDAR POLAT