Zirkonya seramik, lityum disilikat cam seramik ve zirkonya ile güçlendirilmiş lityum silikat cam seramiklere uygulanan farklı yüzey işlemlerinin, kompozit rezinlerin tamir bağlanma dayanımı üzerine etkisi
The effect of different surface treatments on repair bond strength of resin composite to zirconia ceramic, lithium disilicate glass ceramic and zirconia reinforced lithium silicate glass ceramic
- Tez No: 426974
- Danışmanlar: PROF. DR. GÜLFEM ERGÜN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, yüzey işlemleri, hidroflorik asit, kumlama, lazer, kompozit rezin, makaslama bağlanma dayanımı, Dental bonding, Dental stres analizi, Kompozit reçineler, Lazerler, Yüzey özellikleri, CAD/CAM, surface treatments, hydrofluoric acid, sandblasting, laser, resin composite, shear bond strengt, Dental bonding, Dental stress analysis, Composite resins, Sanding, Lasers, Surface properties
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; kompozit rezinlerin 3 farklı CAD/CAM bloğuna (monolitik veya iki farklı veneer seramiği ile veneerlenmiş olarak lityum disilikat cam seramik, itriyum ile stabilize zirkonyum oksit seramik ve zirkonya ile güçlendirilmiş lityum silikat cam seramikler) makaslama bağlanma dayanımları üzerine yüzey işlemlerinin etkilerini termosiklus sonrasında değerlendirmektir. Test materyalleri yüzey işlem tekniğine göre sekiz alt gruba ayrılmıştır (Grup 1: hidroflorik asit + silan + bond, Grup 2: kumlama + silan + bond, Grup 3: lazer + silan + bond, Grup 4: hidroflorik asit + silan, Grup 5: kumlama + silan, Grup: 6: lazer + silan, Grup 7: silan + bond, Group 8: silan). Ek olarak, iki farklı bağlanma sistemi kullanılmıştır. Sonrasında, kompozit rezin tüm örnek yüzeylerine uygulanmıştır. Ardından, örnekler 370C'de 24 saat distile suda bekletilmiştir. Örneklerin yarısı termosiklusa maruz bırakılmıştır ve diğer yarısı 370C'de distile suda bekletilmiştir. Sonrasında, örnekler makaslama bağlanma dayanımı testine tabi tutulmuştur. Kırık tipleri, optik mikroskop ve SEM kullanılarak değerlendirildi. Veriler, Mann Whitney U, Kruskal Wallis ve post-hoc testler ile analiz edildi (p<0,05). İstatistiksel analizler; seramik tipinin, yüzey işlemi tekniğinin ve termosiklusun makaslama bağlanma dayanımı değerleri üzerinde belirgin etkiye sahip olduğunu göstermiştir (p<0,05). Ancak, veneerleme işlemi makaslama bağlanma dayanımı değerlerini etkilememiştir (p=0,046). Kompozit rezinlerin farklı CAD/CAM seramik yüzeylerine tamir bağlanma kapasitelerinin arttırılması için uygun yüzey işlemlerinin kullanılması önerilmektedir.
Özet (Çeviri)
The aim of this study was to evaluate the effect of surface treatments on the shear bond strength of resin composites to three different CAD/CAM blocks (lithium disilicate glass ceramic, yttrium stabilized zirconia ceramic and zirconia reinforced lithium silicate glass ceramic as monolithic or veneered with two different veneering ceramics) following thermocycling. The tested materials were divided into eight subgroups according to the surface treatment technique (Group 1: hydrofluoric acid + silane + bond, Group 2: sandblasting + silane + bond, Group 3: laser + silane + bond, Group 4: hydrofluoric acid + silane, Group 5: sandblasting + silane, Group: 6: laser + silane, Group 7: silane + bond, Group 8: silane). In addition, two different adhesive systems were used. Then resin composite was applied to the surfaces of all specimens. Afterwards, they were stored in distilled water for 24 hours at 370C. The half of the specimens were exposed to thermocycling procedure and the other half were stored in distilled water at 370C. Then specimens were subjected to universal testing machine for shear bond strength test. Failure modes were examined using an optical microscope and SEM. The data were analyzed with Mann Whitney U, Kruskal Wallis and post-hoc tests (p<0,05). Statistical analysis revealed that the ceramic type, surface treatment technique and thermocycling had significant effects on the shear bond strength values (p<0,05). However, veneering procedure had not affected the shear bond strength values (p=0,046). To improve the repair bonding capability of resin composites to different CAD/CAM ceramics, use of appropriate surface treatments are suggested.
Benzer Tezler
- Zirkonya ile güçlendirilmiş lityum silikat cam seramik kalınlığının ışıkla polimerize rezin simanın polimerizasyon dönüşüm derecesine etkisinin değerlendirilmesi
Evaluating the effect of zirconia reinforced lithium silicate glass ceramic thickness on the degree of conversion of LIGHT-cured resin cement
GÜLEN DAL
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiKütahya Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BANU ÇUKURLUÖZ BAYINDIR
- Estetik biohpp, zirkonya ve titanyum implant dayanakları ile desteklenen CAD/CAM monolitik lityum disilikat kronların çiğneme simülatörü ve termal döngü ile yaşlandırılması sonrası kırılma dayanımlarının karşılaştırılması
Comparison of fracture strength of CAD/CAM monolithic lithium disilicate crowns supported by esthetic biohpp, zirconia and titanium implant abutments after chewing simulator and thermal cycling aging
MUHAMMET EMİN AKSAN
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiKırıkkale ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SAADET ATSÜ
- Bilgisayar destekli tasarım ve üretim (CAD/CAM) ile üç farklı materyalden üretilen tek kronların klinik performansı: Bir yıllık başlangıç sonuçlarının değerlendirilmesi
Clinical performance of computer aided design and manufacturing (CAD/CAM) single crowns made from three different materials with one year preliminary results
DİLER ÇETİN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GÜLİZ AKTAŞ
- Güncel CAD/CAM seramik bloklarında farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin incelenmesi
Evaluation of different surface treatments to shear bond strength on current CAD/CAM blocks
ONUR ETÖZ
Diş Hekimliği Uzmanlık
Türkçe
2015
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MURAT KURT
- Seramik esaslı CAD/CAM materyallerinde bitim ı̇şlemleri sonrası yüzey pürüzlülüğü ve bakteri tutulumunun değerlendirilmesi
Evaluation of surface roughness and bacteria retention in ceramic based CAD / CAM materials after finishing processes
MAHMUT ERÇİL
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZGE PARLAR ÖZ