Bor katkılı portland çimentosu ile üretilen betonların mühendislik özellikleri ve yüksek sıcaklık etkisi
The engineering properties and high temperature effects of concrete produced with portland cement boron mixtured
- Tez No: 353465
- Danışmanlar: DOÇ. DR. ŞEMSETTİN KILINÇARSLAN, DOÇ. DR. METİN DAVRAZ
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Borik asit [B(OH)3], çimento hidratasyonu, mekanik özellikler, nötron soğurma kapasitesi, priz süresi, yüksek sıcaklık, Borik asit, Borlu çimentolar, Portland çimentosu, Radyasyon-iyonizan, Boric acid [B(OH)3], cement hydration, the high temperatures, the mechanical properties, the neutron absorption capacity, the setting time, Boric acid, Boron containing cements, Portland cement, Radiation-ionizing
- Yıl: 2014
- Dil: Türkçe
- Üniversite: Süleyman Demirel Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Yapı Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasında, B2O3 kaynağı olarak kullanılan B[OH]3 ile birlikte priz hızlandırıcı ve harç gözenek suyunun alkanitesini artırıcı kimyasal katkı maddeleri kullanımının çimento hidratasyonuna, priz süresine ve mekanik dayanımına etkisi araştırılmıştır. Elde edilen bulgular neticesinde en yüksek %B2O3 oranında ve bu oran için en uygun kimyasal katkı maddesi ile beton üretilmiştir. Üretilen bu beton haricinde biri Borlu Aktif Belit (BAB) çimentosu diğeri Portland CEM I çimentosu kullanılarak iki ayrı kontrol betonu da üretilmiştir. Üretilen üç ayrı tip beton üzerinde çeşitli taze ve sertleşmiş beton deneyleri uygulanarak elde edilen veriler birbirleriyle karşılaştırılmıştır. Sonuç olarak bor bileşiklerinin çimento hidratasyonu kontrolü amacıyla katkı maddesi olarak kullanılabileceği, hidratasyon reaksiyonundaki gecikmenin sodyum alüminat katkısı kullanımı ile denetlenebileceği belirlenmiştir. Ancak BAB betonu örneklerinin kontrol örneklerine göre daha fazla nötron soğurma kapasitesi sergilerken, BSA betonu örneklerinden beklenen yarar sağlanamamıştır. Bu durum, BSA betonunun ağırlıkça B2O3/c oranının BAB betonuna göre yaklaşık 3 kat daha düşük olmasına bağlanmıştır. Ayrıca elde edilen sonuçlar doğrultusunda, bor katkısının betonun yüksek sıcaklıklar altındaki dayanımına olumlu bir etkisi olmadığı belirlenmiştir.
Özet (Çeviri)
In this thesis, the using of B[OH]3 as source of B2O3 and the using of chemical additives as the setting accelerator and the alkalinity increaser of the mortar pore water to the cement hydration, for setting time and mechanical strength were investigated. As a result of the findings, the concrete was produced by the appropriate chemical additives for the highest ratio % B2O3. Also two different types (control) concrete was produced by using boron modified active belite cement (BAB) and portland cement as binding material. On produced concretes as three different types, various fresh and hardened concrete experiments were performed and the data obtained were compared with each other. As a result, boron compounds may be used as additives to control hydration of cement, the delay of the hydration reactions can be controlled by use of sodium aluminate contribution was determined. However concrete samples of BAB were showed more neutron absorption capacity than the control samples, the expected benefits from concrete samples of BSA has not been provided. This stuation was thought to be due to that BSA concrete has approximately 3 times lower B2O3 / cement ratio by weight compared to BAB concrete. Also according to the results obtained was determined that there is not a positive effect of boron additives in concrete strength under the high temperatures.
Benzer Tezler
- Mechanical properties of boron blended cement concretes
Bor katkılı çimentolarla üretilen betonların mekanik özellikleri
ALİ ŞEREF CENGİZ
Yüksek Lisans
İngilizce
2011
İnşaat MühendisliğiGaziantep Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET GESOĞLU
- Beton borulara çelik lif katkısının boru özelliklerine etkisinin deneysel olarak incelenmesi
Experimental investigation of effects of steel-fiber addition to concrete pipes on their mechanical properties of the pipes
KAMURAN ARI
Yüksek Lisans
Türkçe
2004
İnşaat MühendisliğiErciyes Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF.DR. TEFARUK HAKTANIR
- Properties of polymer modified mortars and effects of fly ash and slag incorporation
Polimer modifiye harçların özellikleri ve uçucu kül ve cüruf katkısının etkisi
HAKAN ERDOĞAN ÖZMEN
Yüksek Lisans
İngilizce
2015
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA HULUSİ ÖZKUL
- Alüminyum (III) iyonunun bazı oksijen verici ligandlar ile oluşturduğu komlekslerin ve alüminyum oksidin çimento özelliklerine etkilerinin incelenmesi
Research of the aluminium (III) complexes with some oxigen donor ligans and effects of aluminium oxide on cement properties
MELEK BERKER
- Bor katkılı çimentoların özelliklerinin incelenmesi
Examination of the properties of boron blended cements
CAN DURMUŞ
Yüksek Lisans
Türkçe
2016
İnşaat MühendisliğiDokuz Eylül Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. SELÇUK TÜRKEL