Investigation on properties of wood plastic composite made of treated wood flour with tanalith e and poly lactic acid (pla)
Tanalith-e ile muamele edilmiş odun unundan ve polilaktik asitten (pla) yapilan odun plastik kompozitlerinin özelliklerinin incelenmesi
- Tez No: 467974
- Danışmanlar: PROF. DR. ALİ TEMİZ
- Tez Türü: Yüksek Lisans
- Konular: Ağaç İşleri, Wood Products
- Anahtar Kelimeler: FizikselveMekanik Özellikler, Polilaktik asit, Tanalith E, Termal Kararlılık, Emprenyeli odun, Mechanical and Physical Properties, Polylactic acid, Tanalith E, Thermal stability, Impregnated wood
- Yıl: 2017
- Dil: İngilizce
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı odun unu-PLA kompozitlerinin özelliklerini araştırmaktır. Odun unu-PLA kompozitleri,çift vidalı ekstruder kullanılarak Pinussylvestris L. odun ununun%30, 40 ve 50 oranlarında eklenemesiylehazırlanmış.Kompozithazırlanmadan önce odun ununun bir kısmı %3 Tanalith E ile emprenye edilmiş diğeri kısım ise emprenye edilmemiştir. Yoğunluk ve boşluk hacim fraksiyonu kompozitleri belirlenmiştir. %30 oranında muamele edilmemiş odun unu içeren kompozitlerin su alma ve kalınlığına şişme oranları diğer gruplara göre daha az çıkmıştır. %30 oranında muamele edilmemiş odun unu içeren kompozitlerin çekme ve eğilme direnci en yüksek iken %50 oranında muamele edilmemiş odun unu içeren kompozitlerin eğilme ve çekme modülü en yüksek çıkmıştır. Odun unu- PLAkompozitleri(OPK)'nintermal özellikleri termo gravimetrik analiz ve diferansiyel termal analiz kullanılarak ölçülmüştür. Termoplastik matristeki odun unu varlığı, ağırlık kaybını arttırırken kompozitlerinbozunma sıcaklığını azaltmıştır. Sonuçlar gösteriyor ki kimyasal olarak muamale edilmiş odun unu- PLA kompozitlerinin mekanik özellikleri muamele edilmemiş odun unu ile hazırlanan kompozitlere göre daha düşük çıkmıştır. Su alma testi sonuçlarına göre; kimyasal olarak muamele edilmiş odun unundan hazırlanan kompozitler muamele edilmemiş odun unu ile hazırlanan kompozitlere göre daha yüksek miktarda su almıştır. Bu gösterir ki kimyasal olarak muamele edilmiş odun ununda, bakır oduna bağlanmayı engellemiş ve muamele edilmemiş odun ununa göre daha yüksek miktarda boşluk oluşmasına neden olmuştur. Kimyasal olarak muamele edilmiş OPK yüksek boşluklar SEM'de gözlemlenmiştir. Sonuçlar açıkça gösterir ki OPK'ların özellikleri odun unu içeriğine ve odunun emprenye edilip edilmemesine bağlıdır.
Özet (Çeviri)
The purpose of this study to investigate on the properties of Wood flour -PLA composites. Wood flour -PLA composites reinforced with 30, 40, and 50% of Pinus sylvestris L. wood flour were prepared by using twin-screw extruder. Part of the wood flour was treated with 3% of Tanalith E solution before being used for the composite preparation and the other was used without treatment. The density and void volume fraction composites were determined. The composite contains 30% of untreated wood flour absorbed the least amount of water and the least thickness swelling compared to all the other formulations. The highest value of tensile and flexure modulus at 50% of untreated wood flour content while tensile and flexure strength at 30% of untreated wood flour content in composites. Thermal properties of Wood flour -PLA composites were measured using the thermo gravimetric analysis and differential thermal analysis. Presence of WF in thermoplastic matrix reduced the degradation temperature of the composites while the increased weight loss. Results indicate that the mechanical properties of the chemically treated wood flour-PLA composites were found to be lower than those of the untreated. The water absorption test showed that composite prepared from the chemically treated wood flour absorbed higher amount of water compared to the untreated wood flour composite. This indicate the copper partly inhibit wood bonding and causes presence of high content of voids in the chemical treated wood flour compared to that of untreated. High voids in the chemically treated wood was also observed SEM studies. The results clearly show that the properties of WPCs depend on the wood flour content and also the treatment given to the wood.
Benzer Tezler
- Investigation of the effect of photostabilizers on mechanical properties and surface analysis of cotton fiber reinforced LDPE composites
Foto düzenleyicilerin pamuk lifi takviyeli düşük yoğunluklu polietilen kompozit malzemelerin mekanik özelliklerine ve yüzey analizine etkisinin incelenmesi
HASRET ECE SÖNMEZ
Yüksek Lisans
İngilizce
2015
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. İBRAHİM ERSİN SERHATLI
DOÇ. DR. MUSTAFA BAKKAL
- Ahşap tozu takviyeli polipropilen (PP) esaslı kompozit malzemelerin akış ve mekanik özelliklerinin incelenmesi
Fludty and mechanical properties wood fiber reinforced polyproplyene (PP)
SALİH KAYA
Yüksek Lisans
Türkçe
2012
Makine MühendisliğiKarabük ÜniversitesiMakine Eğitimi Ana Bilim Dalı
DOÇ. DR. ABDULMECİT GÜLDAŞ
YRD. DOÇ. DR. METİN ZEYVELİ
- Yığma duvarların düzlem içi davranışlarının modellenmesi ve analizi
Analysis and modelling of the in-plane behaviour of masonry walls
SEDAT KÖMÜRCÜ
Yüksek Lisans
Türkçe
2017
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ABDULLAH GEDİKLİ
- Sandviç kompozitler ve mimarlıkta kullanım olanakları
Başlık çevirisi yok
BANU YILDIRIM
Yüksek Lisans
Türkçe
1998
Mimarlıkİstanbul Teknik ÜniversitesiMimarlık Ana Bilim Dalı
PROF. DR. NİHAT TOYDEMİR
- Ahşap plastik kompozit malzemeler için yeni auxetic yapının tasarımı ve mekanik özelliklerinin araştırılması
Design of new auxetic structure and investigation of mechanical properties for wood plastic composite materials
FULYA ERDEMİR
Doktora
Türkçe
2024
Makine MühendisliğiGazi ÜniversitesiEndüstriyel Tasarım Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT TOLGA ÖZKAN