Polianilin/Bentonit kompozitinin sentezi, karakterizasyonu ve elektroreolojik özelliklerinin incelenmesi
Synthesis and characterization of Polyaniline/Bentonite composite and its investigation of electrorheological
- Tez No: 391965
- Danışmanlar: DOÇ. DR. MUSTAFA YAVUZ
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Kimya, Polymer Science and Technology, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Süleyman Demirel Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışması; üç aşamada tamamlanmıştır. Birinci aşamada, uygun bir başlatıcı ve çözücü kullanılarak kimyasal polimerleşme ile iletken polianilin (PAni) sentezi gerçekleştirilmiştir. Daha sonra anilin monomeri ile inorganik yapıda olan bentonit'in HCl ortamında başlatıcı (NH4)2S2O8 ile Polianilin/Bentonit (PAni/BNT) kompozit'i sentezlenmiştir. İkinci aşama, sentezlenen numunelerin karakterizasyonunu oluşturmaktadır. Yapısal özellikleri Fourier Transform Infrared Spektroskopisi (FTIR) ile Görünür Bölge Spektrometresi (UV-Vis) aydınlatılarak polimer ve kompozit oluşumunu destekleyen pikler ve bandlar gözlenmiştir. Bozunma sıcaklıkları termal analiz (TGA) ile incelenmiştir ve kompozit yapının PAni'ye göre daha kararlı olduğu belirlenmiştir. Taramalı elektron mikroskobu (SEM) ile numunelerin yüzey morfolojileri incelenmiştir. Her iki yapının da farklı yüzey özelliklerine sahip olduğu görülmüştür. Polimerlerin iletkenlik değerleri dört nokta tekniği ile ölçülmüştür. Son aşama da ise, sentezlenen polimerlerin sıcaklığa bağlı elektriksel iletkenlikleri ölçülmüş ve elektroreolojik (ER) davranışları belirlenmiştir. Sıcaklığa bağlı elektriksel iletkenlik ölçümlerine göre, her iki polimer de yarı iletken davranış göstermiştir. φ=%15 (V/V)'lik hacim kesrinde silikon yağı içerisinde hazırlanan süspansiyonun elektrik alan, kayma hızı, kayma gerilimi, sıcaklık ve frekans gibi değişkenlere karşı ER davranışları belirlenmiştir. Ayrıca, elektrik alan varlığında ve yokluğunda süspansiyona sürünme testleri uygulanarak zaman içerisinde gösterdiği deformasyonlar incelenmiştir. Polimer ve kompozit yapılarının ER aktif malzemeler olduğu anlaşılmıştır. Sentezlenen polimerlerin akıllı malzeme olarak endüstriyel uygulamalar için uygun olabileceği sonucuna varılmıştır.
Özet (Çeviri)
This thesis was completed in three steps. In the first step, synthesis of conducting polyaniline (PAni) were performed by chemical polymerization using an initiator and suitable solvent. Then, Polyaniline/Bentonite (PAni/BNT) composite was synthesized by using (NH4)2S2O8 initiator in HCl medium of the aniline monomer with bentonite which has inorganic structure. The second step is the characterization of the synthesized samples. The structural properties of samples were found using Fourier Transform Infrared Spectroscopy (FTIR) and UV-Visible (UV-Vis) spectrometer peaks and bands were observed that it supported the formation of polymers and composites. Decomposition temperatures were investigated by using thermal analysis (TGA) and it was determined that the composite structure is more stable than PAni. The surface morphology of the samples were investigated by means of scanning electron microscopy (SEM). Both structures were observed to have different surface properties. Conductivity value of the polymers were measured by four probe technique. In the last stage; electrical conductivity depending on temperature of the synthesized polymers were measured and the electrorheological (ER) behaviors are determined. According to electrical conductivity depending on temperature, both of polymers demonstrated on semiconducting behaviors. The effects of some parameters such as electric field, shear rate, shear stres, temperature and frequency on ER behaviors of suspensions prepared in silicone oil of φ=15 % (wt) were determined. Furthermore, Creep tests were applied to suspension in the presence and absence of electric field and deformations observed in suspensions with time were investigated. Polymer and composite structures were found to be ER active materials. The synthesized polymers can be classified as a smart material which is an important parameter for potential industrial applications.
Benzer Tezler
- Bazı iletken polimerlerin kil ve zeolit kompozitlerinin hazırlanması ve karakterizasyonu
Preparation and characterization of clay and zeolite composites of some conductive polymers
ORHAN SOYLU
Doktora
Türkçe
2022
KimyaTokat Gaziosmanpaşa ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEYLAN
PROF. DR. SELÇUK ŞİMŞEK
- Elektrokimyasal olarak oluşturulacak polianilin (PANI) kaplamanın demirli malzemelerin korozyon davranışları üzerine etkilerinin incelenmesi
Electrochemical synthesis and corrosion performance of polyaniline (PANI)coating on iron substrates
ALİ TUNCAY ÖZYILMAZ
- Polianilin ile türevlerinin paslanmaz çelik yüzeyinde elektrokimyasal sentezi ve anti-korozif özellikleri
Electrochemical synthesis of polyaniline and its derivatives on stainless steel and their anti-corrosive properties
EVRİM HÜR
Doktora
Türkçe
2005
KimyaEskişehir Osmangazi ÜniversitesiKimya Ana Bilim Dalı
DOÇ.DR. YÜCEL ŞAHİN
PROF.DR. GÖZEN BEREKET
- Polianilin/silisyum dioksit kompozit maddesinin sentezi, karakterizasyonu ve iletken film yapımı
Synthesis and characterization of polyaniline/silicon dioxide composites and preparation of conductive films
BELGİN ERKAN
Yüksek Lisans
Türkçe
2008
KimyaKahramanmaraş Sütçü İmam ÜniversitesiKimya Ana Bilim Dalı
YRD. DOÇ. DR. HÜSEYİN ZENGİN
- Polianilin ve poli(2-iyodoanilin) çift kaplaması ile polianilin ve poli(2-toluidin) çift kaplamasının korozyon performansları
Corrosion performances by multilayered polyaniline and poly(2-iodoaniline) with polyaniline and poly(2-toluidine) coatings
DERYA ÖZDEMİR
Yüksek Lisans
Türkçe
2008
KimyaEskişehir Osmangazi ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. GÖZEN BEREKET