Farklı taban sıcaklıklarında spray pyrolysıs metoduyla elde edilen SnO2:Sb:F ince filmlerin bazı fiziksel özelliklerine altlık sıcaklığının etkisinin araştırılması
Investigation of effect of substrate temperature on some physical properties of SnO2:Sb:F thin films obtained at different substrate temperatures by spray pyrolysis method
- Tez No: 361211
- Danışmanlar: PROF. BAHATTİN DÜZGÜN
- Tez Türü: Doktora
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Katıhal Fiziği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada spray pyrolysis (püskürtme) tekniği kullanılarak cam altlık üzerine farklı taban sıcaklıklarında yüksek ve düşük çözücü konsantrasyonunda Sb ve F katkılı SnO2 ince filmler (SnO2:Sb:F) büyütülmüş ve elde edilen filmlerin bazı fiziksel özelliklerine, altlık sıcaklığının etkisi araştırılmıştır. XRD ölçümlerinden; ince filmlerin tetragonal polikristal yapıda oldukları ve tercihli yönelimlerin (110) ve (200) boyunca olduğu görülmüştür. UV-VIS ölçümlerinden; yüksek çözücü konsantrasyonunda elde edilen filmler %30, düşük çözücü konsantrasyonunda elde edilenler ise %85 seviyelerinde saydamlığa ve 3,10-3,71 eV aralığında değişen Eg (yasak enerji aralığı enerjisi) değerlerine sahip olduğu anlaşılmış, sıcaklığın etkisi ile saydamlık ve Eg değerlerinin sürekli değiştiği görülmüştür. Yine ince film morfolojilerinin taban sıcaklığından etkilendiği, film yüzeylerinin homojen olduğu ve nano kristallerden oluştuğu gözlenmiş ve yüzey pürüzlülüğünün sıcaklık ile azaldığı anlaşılmıştır. FTIR çalışması ile SnO2 molekülünü oluşturan atomlar arası bağ titreşim frekansları bulunmuş ve Sn-O ve O-Sn-O bağlarının da kristal yapıda olduğu belirlenmiştir. Filmlerin özdirencinin taban sıcaklığına bağlı olarak 5,98 mΩ.cm'e kadar azaldığı, mobilitenin ise 38,2 cm2/V.s'e kadar arttığı müşahede edilmiştir. Fotolüminesans (PL) ölçümlerinden filmlerdeki kusurlar saptanmış olup sıcaklık ile kusur sayısının azaldığı sonucuna ulaşılmıştır. Taban sıcaklığının değişimi ile ince film özelliklerinin etkilendiği ve elde edilen sonuçların önemli derecede literatür verileriyle uyum içerisinde olduğu görülmüştür.
Özet (Çeviri)
In this study, antimony and fluorine doped tin oxide (SnO2:Sb:F) thin films with high and low solution concentrations were deposited on the glass by using spray pyrolysis technique at different substrate temperatures and it was investigated effect of substrate temperature on some physical properties of the prepared films. It was seen from XRD results that the thin films are tetragonal structure with polycrystalline and orientations preferentially along (110) and (200) directions. It was understood from UV-VIS spectrometer results that the films have 30% and 85% transmittance values for high and low solution concentration, respectively, and Eg (band gap energy) values between 3,10-3,71 eV, was seen that these Eg and transmittance values changed continuously with effect of temperatures. Also, It was seen that morphologies of the thin films were affected by substrate temperature, the surface of films was homogeneous and to be made of nano crystalline and understood that decreasing of surface roughness with temperature. The binding stretching vibrations between atoms which it form SnO2 molecule were found with FTIR studies and it was determined that binding ascribed to Sn-O and O-Sn-O was to be in the crystal. It was observed that resistivity of the films decreased until 5,98 mΩ.cm as a function of temperature and also mobility increased until 38,2 cm2/V.s. It was determined from photoluminescence (PL) measurements that films have defects and it was concluded that number of defects decreased with substrate temperature. It was seen that properties of thin films were affected by the substrate temperature and also these result mostly compatible with the results obtained from literature.
Benzer Tezler
- Buğdayda farklı melezleme teknikleri kullanarak tohum tutma oranının saptanılması
Başlık çevirisi yok
İSMAİL TÜZÜN
Yüksek Lisans
Türkçe
1986
ZiraatUludağ ÜniversitesiTarla Bitkileri Ana Bilim Dalı
PROF. DR. HALİS RUHİ EKİNGEN
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Diyabetus mellitus'da gözlenen mikrovasküler komplikasyonların prostaglandinler ile olan ilişkisi
The Relation of microvaskular complications observed in diabetes mellitus with prostoglandins
CANAN NEBİGİL
Doktora
Türkçe
1985
Eczacılık ve FarmakolojiCumhuriyet ÜniversitesiFarmakoloji Ana Bilim Dalı
YRD. DOÇ. DR. YUSUF SARIOĞLU
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- Çoklu amaçların çözümlemesinde amaç programlaması ile genelleştirilmiş ters yaklaşımı ve yem sanayiinde bir uygulama
Goal programming and generalieed inverse approaches in the multi-objective analysis and application in feed industry
HASAN BAL