CAD/CAM sistemi ile farklı yapı ve formdaki bloklardan üretilen tam seramik kronların mikro çatlak analizi ve kırılma dayanımlarının karşılaştırılması
Comparison of fracture strength and micro crack analysis of all ceramic CAD/CAM crowns manufactured with three blocks in different form and structure
- Tez No: 460407
- Danışmanlar: DOÇ. DR. İLGİ BARAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental materyaller, Dental porselen, Dental stres analizi, Dental sızma, Kronlar, CAD/CAM, Dental materials, Dental porcelain, Dental stress analysis, Dental leakage, Crowns
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada CAD/CAM ile üç farklı bloktan üretilen tam seramik monolitik kronların yüzeyindeki oluşan mikro çatlakların incelenmesi ve kronların kırılma dayanımlarının karşılaştırılması amaçlanmıştır. Feldspatik içerikli (Priticrown-Vita Mark II) ve lityum disilikat içerikli (EmaxCAD) materyallerden (n=30) olmak üzere aynı tasarıma sahip 90 adet kron üretilmiştir. Her grup test(n=15) ve kontrol(n=15) olmak üzere iki gruba ayrılmıştır. Test grubunda CAD/CAM ile üretildikten hemen sonra floresan penetrant yöntemiyle mikro çatlak analizi yapılmış ve Cr-Co daylara çinko fosfat simanla simante edildikten sonra 5°C-55°C arasında 5000 döngü uygulanmıştır. Termal döngünün ardından ikinci mikro çatlak incelemesi yapılmış ve kronlara universal test cihazında 0,5 mm/dk hızla kırılana kadar kuvvet uygulanmıştır. Kontrol grubundaki kronlar da CAD/CAM ile üretim işleminden sonra Cr-Co daylara çinko fosfat simanla simante edilmiş ve kırılma dayanımı testine tabi tutulmuştur. Kırık şekilleri incelendikten sonra taramalı elektron mikroskobuyla fraktografik belirteçler belirlenmeye çalışılmıştır. Mikro çatlak değerleriyle kırılma dayanımı arasındaki ilişki Spearman Korelasyon testiyle, kırılma dayanımı değerleri Kruskal Wallis H testi ve Mann Whitney U testiyle, mikro çatlak değerleri Kruskal Wallis H testi ve Wilcoxon İşaretli Sıralar testiyle değerlendirilmiştir. Mikro çatlak sayısı ile kırılma dayanımı değerleri arasında Priticrown materyalinin termal döngü uygulanmayan grubu(r=-,532) hariç istatistiksel olarak anlamlı bir ilişki bulunmamıştır(p>0.05).EmaxCAD kronların kırılma dayanımları diğer iki gruba göre termal döngüden önce ve sonra anlamlı derecede yüksek bulunmuştur(p=0.000). Termal döngünün mikro çatlak sayısı ve kırılma dayanımı üzerinde istatistiksel olarak anlamlı bir etki oluşturmadığı görülmüştür (p>0.05) ve kron formundaki blok yapısına sahip Priticrown materyalinin mikro çatlak oluşumu açısından avantaj sağlamadığı sonucuna ulaşılmıştır.
Özet (Çeviri)
This study intended to analyze micro cracks those occur on the surface of the all ceramic monolithic crowns and compare the crowns' fracture strength values. Totally 90 crowns in same design were manufactured from feldspathic (Priticrown-Vita Mark II) and lithium disilicate(EmaxCAD) blocks, each material grup had 30 crowns. Test (n=15) and control (n=15) groups were prepared for every material. In the test group the crowns were analyzed by florescence penetrant method for micro crack evaluation following the manufacturing process and after cementation onto the Cr-Co die structures with zinc-phospate cement, thermal cycling consists of 5000 cycles between 5°C-55°C was carried out. Second micro crack analysis was applied on crowns that were treated with thermal cycling and the crowns were loaded to fracture at a crosshead speed of 0.5 mm/min in a universal testing machine. The other half of the crowns in each group, after manufacturing process, were directly cemented onto the Cr-Co dies with zinc-phospate cement and loaded to fracture. After evaluating fracture modes, fractographic markings were analyzed by scanning electron microscopy. Spearman Correlation analysis was applied for detecting if there was a relation between micro crack numbers and fracture strength values. Fracture strenth values were analyzed by Kruskal Wallis H and Mann Whitney U tests, micro crack values were analyzed by Kruskal Wallis H and Wilcoxon Signed Rank tests. Except the group of Priticrown material that wasn't treated with thermal cycling(r= -,532), statistically significant relation was not found between micro crack numbers and fracture strength values(p>0.05). There was significant difference between fracture strength values of EmaxCAD crowns and other groups(p=0.000), before and after thermal cycling. Thermal cycling didn't have significant effect on micro crack numbers and fracture strength values (p>0.05) and crown shaped Priticrown blocks didn't provide advantage against micro crack formation.
Benzer Tezler
- CAD/CAM sistemi ile üretilen hibrit abutment destekli anterior restorasyonda kemik rezorpsiyon riskinin ve stres dağılımının sonlu elamanlar analizi ile incelenmesi
Investigation of bone resorption risk and stress distribution in hybrid abutment supported anterior restoration produced with CAD/CAM system by finite element analysis
CİHAN AKDOĞAN
Doktora
Türkçe
2024
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HATİCE ÖZDEMİR
- İmplant destekli sabit protezlerde CAM/CAM sistemleri ile üretilen destek ve üst yapı restorasyonlarının sonlu elemanlar stres analiz yöntemi ve kırılma direnci testi ile karşılaştırmalı olarak incelenmesi
The comparatively investigation of abutment and crown restorations produced by CAD/CAM systems in implant supported fixed prostheses using the finite element stress analysis method and fracture resistance test
NAZİRE ESRA BAĞDATLI
Doktora
Türkçe
2016
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. AHMET ERSAN ERSOY
- Hıp ve non-hıp zirkonya bloklardan cad-cam yöntemi ile üretilen kuron kopinglerinin marjinal uyumlarının karşılaştırılması
Marginal fit comparison of hip and non-hip zirconia copings with 3 different marginal finish lines fabricated with two different cad-cam systems
CUMHUR KORKMAZ
- CAD/CAM yazılımları kullanılarak eklemeli metot ile üretilen kronların marjinal ve internal uyumunun preparasyon tiplerine göre değerlendirilmesi
Evaluation of the marginal and internal fit of crowns fabricated by additive manufacturing using different CAD/CAM software according to various preparation type
GÖRKEM MÜMTAZ
Doktora
Türkçe
2025
Diş HekimliğiAltınbaş ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BERİL KOYUNCU
- Lasercusing, hızlı prototipleme ve konvansiyonel döküm teknikleri ile oluşturulan metal alt yapıların marjinal uyumlarının in vitro incelenmesi
In vitro evaluation of marginal adaptation of metal copings produced by lasercusing, rapid prototyping and conventional casting techniques
ERTUĞRUL ÇETİNKAYA
Doktora
Türkçe
2013
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ATİLLA SERTGÖZ