Manyetokalorik etki gösteren gadolinyum tabanlı alaşımların üretilmesi ve karakterizasyonu
Preperation and characterization of gadolinium based magnetocaloric materials
- Tez No: 394463
- Danışmanlar: DOÇ. DR. ATİLLA COŞKUN
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Manyetokalorik Etki, Manyetik Soğutma, Curie Sıcaklığı, Ark-Ergitme, İnce Film, E-Beam, Magnetocaloric Effect, Magnetic Refrigeration, Curie Temperature, Arc-Melting, Thin Film, E-beam
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Muğla Sıtkı Koçman Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Yaygın bir ihtiyaç olan soğutma, günümüzde çoğunlukla gaz sıkıştırmalı soğutucular ile yapılmaktadır. Çok düşük sıcaklık (<10K) gereksinimlerinde ise manyetokalorik etkiye (MKE) dayalı manyetik soğutma (MS) sistemleri tercih edilmeye başlanmış ve bu sistemler giderek yaygınlaşmıştır. Oda sıcaklığında devasa MKE gösteren Gd5Si2Ge2 bileşiğinin 1997 yılında bulunması bir dönüm noktası olmuş ve bu bileşiğin kullanıldığı MS uygulamaları öncül olarak yapılmıştır. Bu tez çalışması kapsamında, Gd5Si2Co2, Gd5Si2Ge2, Gd5Si2Fe2 alaşımları ark ergitme yöntemiyle ve Gd5Si2Fe2 ince filmi de e-beam ince film üretim tekniği ile hazırlanmıştır. Üretilen alaşımların ve ince filmin yapısal ve morfolojik özellikleri atomik kuvvet mikroskobu (AFM), taramalı elektron mikroskobu (SEM-EDS) ve X-ışınları kırınımı (XRD) analizleriyle, manyetik özellikleri ise fiziksel özellikleri ölçüm sistemi (PPMS) ile incelenmiştir. Yapılan analizler sonucunda, alaşımların ve ince filmin başarılı bir şekilde üretildiği bulunmuştur. Özellikle literatürde ilk defa yapılmış olan Gd5Si2Fe2 ince filmin ısıl işlem sonrası metalik davranış kazanması da ayrı bir başarıdır. Isıl işlem sonrası alaşımların birden fazla manyetik faz içerdikleri bulunmuştur. Alaşımların EDS analizlerinden de birden fazla faz oluşumunun bulunması, manyetik ve elektriksel ölçümleri destekleyen sonuçlardır. Alaşımların manyetik ve elektriksel ölçümleri de neredeyse uyum içerisindedir.
Özet (Çeviri)
Cooling systems, which are highly demanded in all area of daily life, are widely used for keeping our foods cool and living spaces in comfort temperature. Today, process of cooling is mostly realized by means of vapor compression. Whereas, for very low temperature (<10K) needs magnetic cooling systems have started to be preferred and become widespread. There are advantages and disadvantages of both systems against each other. In spite of their very low efficiency, vapor compression cooling systems are the ones which realize cooling process at room temperature, are mass produced and sold in commercial abundance. In contrast, magnetic cooling systems have high efficiency and are used in scientific and technological purposes at very low temperatures below room temperature. However, refrigeration that is of commercial importance is the one which is applicable at around room temperature. In this study, Gd5Si2Co2, Gd5Si2Ge2, Gd5Si2Fe2 alloys are synthesized by using arc-melting method and Gd5Si2Fe2 thin film is coated by using e-beam method. Morphological and structral properties of the samples are analyzed by using atomic force microscopy (AFM), scanning electron microscopy - energy dispersive spectroscopy (SEM-EDS) and X-ray diffraction (XRD) techniques, magnetic properties are explored by physical properties measurement system (PPMS). As a consequence of the analyses it has been showed that the thin film and alloy samples are synthesized properly. Especially it is another succes that the Gd5Si2Fe2 thin film has showed metallic behaviour after annealing.
Benzer Tezler
- Sol-jel yöntemi ile hazırlanan La1-xMgxMn1-yCoyO3 bileşiklerinin yapısal ve manyetik özelliklerinin incelenmesi
Investigation of structural and magnetic properties of La1-xMgxMn1-yCoyO3 compounds prepared by sol-gel method
AHMET ÇETİN
Yüksek Lisans
Türkçe
2009
Fizik ve Fizik MühendisliğiMuğla ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. ERGÜN TAŞARKUYU
- Manyetokalorik etki gösteren manganitli bileşiklerin üretilmesi ve karakterizasyonu
Preparation and characterization of the magnetocaloric effect in perovskite manganites samples
YUSUF SAMANCIOĞLU
Yüksek Lisans
Türkçe
2010
Fizik ve Fizik MühendisliğiMuğla ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. ATİLLA COŞKUN
- Manyetokalorik etki gösteren la0.67sr0.33mno3 perovskit bileşiğine yapılan ba katkısıyla değişen yapısal ve manyetik özelliklerin incelenmesi
Başlık çevirisi yok
PINAR BAYKARA
Yüksek Lisans
Türkçe
2019
Fizik ve Fizik MühendisliğiMuğla Sıtkı Koçman ÜniversitesiFizik Ana Bilim Dalı
DR. ÖĞR. ÜYESİ YUSUF SAMANCIOĞLU
- Manyeto yapısal geçişlerde manyetokalorik özellikler üzerine histerezisin etkisi
The effect of histerezis on magnetocaloric properties at magnetostructural transitions
ATAKAN TEKGÜL
Doktora
Türkçe
2016
Fizik ve Fizik MühendisliğiAkdeniz ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. NURİ ÜNAL
- Gd5Si2-yGe2-yGa2y alaşımının yapısal ve manyetik özelliklerinin incelenmesi
The investigation of structural and properties of Gd5Si2-yGe2-yGa2y alloy
SEDA AKSOY
Yüksek Lisans
Türkçe
2006
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
PROF.DR. YALÇIN ELERMAN