Güncel kompozitlerin farklı tabakalama teknikleriyle uygulanmasının mikrosızıntı üzerine etkilerinin incelenmesi
The investigation of the effects of novel composites applied with different layering techniques on microleakage
- Tez No: 458271
- Danışmanlar: YRD. DOÇ. DR. AYŞE DÜNDAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental restorasyon, Dental sızma, Kompozit reçineler, Dental materials, Dental restoration, Dental leakage, Composite resins
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Mikrosızıntı, restoratif diş hekimliğinin önemli sorunlarından biridir. Bu in vitro çalışmanın amacı, boya penetrasyon yöntemini kullanarak inkremental veya bulk-fill tekniği ile uygulanan yeni kompozit materyallerin mikrosızıntı potansiyelini değerlendirmektir. Yöntem: Yeni çekilmiş 120 adet büyük azı dişe standart Black I kaviteler (3mm x 3mm x 4mm) hazırlandı. Bir nanohybrid (Filtek™ Z550), bir bulk-fill (X-tra fil) ve bir seramik içerikli bulk-fill kompozit (Admira Fusion X-tra) test edildi. Restorasyon yöntemi olarak bulk-fill ve inkremental uygulama teknikleri kullanıldı. Örnekler rastgele 6 gruba (n = 20) ayrıldı ve restoratif prosedürlerden sonra numuneler 1000 çevrimlik termal döngüye (5ºC-55ºC) tabi tutuldu. Mikrosızıntı testi, % 1'lik metilen mavisi boyası kullanılarak uygulandı. Dişlerin kesitleri, boya penetrasyon derecesi açısından stereo mikroskop altında değerlendirildi. İstatistiksel analizler Kruskal-Wallis ve Mann-Whitney-U testleri ile gerçekleştirildi (p=0,05). Bulgular: Kompozit rezin grupları ile mikrosızıntı sonuçları arasındaki ilişki istatiksel olarak anlamlı bulunmuştur (p<0,05). En fazla mikrosızıntı değerleri X-tra fil tek tabaka (bulk) tekniğiyle uygulanan grup gösterirken, bunu iki tabaka halinde uygulanan Filtek™ Z550 grubu takip etmektedir (p<0,05). İnkremental teknikle uygulanan Admira Fusion X-tra en az mikrosızıntı göstermiştir. Filtek ™ Z550 hariç, tüm kompozitlerde iki uygulama tekniği arasında anlamlı bir fark gözlenmiştir (p<0,05). Sonuç: Admira Fusion X-tra inkremental uygulama tekniğiyle hazırlandığında en düşük mikrosızıntı değeri göstermiştir.
Özet (Çeviri)
Objective: Microleakage is one of the major problems of restorative dentistry. The aim of this in vitro study was to evaluate the microleakage potential of novel composite materials applied with either incremental or bulk fill technique using dye penetration method. Method: Standard Black I cavities were prepared (3mm x 3mm x 4 mm) to 120 freshly extracted molar teeth. A nanohybrid (Filtek™ Z550), a bulk fill (X-tra fil) and a ceramic reinforced bulk fill composite (Admira Fusion X-tra) was tested. Bulk fill and incremental application techniques were used as restoration method. Specimens were randomly separated in 6 group (n=20) and after restorative procedures, samples were thermal cycled for 1000 cycles (5ºC-55ºC). Microleakage test was applied with using %1 methylene blue dye. Sections of the teeth were evaluated under stereo microscope in terms of dye penetration degree. Statistical analyses were conducted with Kruskal-Wallis and Mann-Whitney-U tests (p=0.05). Results: The relationship between composite resin groups and microleakage degrees were statistically significant (p<0.05). The higher microleakage scores were observed in X-tra fil bulk fill group followed by Filtek™ Z550 incremental group (p<0.05). Admira Fusion X-tra with incremental application technique showed least microleakage. With exception of Filtek™ Z550, a significant difference between two layering technique was observed in all composite (p<0.05). Conclusion: Admira Fusion X-tra exhibited the lowest microleakage degree when it was prepared with incremental application techniques.
Benzer Tezler
- Farklı polimerizasyon sistemlerinin farklı tabakalama kalınlıklarında uygulanan yeni nesil bulk-fill kompozitlerin bağlanma dayanımına etkisi
The effect of different polymerization systems on bond strength of new generation bulk-fill composites applied at different layering thicknesses
TAHA BATURAY BİLİR
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiOndokuz Mayıs ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. NİHAN GÖNÜLOL
- Güncel bulk fill kompozitlerle geleneksel rezin kompozitlerin eroziv-abraziv uygulamalar sonrası yüzey özelliklerinin karşılaştırılmalı olarak incelenmesi
Comparative investigation of the surface properties of contemporary bulk fill composites and conventional resin composites after erosive-abrasive applications
LEYLA DEVLETLİ ÖZYİĞİT
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiKaradeniz Teknik ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GÜNEŞ BULUT EYÜBOĞLU
- Karbon kompozitlerin cıvatalı ve yapıştırmalı bağlantılarında hasar analizi
Failure analysis of bolted and bonded carbon composite joints
AHMET FARUK KURAR
Yüksek Lisans
Türkçe
2018
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
ÖĞR. GÖR. LEVENT KIRKAYAK
- Karışık sonlu elemanlar yöntemiyle düzlem kompozit eğri eksenli çubukların geometrik doğrusal olmayan davranışlarının analizi
Analysis of geometrically nonlinear behavior of plane composite curved rods via mixed finite element method
SEDAT KÖMÜRCÜ
Doktora
Türkçe
2023
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ALİ NURİ DOĞRUOĞLU
- Farklı solüsyonların güncel posterior kompozitlerin yüzey yapısı ve çözünürlüklerine etkisi
The effect of different solutions on the surface structure and solubility of current posterior composites
ÖZGÜN KOKOZ ÇİTAKER
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiDicle ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ELİF PINAR BAKIR