Farklı döküm yöntemleri ve alaşımlar kullanılarak elde edilen kuron restorasyonların marjinal uyumlarının karşılaştırılması
Comparison of marginal fit of crown restorations fabricated with different casting techniques and alloys
- Tez No: 351350
- Danışmanlar: DOÇ. DR. SERHAT SÜHA TÜRKASLAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Kuron restorasyonlar, marjinal uyum, lazer sinterleme, metal milleme, indüksiyon döküm, konvansiyonel döküm, Dental materyaller, Dental restorasyon, Kronlar, Takma diş tabanları, Takma dişler, Crown restorations, marginal fit, laser-sintering, metal milling, induction casting, conventional casting, Dental materials, Dental restoration, Crowns, Denture bases, Dentures
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Süleyman Demirel Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Yapılan bu çalışmada bir veya birbirine komşu iki dişeksikliği nedeniyle uygulanan 3 veya 4 üyeli köprü restorasyonu söz konusu olduğunda farklımetal altyapıelde etme yöntemlerinin marjinal aralık üzerine etkileri değerlendirilmiştir. Ayrıca metal alt yapıüzerine estetik materyal olarak seramik materyalin uygulanmasısırasında gerçekleşen ısıuygulamasıve fırınlama işlemlerinin de marjinal aralığıönceden kaydedilmişmetal alt yapıüzerinde meydana getirdiği değişiklik miktarlarıda değerlendirilmiştir. Buna ilave olarak konvansiyonel döküm metodu ile diğer yeni döküm tekniklerinin birbiri ile olan uyum farklılıklarıda incelenmiştir. Çalışmamızda 6 farklıdeney grubu 4 farklıüretim tekniği ile hazırlandıve her grup için 10 adet 3 ve 4 üyelimetal destekli sabit bölümlü protez çalışmaya dahil edildi. Marjinal aralık ölçümleri her iki aşamadan sonra da gerçekleştirildi. Her bir kuron marjininde 40nokta belirlenerek ölçümler için stereomikroskop kullanıldı. Metal altyapıhazırlanmasıve seramik fırınlanma aşamalarından sonraki marjinal aralık ölçümleri sırasıyla konvasiyonel döküm grubunda 3 üyeli köprülerde 160.33 µm ve170.05 µm, 4 üyeli köprülerde 149.21 µm ve 171.61 µm, indüksiyon döküm grubunda 3 üyeli köprülerde 83.21 µm ve 90.95 µm, 4 üyeli köprülerde 81.70 µm ve 87.60 µm, lazer sinterleme grubunda 3 üyeli köprülerde 57.02 µm ve 75.37 µm, alt grubunda 27.00 µm ve 33.40 µm, 4 üyeli köprülerde 56.24 µm ve 80.63 µm, alt grubunda 31.9 µm ve 38.3 µm, metal milleme grubunda 3 üyeli köprülerde 71.31 µm ve 72.42 µm, alt grubunda 37.80 µm ve 40.40 µm, 4 üyeli köprülerde 71.06 µm ve 73.56 µm, alt grubunda 35.50 µm ve 37.70 µm olarak belirlendi ve konvansiyonel 3 ve 4 üyeli köprü gruplarıhariç diğer gruplardaki marjinal aralık değer ortalamalarıklinikte kabul edilebilir marjinal aralık seviyelerinin altında olarak tespit edildi. Tüm metal-seramik köprü gruplarında marjinal aralık değişimleri porselen fırınlama aşamasından sonra artışgösterdi ve metal milleme grubu hariç diğer tüm gruplar arasındaki aralık değişimleri anlamlı olarak farklılık gösterdi. Genel olarak, metal milleme metal seramik köprü grupları arasında fırınlama aşamalarında marjinal aralık değişiminde fark gözlenmedi.
Özet (Çeviri)
This study sought to evaluate and compare the marginal and internal fit in vitro of single unit FDP?s in different metal alloys made using four fabrication techniques, and to conclude the misfit is present. The specimens were fabricated with four different production techniques and they were evaluated within 6 groups where 10 three and four unit bridge simulations were assigned for each group. In addition, we examined the marginal adaptation of metal-ceramic bridges after the firing cycles for porcelain veeners and these scores were compared with the final marginal adaptations of the previously recorded scores for the metal framework groups. 40 points were defined at the crown margins and a stereomicroscope was used for measurements. For the conventional casting group after the metal framework production and porcelain firing cycles marginal gap values were found to be 160,33 µm and 170,05 µm in 3 unit FPD?s and 149.21 µm and 171.61 µm in 4 unit FPD?s in order. For the induction casting group the values were 83.21µm and 90.95 µm in 3 unit FPD?s and 81.70 µm and 87.60 µm in 4 unit FPD?s in order. Laser sintering 3 unit FPD?s marginal gap measurements were 57.02 µm and 75.37 µm; 27.00 µm and 33.40 µm for subgroup and 4 unit measurements were 56.24 µm and 80.63 µm; 31.9 µm and 38.30 µm for subgroup in order. Direct metal miling 3 unit FPD?s marginal gap measurements were 71.31 µm and 72.42 µm; 37.80 µm and 40.40 µm for subgroup. 4 unit measurements were 71.06 µm and 73.56 µm; 31.90 µm and 38.30 µm in order. All the groups were at the clinically acceptable levels except conventional casting method samples. In all metal-ceramic groups, the marginal gap changes occured after porcelain firing stages and marginal gap changes were found statistically different in each groups. There were no statistically significant differences in the comparison of the marginal gap measurement changes between direct metal milling groups during the firing cycles.
Benzer Tezler
- EZ43 magnezyum alaşımlarının mekanik ve biyouyumluluk davranışlarına neodinyum ve seryum alaşım elementleri ile çok yönlü dövme işleminin etkilerinin incelenmesi
Investigation of the effects of multi-directional forging process with neodinum and cerium alloy elements on the mechanical and biocompatibility behavior of EZ43 magnesium alloys
ÖZCAN BÜYÜKGENÇ
Doktora
Türkçe
2024
Mühendislik BilimleriKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HAYRETTİN AHLATCI
- Tekrarlanan döküm işleminin temel metal alaşımında biyouyumluluk üzerindeki etkisinin in vitro değerlendirilmesi
In vitro evaluation of the effect of recasting on biocompatibility of base metal alloy
PINAR DURKAYA
Doktora
Türkçe
2013
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÜLAY KANSU
- Assessment of properties and mechanical behavior of novel Al/Mg cast alloys
Yeni nesil Al/Mg dökme alaşımlarının özelliklerinin ve mekanik davranışının değerlendirilmesi
KAMİL ARMAĞAN GÜL
Doktora
İngilizce
2024
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI
PROF. DR. ÖZGÜR ASLAN
- Investigation of the structural and mechanical properties of the single crystal CMSX-4 SLS superalloy exposed to high temperature for long term
Yüksek sıcaklığa uzun süreli maruz bırakılan tek kristal CMSX-4 SLS süperalaşımın yapısal ve mekanik özelliklerinin incelenmesi
SERTAÇ ALPTEKİN
Yüksek Lisans
İngilizce
2021
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Grafen takviyeli orta entropili alaşımların bor kaplanabilirliğinin araştırılması
Investigation of boron coatability of graphene reinforced medium entropy alloys
NAZMİYE NUR KÜÇÜKELÇİ
Yüksek Lisans
Türkçe
2024
Metalurji MühendisliğiAfyon Kocatepe ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ERSAN MERTGENÇ
DR. ÖĞR. ÜYESİ RIZA KARA