Hizmet ömrünü tamamlamış kreozot içeren emprenyeli ürünlerin odun plastik kompozitlerinde (OPK) değerlendirme olanaklarının araştırılması
Investigation on evaluation opportunities of impregnated products containing creosote that completed the service in wood plastic composites (WPCs)
- Tez No: 413500
- Danışmanlar: PROF. DR. ALİ TEMİZ
- Tez Türü: Doktora
- Konular: Ağaç İşleri, Wood Products
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, hizmet süresi sona ermiş kreozot içeren tel direklerinin geri dönüşümü ve remidasyonu amacıyla üretilen OPK'ların; benzetilmiş ve doğal dış ortam performansları, biyolojik dirençleri, fiziksel, mekanik, termal ve morfolojik özellikleri incelenmiştir. Ayrıca GC/MS yardımıyla kreozotun yapısı aydınlatılmıştır. Sonuç olarak; belirlenen 250 bileşikten %40'ı PAH bileşenlerini temsil ettiği saptanmıştır. Remidasyon işlemi ile Polisiklik Aromatik Hidrokarbon (PAH)'lar, önemli oranda uzaklaştırılmıştır. OPK'ların dış ortam testlerinde, elde edilen parametrelere göre (FTIR, renk, yüzey pürüzlülüğü gibi) en iyi sonuçlar kreozot içeren gruplarda olmuştur. Söz konusu parametreler, odun oranı artmasıyla artmış, uyumlaştırıcı kullanımı ile düşmüştür. Yüksek Yoğunluklu Polietilen (YYPE), dış ortam performansları bakımından Polipropilen (PP)'e göre üstünlük göstermiştir. Toprakla temas testinde; beyaz çürüklük mantarı, kontrol grupları ve referans sarıçam örnekleri üzerinde saptanmış olup sarıçam örneklerinde termit zararı da söz konusu olmuştur. Deniz testinde; kontrol grupların yüzeysel zarara maruz kalırken masif sarıçam örnekleri T. navalis tarafından tamamen tahrip edilmiştir. Çürüklük testleri sonrası kreozot gruplarında ağırlık kayıpları çok düşük olmuştur. Remidasyon gruplarında su alma ve kalınlık artışı yüksek bulunmuştur. Kreozot gruplarında eğilme ve çekme dirençleri kontrole göre daha düşük olurken darbe direnci hariç eğilme, çekme ve vida tutma dirençleri bakımdan PP grupları daha iyi sonuçlar vermiştir.
Özet (Çeviri)
In this study, accelerated and natural outdoor performances, biological resistances, physical, mechanical, thermal and morphological properties of WPCs produced in order to the recycle and remediate of out of service creosote treated utility poles were investigated. In addition, structure of creosote was illuminated by the help of GC/MS. As a result, it was observed that 40% of the designated 250 compounds represented the PAHs. A large part of the PAHs were removed through remidation process. According to the parameters obtained in weathering tests (such as FTIR, discoloration, roughness) the WPCs produced from creosote treated wood powder showed the best performance. The parameters mentioned above increased with the increase in wood ratio, and decreased with the use of coupling agents. YYPE demonstrated superiority in terms of outdoor performances compared to PP. In ground contact test, white rot fungus was isolated and identified in control and Scotch pine samples. Thermite damage was also observed in Scotch pine samples. In marine test, while superficial damage occurred in control groups, solid Scotch pine samples were completely destroyed by T. navalis. The weight losses in creosote groups were at very low level after the decay tests. The water intake and increase in thickness were observed to be high in remidation groups. While bending and tensile strengths were lower in creosote treated WPCs compared to control, PP groups gave better results in terms of bending, tensile and screw withdrawal strengths except for the impact resistance.
Benzer Tezler
- Hizmet ömrünü tamamlamış demiryolu balastının karayolu üstyapı kaplamasında kullanılması
Use of end of life railroad ballast in highway pavement coating
OSMAN KARATAŞ
Yüksek Lisans
Türkçe
2023
İnşaat MühendisliğiTekirdağ Namık Kemal Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. AYLİN AKYILDIZ
- A profitability analysis of product sales and leasing in supply chains
Tedarik zincirlerinde ürün ve hizmet satışının karlılığının incelenmesi
CANER DEMİRAYAK
Yüksek Lisans
İngilizce
2010
Endüstri ve Endüstri MühendisliğiBoğaziçi ÜniversitesiEndüstri Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. AYBEK KORUGAN
- Bitümlü karışımların geri dönüşüm yöntemlerinin incelenmesi
A research on recycling methods in bituminious pavement
İNANÇ SALTA
Yüksek Lisans
Türkçe
2010
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. MURAT ERGÜN
- Çelik özlü konveyör bant hurdalarının geri kazanımı ile pirolitik yağ eldesi
Recovery of steel cored conveyor belt waste and obtai̇ni̇ng pyrolyti̇c oi̇l
ÜSAME KOZ
Yüksek Lisans
Türkçe
2026
Çevre MühendisliğiKahramanmaraş Sütçü İmam ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YAKUP CUCİ
- Örnek gemi geri dönüşüm tesisi geliştirilmesi - Türkiye örneği
Best practice for ship recycling facilities - The case of Turkey
BURAK KEMERCİ
Yüksek Lisans
Türkçe
2016
Gemi Mühendisliğiİstanbul Teknik ÜniversitesiDeniz Ulaştırma İşletme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÖZCAN ARSLAN