İki farklı LED ışık cihazının nanohibrid kompozit rezinin mikromekanik özellikleri üzerine etkisi
Effect of two different LED light curing units on the micromechanical properties of a nanohybrid composite resin
- Tez No: 383173
- Danışmanlar: PROF. DR. SEVİL GÜRGAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental çimentolar, Işık, Kompozit reçineler, Mikromekanik, Nanopartiküller, Dental materials, Dental cements, Light, Composite resins, Micromechanic, Nanoparticles
- Yıl: 2015
- Dil: Türkçe
- Üniversite: Hacettepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu in vitro çalışmanın amacı, iki farklı mesafeden uygulanan 2 LED ışık cihazının farklı polimerizasyon programlarının bir nanohibrid kompozit rezinin (Kalore/GC) mikromekanik özellikleri üzerine etkilerini incelemektir. İki mm kalınlığında hazırlanan 72 kompozit rezin örneği yüksek güçteki iki LED ışık cihazı (Bluephase 20i/Ivoclar Vivadent ve FlashMax P3/CMS Dental) ile 0 ve 7 mm mesafelerden 6 gruba ayrılarak (n=6), Grup a: Bluephase 20i – 10 sn – Yüksek güç, Grup b: Bluephase 20i – 15 sn – Yüksek güç, Grup c: Bluephase 20i – 5 sn – Çok yüksek güç, Grup d: Bluephase 20i – 15 sn – Yavaş başlangıç, Grup e: FlashMax P3 – 4 mm uç – 3 sn, Grup f: FlashMax P3 – Uçsuz – 3 sn, polimerize edilmiştir. Örneklerin polimerizasyonu sırasında alt yüzeylerine ulaşan ışık şiddetleri eş zamanlı olarak radyometre (MARC Resin Calibrator) ile ölçülmüştür. Üst ve alt yüzeylerinin Vickers sertlik (HV) ve elastisite modülü (E) değerleri otomatik üniversal bir sertlik belirleyici cihaz (Fischerscope H100C) ile 37°C de 24 saat distile suda bekletildikten sonra kaydedilmiştir. Enerji yoğunluğunun, uygulama mesafesinin ve yüzey farklılıklarının etkileri Tek Yönlü Varyans Analizi, Tukey ve t testleri ile analiz edilmiştir (p=0.05). Tüm gruplarda ışık uygulama mesafesi 0 mm'den 7 mm'ye çıkartıldığında kompozit rezinin polimerizasyonu sırasında üst ve alt yüzeylerinde oluşan ışık şiddeti ve enerji yoğunluğunun azaldığı belirlenmiştir. 0 mm mesafede en yüksek üst yüzey HV (76.61 ± 5.85 N/mm2) ve E (10.42 ± 5.85 GPa) değerleri Grup b'de, 7 mm mesafede en düşük üst yüzey HV (49.41 ± 13.11 N/mm2) ve E (6.63 ± 1.87 GPa) değerleri Grup e'de görülmüştür (p<0.05). 0 ve 7 mm mesafelerde en düşük alt yüzey HV ve E değerleri Grup e'de bulunmuştur (p<0.05). Işık uygulama mesafesinin arttırılması Grup e'de alt ve üst yüzeylerin mikromekanik özelliklerini anlamlı olarak zayıflatmıştır (p<0.05). LED ışık cihazlarının ışık şiddetlerinin üreticilerinin bildirdiğinden daha yüksek olduğu bulunmuştur. Farklı ışık enerji yoğunluklarının (0.01 J/cm2 - 23.13 J/cm2) ve uygulama mesafelerinin (0 ve 7 mm) nanohibrid kompozit rezinin alt ve üst yüzeylerinin mikromekanik özelliklerini etkilemiştir. Kompozit rezinlerin üst ve alt yüzeylerinin mikromekanik özelliklerinin kullanılan ışık cihazlarının bu yüzeylerde oluşturduğu ışık şiddetinden çok enerji yoğunluğundan etkilendiği sonucuna varılmıştır.
Özet (Çeviri)
The aim of this in vitro study was to investigate the effects of different curing modes of two LED light curing units from two exposure distances on the micromechanical properties of a nanohybrid composite resin (Kalore/GC). Seventy-two specimens of composite resin with 2 mm thickness (n=6) were cured using two high irradiance LED light curing units (Bluephase 20i/Ivoclar and FlashMax P3/CMS Dental) at 0 and 7 mm exposure distances. The curing conditions were: Grup a: Bluephase 20i – 10 s – High power, Grup b: Bluephase 20i – 15 s – High power, Grup c: Bluephase 20i – 5 s – Turbo, Grup d: Bluephase 20i – 15 s – Soft start, Grup e: FlashMax P3 – 4 mm tip – 3 s, Grup f: FlashMax P3 – without tip – 3 s. The transmitted light power and energy density were evaluated at specimens' bottom in real time during curing, with a radiometer (MARC Resin Calibrator). Vickers hardness (HV) and modulus of elasticity (E) were measured with an automatic universal hardness indenter (Fisherscope H100C) at specimens' top and bottom surfaces after storing 24 hours in distilled water at 37°C. Effects of energy densities, exposure distances and surface conditions were analyzed using One Way Variance Analyze, Tukey and t tests (p=0.05). Different energy densities were observed for all groups according to distance and surface conditions. In all groups, a decrease in intensity and energy density formed in the top and bottom of the composite resin surfaces during the polymerization was determined when the exposure distance was removed from the 0 to 7 mm. The highest hardness (76.61 ± 5.85 N/mm2) and modulus of elasticity (10.42 ± 5.85 GPa) values were observed in the Group b at 0 mm, the lowest hardness (49.41 ± 13.11 N/mm2) and modulus of elasticity (6.63 ± 1.87 GPa) values were observed in the Group e at 7 mm for top surfaces (p<0.05). Increasing the exposure distance was significantly impaired the micromechanical properties of the top and bottom surfaces in the Group e (p<0.05). The light intensities of LED light curing units were higher than the manufacturers' reported. Different light energy densities (0.01 J/cm2 - 23.13 J/cm2) and exposure distances (0-7mm) influenced the micromechanical properties of top and bottom surfaces of a nanohybrid composite. The top and bottom surfaces' micromechanical properties of composite resins were affected by the energy density more than the light intensity of the used light curing units.
Benzer Tezler
- Güncel diş renkli restoratif dolgu materyallerine farklı uygulama prosedüründeki ev tipi beyazlatma ajanları uygulandıktan sonra fiziksel özelliklerinin in vitro olarak incelenmesi
In vitro investigation of tooth colored restorative materials' physical properties after different application procedures of home bleaching agents
GÖKÇE DÖNMEZ KIRAN
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. NAZMİYE DÖNMEZ
- Rezin esaslı restoratif materyallerin yüzey pürüzlülüğüne beyazlatıcı diş macununun etkisi
The effect of whitening toothpaste on surface roughness ofresin-based restorative materials
CEMİLE YILMAZ
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiAfyonkarahisar Sağlık Bilimleri ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZGÜR KANIK
- Işık kaynaklarının farklı kompozit rezinlerin bulk-fill kompozitle tamirinde bağlanma dayanımı üzerine etkisi
Effect of light sources on bond strength of different composite resins repaired with bulk-fill composite
VAHTİ KILIÇ
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiCumhuriyet ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. FERİDUN HÜRMÜZLÜ
- Halojen ve led ışık kaynakları ile polimerize edilerek, farklı bitirme / polisaj teknikleri uygulanan iki farklı restoratif materyalin; yüzey sertliği, yüzey pürüzlülüğü ve biaksiyal fleksural dayanımlarının in vitro incelenmesi
Polymerized with halogen and led light sources,two different restorative materials applied for different finishing / polishing techniques; in vitro investigation of surface hardness, surface roughness and biaxial flexural strength
RÜYA ALPAR
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiSüleyman Demirel ÜniversitesiÇocuk Diş Hekimliği Ana Bilim Dalı
PROF. DR. ÇİĞDEM KÜÇÜKEŞMEN
- İki farklı ışık cihazı ile polimerize edilen üç farklı kompozitin renk stabiliteleri
Color stability of three different resin composites polymerized with two different light curing units
RUHSAN MÜDÜROĞLU ADIGÜZEL
Diş Hekimliği Uzmanlık
Türkçe
2016
Diş HekimliğiAnkara ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. ADİL NALÇACI