Farklı yüzey işlemleri uygulanmış lityum disilikat seramiklerle rezin simanın mikrogerilim bağlanma dayanımlarının incelenmesi
The evaluation of different surface treatments on microtensile bond strength between lithium disilicate ceramics and resin cement
- Tez No: 374828
- Danışmanlar: DOÇ. DR. GÖKNİL ERGÜN KUNT
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Lityum disilikat seramik, mikrogerilim bağlanma dayanımı, rezin siman, ısı uygulaması, yüzey işlemleri, Dental bonding, Dental cementum, Dental materyaller, Dental porselen, Dental restorasyon, Dental stres analizi, Dental çimentolar, Kompozit reçineler, Lithium-disilicate ceramic, microtensile bond strength, resin cement, heat treatment, surface treatment, Dental bonding, Dental cementum, Dental materials, Dental porcelain, Dental restoration, Dental stress analysis, Dental cements, Composite resins
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Ondokuz Mayıs Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Çalışmamızın amacı, en son geliştirilen lityum disilikat seramik sistemi olan IPS e.max Press seramikler ile rezin simanın bağlantısında farklı yüzey işlemlerinin etkinliğini, mikrogerilim test metodu ile incelemektir. Materyal ve Metot: Mikrogerilim bağlantı testi için, 13x13x3 mm ebatlarında 8 adet IPS e.max Press örnek üreticinin talimatları doğrultusunda hazırlandı ve seramiklerin kompozit rezin dublikatları elde edildi. Seramik yüzeylerine sırasıyla şu yüzey işlemleri uygulandı: Grup K (Kontrol): hiçbir yüzey işlemi uygulanmadı, Grup S: silan uygulandı, Grup ALS: 50 μm'lik alüminyum oksit partikülleriyle kumlama + silan, Grup CS: silika ile modifiye edilmiş 30 μm'luk alüminyum oksit partikülleriyle kumlama (CoJet) + silan, Grup SHT1: silan + 100 oC'de ısı 1dak, Grup SHT2: silan + 100 oC'de ısı 2dak, Grup HF: % 9.5'luk hidroflorik asit, Grup HFS: % 9.5'luk hidroflorik asit + silan uygulandı. Yüzey işlemi uygulanan seramikler rezin siman ile kompozit bloklara simante edildi. Örnekler mikrogerilim bağlantı testi için, adeziv yüzeye dik bir şekilde 1 mm2 bağlantı alanı elde edecek şekilde elmas bir separe ile kesildi. Her gruptan 20'şer adet bar seçildi. Mikrogerilim test cihazında 1 mm/dak hızında yükleme yapılarak mikrogerilim bağlantı testi uygulandı. Veriler tek yönlü varyans analizi (ANOVA) ve Post-hoc testi ile istatistiksel olarak değerlendirildi. Bulgular: En yüksek bağlantı değerleri Grup HFS'den elde edildi ve bu grup ile diğer tüm gruplar arasında istatistiksel olarak anlamlı fark bulundu (p<0,05). Sonuç: Silana 100 oC'de ısı uygulanması lityum disilikat seramik ile rezin siman arasında bağlantıyı arttırmıştır. Fakat lityum disilikat seramiklerde hidroflorik asit ardından silan uygulanması halen en etkili yüzey uygulamasıdır.
Özet (Çeviri)
Aim: The aim of this study was to evaluate the influence of different surface treatments on the microtensile bond strength of resin cement to lithium disilicate ceramic (IPS e.max Press). Material and Method: For microtensile bond strength test; eight 13×13×3 mm IPS e.max Press specimens were fabricated according to the manufacturer's instructions. Ceramic blocks were dublicated in composite resin. Surface treatment groups were as follows: Group K: no surface treatment; Group S: silane alone; Group ALS: airborne-particle abrasion with 50 µm aluminum oxide particles+silane; Group CS: airborne-particle abrasion with 30 µm aluminum oxide particles modified with silica (CoJet) + silane; Group SHT1: silane + heat treatment was performed with heat gun (100 oC, 1 min); Group SHT2: silane + heat treatment was performed with heat gun (100 oC, 2 min); Group HF: acid etching with 9.5% hydrofluoric acid for 1 min; Group HFS: acid etching with 9.5% hydrofluoric acid for 1 min + silane. Each conditioned ceramic block was bonded to the resin composite block with resin cement. Specimens sectioned perpendicular to the bonding area of 1mm2 (20 beams per group) for microtensile bond strength testing. The microtensile bond strength tests were performed in Microtensile Tester with a crosshead speed of 1mm/min. The mean bond strengths of the specimens of each block were statistically analyzed using ANOVA and Post-hoc test. Results: Analysis showed that the bond strength was significantly higher in Group HFS and there were statistically differences between the all groups (p<0.05). Conclusions: Drying the silane with 100 oC warm air significantly increased bond strength between lithium disilicate ceramics and resin cement, but hydrofloric acid etching followed by silanization is the most effective surface treatment for lithium disilicate ceramics.
Benzer Tezler
- Farklı yüzey protokollerinin lityum disilikat cam seramiklerin mikroçekme bağ dayanımına ve rezin siman bağlantısına etkisi
The effect of different surface protocols on the microtensile bond strength and resin cement bonding of lithium disilicate glass ceramics
OLKAN GÜRBÜZ
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MÜBİN SITKI ULUSOY
- Lityum disilikat seramiklerde rezin siman bağlantısı ve baskı dayanımının in vitro olarak değerlendirilmesi
The in vitro evaluation of bonding strength to resin cement and fracture strength on lithium disilicate glass ceramics
HATİCE ÖZDEMİR
Doktora
Türkçe
2013
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LÜTFÜ İHSAN ALADAĞ
- Farklı bitirme işlemleri uygulanan CAD/CAM seramiklerin termal yaşlandırma sonrası renk stabilitelerinin değerlendirilmesi
The evaluation of the color stability of CAD / CAM ceramics after different finishing procedures and thermal aging
FUNDA SOYSAL
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NERMİN DEMİRKOL
- İndirekt laminate veneer restorasyonlara uygulanan farklı tamir yaklaşımlarının makaslama bağlanma kuvveti ile değerlendirilmesi
Evaluation of shear bond strength of different repair procedures applied to indirect laminate veneers
ABDELRAHMAN WASFI FAYEZ MUSTAFA
Doktora
Türkçe
2019
Diş HekimliğiGazi ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
DOÇ. DR. SUAT ÖZCAN
- Güncel CAD/CAM seramik bloklarında farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin incelenmesi
Evaluation of different surface treatments to shear bond strength on current CAD/CAM blocks
ONUR ETÖZ
Diş Hekimliği Uzmanlık
Türkçe
2015
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MURAT KURT