Farklı yüzey işlemi uygulanmış zirkonyum oksit esaslı alt yapıların üst yapı porselenine olan bağlanma dayanımının değerlendirilmesi
Evaluation of bond strength between veneering porcelains and different surface treated zirconium oxide based frameworks
- Tez No: 393959
- Danışmanlar: PROF. DR. LÜTFÜ İHSAN ALADAĞ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Bağlanma Dayanımı, CO2 lazer, Yüzey İşlemleri, Zirkonya, Zirkonyum oksit tozu, Liner, Dental bonding, Dental materyaller, Dental porselen, Yüzey özellikleri, Zirkonyum oksit, Bond Strength, CO2 laser, Surface Treatments, Zirconia, Zirconium oxide powder, Liner, Dental bonding, Dental materials, Dental porcelain, Surface properties, Zirconium oxide
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Estetik, biyouyumluluk ve üstün mekanik özelliklere sahip olan zirkonya, tam seramik sistemlerde, son yıllarda yaygın olarak alt yapı materyali olarak kullanılmasına rağmen, veneer seramiği ile arasındaki bağlantı mekanizması henüz net olarak bilinmemektedir. Bu çalışmanın amacı, zirkonya alt yapılara uygulanan farklı yüzey işlemlerinin, materyallerin ortalama yüzey pürüzlülüğüne ve faz değişimine olan etkisinin incelenmesi ve uygulanan farklı yüzey işlemleri ile birlikte liner materyalinin, zirkonya alt yapı ile veneer seramiği arasındaki bağlanma dayanımına olan etkisinin araştırılmasıdır.Yapılan çalışmada, 80 adet, 8x8x3 mm boyutlarında Lava zirkonya alt yapı blokları hazırlandı. Uygulanan yüzey işlemlerine göre örnekler 4 gruba ayrıldı (n=20): Kontrol, kumlama (50μm Al2O3), CO2 lazer ile pürüzlendirme ve zirkonyum oksit tozu eklenerek pürüzlendirme. Örneklerin, profilometre ile yüzey pürüzlülüğü ölçümü yapıldı ve X- ray difraksiyon (XRD) analizi ile faz yapısı belirlendi. Yüzey işlemi uygulanan her bir grubun yarısına IPS e.max ZirLiner uygulandı (n=10). Tüm gruplara, tabakalama tekniği (IPS e.max Ceram) ile 5 mm çapında ve 3 mm yüksekliğinde veneer porselen uygulandı. Örneklerin bağlantı yüzeylerine, universal test cihazında 0,5 mm/dk hızla kesme kuvveti uygulandı. Bağlanma dayanımı testinden sonra örneklerin kopma ve yüzey işlemi yapılmış yüzeyleri, SEM ve EDS analizi ile incelendi. Verilerin analizi, Kruskal Wallis H Testi (p<0.05) ve Mann Whitney U testi ile değerlendirildi (p<0.05). Çalışmanın sonucuna göre, zirkonya yüzeyinin zirkonya tozu ile kaplanarak modifiye edilmesi, yüzey pürüzlülüğünü ve zirkonya veneer bağlantı dayanımı anlamlı bir şekilde arttırmıştır. XRD analizine göre, kumlama diğer yüzey işlemlerinden daha fazla monoklinik zirkonya yapı oluşumuna neden olmuştur. Liner uygulanması zirkonya ve veneer arasında bağlanma dayanımını olumsuz yönde etkilemiştir.
Özet (Çeviri)
In recent years, zirconia is widely used strengthening core material for all ceramic systems which has esthetics, biocompatibility and mechanical properties but bonding mechanism between zirconia and veneering ceramic is still unknown. The purpose of this study was to evaluate the effect of different surface treatments on mean surface roughness and phase transformation and to investigate the effect of different surface treatments and liner material applied zirconia frameworks on shear bond strength. In the study, eighty (8 x8 x3 mm) zirconia framework blocks were prepared. Samples were divided into 4 groups according to the surface treatment (n=20); Control, sandblasting (50 μm Al2O3), CO2 laser etching, zirconium oxide powder caoating before sintering. Surface roughness was measured by using profilometer and X-ray diffraction analysis was performed to characterize the crystalline phases for all specimens. Liner (IPS e.max Ceram ZirLiner), was applied to half of these specimens (n=10). All subgroups were veneered (5 mm in diameter, 3 mm in thickness) with layering ceramic (IPS e.max Ceram). The samples were tested in a universal testing machine with a cross head speed of 0,5mm/min. After shear bond strength test, fractured surface specimens and surface treatments were evaluated with SEM and EDX. The data were analyzed by using the Kruskal Wallis H Testi and Mann Whitney U test for multiple comparison. According to the results of this study, modifying the zirconia surface with powder coating could significantly increase the surface roughness and the shear bond strength of zirconia to veneering porcelain. XRD analysis revealed that sandblasting was contained more monoclinic zirconia than the other surface treatments. Liner application negatively affected the bond strength between the zirconia and the veneer.
Benzer Tezler
- Zirkonya ve veneer seramik arasındaki bağlantıya farklı fırınlama uygulamalarının etkisi
Connection between the effect of different applications for firing zirconia and veneer ceramic
TÜRKER AKAR
Doktora
Türkçe
2014
Diş HekimliğiCumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAKAN DEMİR
- Farklı lazer uygulamalarının zirkonya esaslı alt yapıların faz değişimine ve üst yapı porselenin bağlanma dayanımına etkisinin incelenmesi
Investigation of the effect of different laser applications on the phase change of zirconia based substructures and the bonding strength of superstructure porcelain
SELİN AYCAN
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FATİH MEHMET KORKMAZ
- Sinterize öncesi ve sonrası zirkonyum oksit esaslı alt yapı üzerine uygulanan farklı yüzey işlemlerinin bükülme dayanıklılığına etkisinin araştırılması
Investigation of different surface treatment of zirconia frameworks after and before sintering on biaxial flexural strength
ÜMİT GÜNEY
Doktora
Türkçe
2016
Diş HekimliğiCumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. FAİK TUĞUT
- Novel approaches for protection of light metals under various wear conditions via micro arc oxidation process
Hafif metallerin mikro ark oksidasyon yöntemiyle farklı aşınma şartlarında korunmasına yönelik yenilikçi yaklaşımlar
FAİZ MUHAFFEL
Doktora
İngilizce
2021
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Zirkonyum oksit esaslı seramik ile rezin simanın bağlantısına farklı yüzey işlemlerinin etkileri
The effects of different surface treatments on the bond strength of zirconium-oxide ceramic and adhesive resin
SELMA ŞEN
Doktora
Türkçe
2010
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GÖZLEM CEYLAN