Rezin coating materyaline uygulanan farklı yüzey işlemlerinin rezin siman-rezin coating arasındaki bağlanma dayanımı üzerine olan etkisinin in vitro incelenmesi
Effect of surface treatments on bonding between resin coating and resin cement
- Tez No: 342056
- Danışmanlar: DOÇ. DR. ESRA CAN
- Tez Türü: Yüksek Lisans
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental cementum, Dental materyaller, Dental çimentolar, Kompozit reçineler, Yüzey özellikleri, Dental bonding, Dental cementum, Dental materials, Dental cements, Composite resins, Surface properties
- Yıl: 2011
- Dil: Türkçe
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada rezin coating materyali üzerine uygulanan farklı yüzey işlemlerinin rezin coating - rezin siman arasındaki bağlanma dayanımı üzerine olan etkisinin in vitro incelenmesi amaçlanmıştır.Çalışmada; çekilmiş, sürmüş, çürüksüz, apeksifikasyonu tamamlanmış 40 adet üçüncü büyük azı dişi kullanıldı. Dişlerin oklüzal minesi 100 grit silikon karbit (SiC) zımpara ile kaldırıldı ve orta dentin yüzeyindeki smear tabakası (kalan dentin kalınlığı 2-3 mm) 600 grit SiC ile standardize edildi. Bütün örneklerin dentin yüzeyine çok basamaklı total etch adeziv sistem (Syntac Primer, Syntac Adhesive, Heliobond; Ivoclar Vivadent) ve akışkan kompozit (Tetric EvoFlow; Ivoclar Vivadent) ile rezin coating yapıldı. Hazırlanan örnekler 1 hafta geçici restorasyon (Systemp.Inlay; Ivoclar Vivadent) ile 37 ?C'de distile su içerisinde bekletildikten sonra rastgele olarak rezin coating materyali üzerine uygulanacak olan yüzey işlemlerine göre (asit + silan + bonding; frez + silan + bonding; frez + bonding; silika kaplama + silan + bonding; silika kaplama + bonding) 5 gruba ayrıldı (n=8).5 mm kalınlığında 7 mm çapında hazırlanan indirekt restorasyonlar (SR Adoro;Ivoclar Vivadent) dual cure rezin siman (Variolink II; Ivoclar Vivadent) ile farklı yüzey işlemleri uygulanan coating materyaline simante edildi. Örnekler 37°C distile suda 24 saat bekletildikten sonra, bağlanma yüzeyine dik olacak şeklinde önce mezio-distal, daha sonra da vestibülo-lingual yönde kesildi ve 1x1 mm boyutunda dentin-kompozit çubukları hazırlandı. Çubukların pulpa üzerinde kalan dentin miktarı 2-3 mm arasında olanları seçildi ve universal test cihazına (Instron 3345, ABD) adapte edilen Bencor Multi T Testing Device'a bağlanarak 1mm/dak ile kopana kadar çekme kuvveti uygulandı. Mikrotensil bağlanma dayanımı ölçümlerinin (MPa) aritmetik ortalama ve standart sapma değerlerine ilişkin bulgular one way ANOVA ve Tukey post hoc testi ile istatistiksel olarak analiz edildi (p<0,05). Silika kaplama+silan+bonding grubu (41,05 ± 7,02 MPa) istatistiksel olarak en yüksek bağlanma değerini gösterdi (p<0,05). Frez+silan+bonding grubu (32,91 ± 6,66MPa) ile silika kaplama+bonding grupları (34,27 ± 5,94 MPa) arasında istatistiksel olarak anlamlı fark bulunmadı (p>0,005), ancak her iki grup da silika ivkaplama+silan+bonding grubuna göre istatistiksel olarak anlamlı derecede düşük bağlanma değeri gösterdi (p<0,05). Asit+silan+bonding grubu (27,27 ± 5,75 MPa) ile frez+bonding grubu (24,70 ± 5,85 MPa) arasında istatistiksel olarak fark bulunmadı(p>0,05) ve bu gruplar istatistiksel olarak anlamlı derecede en düşük bağlanma değerleri gösterdi (p<0,05).Bu in vitro çalışmanın sonuçlarına göre, rezin coating - rezin siman bağlanmasında mekanik retansiyon ve silan uygulamasının adezyonu arttırdığı saptanmıştır. Silan ile birlikte uygulanan silika kaplama en yüksek bağlanma performansı gösteren tekniktir.
Özet (Çeviri)
The aim of this in vitro study was to evaluate the effect of different surface treatments on resin coating material on bonding between resin coating and resin cement.Occlusal enamel of 40 extracted noncarious human third molars were removed using 100 grit SiC paper and smear layer on the mid-coronal dentin was standardized using 600 grit SiC. Resin coating on mid-coronal dentin was performed with a multi step etch&rinse adhesive system (Syntac Primer, Syntac Adhesive, Heliobond; Ivoclar Vivadent) and a flowable resin composite (Tetric EvoFlow, Ivoclar Vivadent). All resin coated specimens were temporized with a temporary filling material (Systemp.Inlay, Ivoclar Vivadent) and kept in distilled water for 7 days at 37?C. Then, the specimens were randomly divided into 5 groups according to the surface treatments (etching+silan+bonding, bur+silan+bonding, bur+bonding, silica coating+silan+bonding, silica coating+bonding) applied on resin coating material (n=8).Indirect restorations (SR Adoro, Ivoclar Vivadent) 5 mm in thickness and 8 mm in diameter were luted with a dual cure resin cement (Variolink II, Ivoclar Vivadent) according to the manufacturer's instructions. After storage in distilled water for 24 hours at 37?C, each specimen was sectioned first mesiodistally into serial slabs, then vestibulolingually using the low speed diamond saw under water lubrication in order to obtain 1x1 mm composite-dentin sticks. Microtensile bond strengths were determined from that specimens which remaining dentin thickness were 2 and 3 mm. Microtensile bond strength (MPa) was evaluated using Bencor Multi Testing device attached to a universal testing machine (Instron 3345, USA). Data were analyzed using one way ANOVA and post hoc Tukey tests (p<0,05). Silica coating+silan+bonding group showed significantly the highest bond strength (41,05 ± 7,02 MPa) (p<0,05). There were no significant differences between bur+silan+bonding (32,91 ± 6,66 MPa) and silica coating+bonding (34,27 ± 5,94 MPa) groups (p>0,05) whereas they showed significantly lower bond strengths than silica coating+silan+bonding group (p<0,05). There were also no significant differencesbetween etching+silan+bonding (27,27 ± 5,75 MPa) and bur+bonding (24,70 ± 5,85MPa) (p>0,05) which showed significantly the lowest bond strengths (p<0,05).viThe results of this in vitro study indicated that mechanical retention and silan application improved adhesion between resin coating-resin cement. In comparison to other surface treatments, silica coating with additional silane application showed the highest bonding performance
Benzer Tezler
- Farklı yüzey uygulamalarının ve farklı rezin simanların cad/cam freze tekniği ile üretilen zirkonya post sisteminde retansiyona ve dirence etkilerinin invitro olarak değerlendirilmesi
Evaluating the effects of different surface treatments and different resin luting agents in the zirconia post system which produced by CAD/CAM copy-milling fabricating techniques for retention and resistance: Invitro study
DERYA TOPRAK
Doktora
Türkçe
2011
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ZELAL SEYFİOĞLU POLAT
- Zirkonya alt yapıya uygulanan farklı yüzey işlemlerinin zirkonya-siman arasındaki fiziksel bağlanma özelliklerine etkisinin araştırılması
Investigation of effects of surface treatment applied zirconia copings between zirconia-cement physical binding properties
BENGİSU YILDIRIM
Doktora
Türkçe
2014
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. AHMET SARAÇOĞLU
- Güncel CAD/CAM hibrit seramiklere uygulanan farklı yüzey işlemlerinin makaslama bağlanma dayanımına etkisinin değerlendirilmesi
Evaluation of the effects of different surface treatments on the bonding strength of recent CAD/CAM hybrid ceramics
MERVE TOKGÖZ ÇETİNDAĞ
Diş Hekimliği Uzmanlık
İngilizce
2017
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AYŞE MEŞE
- Farklı yüzey işlemlerinin zirkonya ile rezin siman arasındaki bağlantı kuvveti üzerine etkisi
The effect of different surface treatments on the bond strength between zirconia and resin luting cement
GÖKHAN ÇİÇEKCİ
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LALE KARAAĞAÇLIOĞLU
- Hemen dentin örtüleme sonrası uygulanan geçici yapıştırma simanın farklı temizleme yöntemleri ile uzaklaştırılmasının dual cure rezin simanın dentine makaslama bağlanma dayanımına etkisi
The effect of removing temporary luting cement with differentcleaning methods applied immediate dentin sealing on the shearbond strength of dual-cure resin cement to dentin
ZEYNEP AYDIN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CEMİLE KEDİCİ ALP