Bir nanohibrit kompozit rezinin tamirinde farklı yüzey işlemleri ve akışkan kompozit kullanılmasının pürüzlülük, mikrosızıntı ve bağlanma dayanımı yönünden incelenmesi
Evaluation of different surface treatments' and flowable composites' effects on surface roughness, microleakage and shear bond strength in repair of A nanohybrid composite resin
- Tez No: 445556
- Danışmanlar: DOÇ. DR. DİĞDEM EREN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental restorasyon, Dental restorasyon-sürekli, Dental sızma, Kompozit reçineler, Lazerler, Yüzey pürüzlülüğü, Dental bonding, Dental materials, Dental restoration, Dental restoration-permanent, Dental leakage, Composite resins, Lasers, Surface roughness
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Cumhuriyet Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Çalışmamızın amacı farklı yüzey işlemleri ve akışkan kompozitler kullanarak nanohibrit kompozit rezin için etkili bir tamir protokolü bulmaktır. Bu amaçla Filtek Z550 ile hazırlanan bloklar yüzey işlemlerine göre Grup 1 (kontrol), Grup 2(frez), Grup 3 (frezz+silan), Grup 4 (Al2O3), Grup 5 (Al2O3+silan), Grup 6 (tribokimyasal silika kaplama), Grup 7 (lazer), Grup 8 ( lazer+silan) olmak üzere ayrıldı.Profilometre ile incelenen örneklerin pürüzlülük değerleri Ra cinsinden kaydedildi. Mikrosızntı ve makaslama testleri için ayrıca örnekler hazırlandı ve yüzey işlemleri uygulandıktan sonra Filtek Z550 (Z550), G-aenial Flo (GA), Vertise Flow (VF) ile tamir görmek üzere üçer alt gruba ayrıldı. Guplar arasındaki fark ve korelasyon için Kruskal Wallis ve Spearman'ın Korelasyon testi kullanıldı. Grup 1 ve Grup 4-6 arasındaki pürüzlülük farkı istatistiksel olarak anlamlı değildir. Grup 2, Grup 3, Grup 7 ve Grup 8 bunlardan daha yüksek ve kendi aralarında benzer pürüzlülük değerleri göstermiştir. MS testinde grup ortalamaları skor 0 ''sızıntı yok'' olarak bulunmuştur. Makaslama testinde, kontrol grubuna göre en yüksek değeri Grup 6, en düşük değeri G7 ve G8 göstermiştir (p<0,05). Makaslama testinde Grup 7 VF ve Grup 8 VF en düşük, Grup 6 GA en yüksek sonuçları vermiştir. Pürüzlülük ile mikrosızıntı ve bağlanma dayanımı arasında korelasyon yoktur. Bu çalışmanın sınırları içinde, nanohibrit kompozit rezinlerin tamirinde tribokimyasal silika kaplamanın etkili yüzey işlemi olduğu söylenebilir. Sayısal pürüzlülük değerinin değil ama yüzey topografisinin bağlanma dayanımına etkisi vardır.
Özet (Çeviri)
We aimed to find an effective repair protocol for nanohybrid resin composites using different surface treatments and flowable composites. Composite blocks from Filtek Z550 were grouped as Group 1 (control), Group 2 (bur), Group 3 (bur+silane), Group 4 (Al2O3), Group 5 (Al2O3+silane), Group 6 (tribochemical silica coating), Group 7 (laser), Group 8 (laser+silane). Surface roughness values of the blocks measured by profilometer saved as Ra unit. Composite blocks were also prepared for each of the microleakage and bonding tests. Same surface treatments were applied and three subgroups according to fresh composites were set; Filtek Z550 (Z550), G-aenial Flo (GA) and Vertise Flow (VF). Kruskal Wallis and Spearman's corelation tests were used for detecting the difference and relation between groups in order. Roughness values showed no statically significant difference between Groups 1, 4-6. Higher roughness values were observed in Groups 2, 3, 7 and 8. All groups showed score 0, meant no microleakage. Shear bond test revealed Group 7 VF and Group 8 VF showed the least, Group 6 GA showed the highest values. No correlation was observed between roughness and microleakage or roughness and shear bond strength. In the limits of our study, tribochemical silica coating is good in bonding as a surface treatment. Bond strength isn't related to digital roughness values but a relation with surface topography exists.
Benzer Tezler
- Self cured universal adezivin farklı yüzey işlemleri sonrası tamir bağlanma dayanımının incelenmesi
Investigation of repair bond strength of A self-cured universal adhesive after different surface treatment
ECEM DOĞAN
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BEGÜM BÜŞRA CEVVAL ÖZKOÇAK
- Kompozit tamirinde farklı yüzey hazırlama yöntemlerinin ve yaşlandırma sürelerinin bağlanma dayanıklılığına etkisi
The effect of different surface preparation methods and various aging periods on bond strength for composite repair
MELTEM NERMİN DURSUN
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiHacettepe ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ESRA ERGİN
- Bulk fill kompozit rezinlerin tamirinde kullanılan farklı tip adeziv sistemlerin bağlanma dayanımına etkisi
Effect of different adhesive systems on repair bond strength of bulkfill composite resin
BURCU OĞLAKÇI
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiBaşkent ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. NESLİHAN ARHUN
- Akıllı kromatik teknolojisi ile üretilmiş kompozit rezinin renk stabilitesi ve yüzey pürüzlülüğünün değerlendirilmesi
Evaluation of color stability and surface roughiness of composite resin produced with smart chromatic technology
ALPER CUMHUR
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BEGÜM BÜŞRA CEVVAL ÖZKOÇAK
- Farklı fiberlerle güçlendirilmiş kompozit rezinin mine ve dentine bağlanma dayanımının makaslama testi metoduyla değerlendirilmesi ve taramalı elektron mikroskobu (SEM) ile incelenmesi
Evaluation of bond strengths of different fiber reinforced composites to enamel and dentine with shear bond test method and scannig electron microscopy (SEM) observations
NURCAN ÖZAKAR İLDAY
Doktora
Türkçe
2010
Diş HekimliğiAtatürk ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. NİLGÜN SEVEN