Al-Si-Mg alaşımlarına ilave edilen Cu ve Fe'in mikroyapı ve mekanik özelliklere etkisi
The effect of Cu and Fe addition to Al-Si-Mg alloys on microstructure and mechanical properties
- Tez No: 405850
- Danışmanlar: YRD. DOÇ. DR. TANSEL TUNÇAY
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İmalat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, Al-Si-Mg alaşımlarına ilave edilen bakır (Cu) ve demirin (Fe), mikro yapı ve mekanik özellikleri üzerine etkisi incelenmiştir. Döküm metodu ile Al-Si-Mg alaşımları üretildi (% 0,1-0,2 ve 0,4 Cu ve % 0,3-0,6 ve 1,2 Fe içeren) ve T6 ısıl işlemi uygulandı. Mikro yapı incelemelerinde, optik mikroskop, Tarama Elektron Mikroskobu (SEM) ve X-ışınımı kırınımı analizi (XRD) kullanıldı. İlaveten, yoğunluk ve mikro sertlik ölçümleri yapıldı. Mekanik özelliklerin incelenmesinde çekme ve aşınma testi uygulandı. Çekme testinde çekme hızı 1 mmdk-1 kullanıldı. Aşınma testlerinde 1 ms-1 sabit hız altında 10-40 N yük altında, 500-2000 m. mesafelerinde uygulanmıştır. Yapılan çalışmalar sonucunda, artan Fe miktarına bağlı olarak çekme mukavemetinin ve yüzde uzama miktarının azaldığı belirlenmiştir. Bunun sebebi, Fe miktarının artmasıyla yapıda oluşan Al-Si-Fe esaslı intermetaliklerin yapısının ve morfolojisinin değişimidir. Buna karşın Cu miktarının artmasıyla yapıda oluşan AlCu2 fazının artmasından dolayı, çekme mukavemetinin ve uzamanın artığı belirlenmiştir. Aşınma testi sonuçlarına göre, demir ilave edilen gruplarda 10 ve 20 N yük altında % 0,6 Fe alaşımında en düşük ağırlık kaybı ölçüldü. 40 N yük altında ise % 0,2 Fe alaşımında en düşük ağırlık kaybı ölçüldü. Cu ilavesi ile 10 ve 20 N yük altında en düşük ağırlık kaybı % 0,2 Cu alaşımında, 40 N yük altında ise en düşük ağırlık kaybı % 0,4 Cu alaşımında ölçülmüştür.
Özet (Çeviri)
In this study, the effect of copper (Cu) and iron (Fe) added to Al-Si-Mg alloy on the microstructure and mechanical properties were investigated. Al-Si-Mg alloys (containing 0,1, 0,2 % and 0,4% Cu and 0,3, 0,6 and 1,2 % Fe) were produced by casting method and subjected to a T6 heat treatment. The micro-structure analyses were performed by optical microscopy (OM), scanning electron microscopy (SEM) and X-Ray diffraction analysis (XRD). In addition, density and micro hardness measurements were made. Tensile tests and wear tests were carried out for investigation of the mechanical properties and wear behaviour. In tensile tests, cross-head speed used was 1 mmmin.-1. Wear tests were carried out at 1 ms-1 sliding speed under 10-40 N loads. The results showed that the tensile strength and the percent elongation were reduced, as the amount of Fe increased. This was explained by the change in the structure and morphology of Al-Si-Fe based intermetallics with increasing Fe amount. However, it was determined that tensile strength and elongation were increased due to formation of AlCu2 phases with increasing Cu amount. According to wear test results, the lowest weight loss were measured for the alloy containing 0,6 % Fe under 10 and 20 N loads. Under 40 N load, the lowest weight loss was measured for the alloy containing 0,2 % Fe. Under 10 and 20 N loads, the lowest weight loss was measured for the alloy containing 0,2 Cu. However, Under 40 N, the lowest weight loss was measured for the alloy containing 0,4 % Cu.
Benzer Tezler
- 6063 aluminyum alaşımlarının korozyon direnci üzerine anodizasyon öncesi yüzey işlemlerinin ve AA anodizasyonla üretilmiş ince oksit filmlerinin etkisi
The Effect of pretreatment and thin layer sulfuric acid a C anodization of 6063 aluminum alloys on its corrosion resistance
FERİHA SERTÇELİK
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- Diesel motorları yakıt püskürtme sistemlerinin dinamik simülasyonu
Başlık çevirisi yok
İRFAN KARAGÖZ
Yüksek Lisans
Türkçe
1986
Makine MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. OĞUZ BORAT
- Sürücülerde kandaki alkol miktarı ile trafik kazası arası ilişki
Başlık çevirisi yok
Z.SEMRA GÜMRÜKÇÜ
Yüksek Lisans
Türkçe
1986
UlaşımGazi ÜniversitesiKazaların Çevresel ve Teknik Araştırması Ana Bilim Dalı (disiplinlerarası)
PROF. DR. RIDVAN EGE
- İlkokul çağı erkek çocuklarında inmemiş testis anomalisi ve insidansı
The anomaly and incidence of cryptorchidism in primary school boys
SERDAR SEZGİN