Seramik rezin kompozit CAD/CAM blokların bağlanma dayanımı ve yüzey pürüzlülüğü üzerine farklı yüzey işlemlerinin etkilerinin değerlendirilmesi
Evaluation of the effects of different surface treatments on the surface roughness and bond strength of ceramic resin composite CAD/CAM blocks
- Tez No: 412564
- Danışmanlar: YRD. DOÇ. DR. AHMET KÜRŞAD ÇULHAOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental cementum, Dental porselen, Dental restorasyon, Dental stres analizi, Kompozit reçineler, Lazerler, Mikroskopi-elektron taramalı, Profilometre, Yüzey pürüzlülüğü, Dental bonding, Dental cementum, Dental porcelain, Dental restoration, Dental stress analysis, Composite resins, Lasers, Microscopy-electron scanning, Profilometer, Surface roughness
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı farklı yüzey işlemlerinin seramik rezin kompozitlerin yüzey pürüzlülüğü ve bağlanma dayanımı üzerindeki etkilerinin araştırılmasıdır. Vita Enamic ve Lava Ultimate materyaline (n=124) ait 248 adet örnek öncelikle kontrol, kumlama, asit ve lazer gruplarına (n=31) ayrılmıştır. Örneklerin yüzey pürüzlülükleri ölçüldükten sonra her gruptan birer örnek 3D profilometre ve SEM analizleri için kullanılmıştır. Daha sonra her bir yüzey işlemi grubu (n=30) ortalama pürüzlülük değerleri benzer olacak şekilde tekrar 2 alt gruba ayrılarak kontrol, silan, kumlama, kumlama + silan, asit, asit + silan, lazer, lazer + silan grupları (n=15) oluşturulmuştur. Rezin siman (Panavia F 2.0), özel bir test aparatı (SDI SBS Rig) kullanılarak seramik rezin kompozit yüzeylerine uygulanmıştır. Elde edilen örneklere suda bekletme (24 saat) ve termal döngü (2000 devir, 5-55 ºC) işlemleri uygulandıktan sonra makaslama bağlanma dayanımı testi uygulanmış ve kırılma türleri değerlendirilmiştir. Yüzey pürüzlülük değerleri one-way ANOVA ve post-hoc tamhane, bağlanma dayanımı değerleri Kruskal-Wallis, Mann Whitney U ve bağımsız örneklem t-testi, yüzey pürüzlülük-bağlanma dayanımı değerleri arasındaki korelasyon ise Spearman testi ile değerlendirilmiştir (p<0.05). Her bir materyale ait yüzey işlemi grupları, kontrol gruplarından daha pürüzlü yüzey yapısı oluşturmuş (p=0,000) ve yüzey işlemi grupları arasında anlamlı farklılık bulunmuştur (p=0,000). Yüzey işlemlerinden sonra silan uygulaması Vita Enamic materyalinin bağlanma dayanımını anlamlı derecede arttırırken (p=0,000), Lava Ultimate materyalinde lazerle pürüzlendirme hariç arttırmamıştır (p=0,140). Her iki materyal için de lazer + silan grupları en yüksek bağlanma dayanımını sağlamış ve yüzey işlemi grupları arasında anlamlı farklılık bulunmuştur (p=0,000). Vita Enamic materyalinin kumlama grubu için negatif, asit grubu için pozitif korelasyon gözlenirken, diğer gruplarda anlamlı bir korelasyon gözlenmemiştir.
Özet (Çeviri)
The aim of this study is to investigate the effects of different surface treatments on surface roughness and bond strength of the ceramic resin composites. 248 samples prepared with Vita Enamic and Lava Ultimate (n=124) were classified firstly as Control, Sandblasting, Acid etching and Laser irradiation groups (n=31). After the measurement of surface roughness, a sample from each group were used for 3D profilometry and SEM analysis. Then, each surface treatment group (n = 30) was divided into two subgroups including the Control, Silane, Sandblasting, Sandblasting+Silane, Acid, Acid+Silane, Laser and Laser+Silane groups (n = 15) considering to have similar mean roughness value. Resin cement (Panavia F 2.0) was applied to surface of the samples using SDI SBS rig. After water storage (24 hours) and termal cycling (2000 cycles, 5-55 ºC), the shear bond strength test was performed and then failure modes were evaluated. Surface roughness data was analyzed by one-way ANOVA and post-hoc tamhane. Bond strength data was analyzed by Kruskal-Wallis, Mann Whitney U and independent samples t-test. The relationship between surface roughness and shear bond strength values were determined by Spearman's correlation analysis (p<0.05). The surface treatment groups of each material had higher surface roughness values than control groups (p=0,000) and significant diferences was found among surface treatment groups for both materials (p=0,000). After surface treatments, Silane application improved bond strength significantly in Vita Enamic while did not increase in Lava Ultimate except laser irradiation. For both materials, Laser+silane groups provided highest bond strenght and significant difference was found among surface treatment groups (p=0,000). While it was observed that the correlation was negative for sandblasting group and positive for acid etching group of Vita Enamic material, no significant correlation was observed in the other groups.
Benzer Tezler
- Farklı yüzey işlemlerinin üstyapı kompozit rezinlerin CAD/CAM alt yapılarına bağlanma dayanımına ve mikrosızıntısına etkisinin incelenmesi
The effect of different surface treatements of CAD/CAM sub-structures on bond strength and mikroleakage of veneering composite resins
MUSTAFA ZEİNALABDEEN
Doktora
Türkçe
2015
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. FATİH SARI
DOÇ. DR. SEÇİL NEMLİ
- İki farklı CAD/CAM bloğunun tamir kapasitelerinin ve renk stabilitelerinin değerlendirilmesi
Evaluation of repair capacities and color stability of TWO different CAD / CAM blocks
HASİBE SEVİLAY BAHADIR
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiKırıkkale ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YUSUF BAYRAKTAR
- Hibrit cad-cam seramiklerin farklı yüzey işlemleri uygulanması sonrasında rezin siman ile olan bağlantı dayanımının incelenmesi
Investigation of bond strength between resin cement and hybrid ceramic after applying different surface treatments
BURAK KÖSEOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAtatürk ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. YUSUF ZİYA BAYINDIR
- Güncel CAD/CAM seramik bloklarında farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin incelenmesi
Evaluation of different surface treatments to shear bond strength on current CAD/CAM blocks
ONUR ETÖZ
Diş Hekimliği Uzmanlık
Türkçe
2015
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MURAT KURT
- Zirkonya içerikli CAD-CAM blokların farklı yüzey işlemleri ile reçine simanla bağlanma dayanımlarının karşılaştırılması
Effects of different surface treatments on the bond strength of resin cement to zirconia-based CAD-CAM materials
BİKE ALTAN
Doktora
Türkçe
2018
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FİRDEVS BETÜL TUNCELLİ