Deniz suyunun farklı tip ve dozajdaki mineral katkılı kendiliğinden yerleşen harçların mekanik ve durabilite özelliklerine etkisi
Effects of sea water to mechanical and durability features of different type and dosage self-compacting mineral additive grouts
- Tez No: 334590
- Danışmanlar: YRD. DOÇ. DR. MEHMET KARATAŞ
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Uçucu kül, Silis dumanı, Magnezyum sülfat atağı, Deniz suyu etkisi, dayanım, dayanıklılık, Fly Ash, Silica Fume, Magnesium Sulfate Attack, Effects of Sea Water, Strength, Endurance
- Yıl: 2013
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Yapı Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Gerçekleştirilen deneysel çalışmada mineral katkı olarak uçucu kül (UK) ve silis dumanı (SD) ile üretilen harçların deniz suyu ve sülfat ortamlarındaki performansları araştırılmıştır. Bu kapsamda %10, %20 ve %30 UK ikameli; %6, %9, %12 ve %15 SD ikameli ve %10UK+%6SD, %10UK+%9SD, %10UK+%12SD, %10UK+%15SD, %20UK+%6SD, %20UK+%9SD ikameli ikili karışımlar olmak üzere kontrol harcıyla birlikte 14 seri harç numuneleri üretilmiştir. Toplam 182 adet 40×40×160 mm harç numuneleri hazırlanmış ve farklı kür sürelerinde sırasıyla şehir şebeke suyu, %10 magnezyum sülfat ve Akdeniz?den temin edilen deniz suyunda bekletilmiştir. Tüm kür türleri için harç numunelerinin farklı kür sürelerinde eğilmede çekme dayanımları ve basınç dayanımları ölçülmüş ve aynı zamanda numunelerde meydana gelen yüzeysel bozulmalar periyodik olarak gözlemlenmiştir. Çalışma sonucunda standart küre maruz harçlarda en yüksek dayanıma %10 UK içeren harç numunesinin sahip olduğu belirlenmiştir. Magnezyum sülfat atağına maruz harçlarda yüzey yumuşamasıyla birlikte çatlak oluşumu türünde bozulmalara rastlanmıştır. Magnezyum sülfat çözeltisinde bekletilen harçların eğilmede çekme dayanımlarının arttığı, basınç dayanımlarının belirgin şekilde değişmediği görülmüştür. Deniz suyuna maruz harçlarda tüm numunelerin eğilmede çekme dayanımları artmış ve basınç dayanımı sonucuna göre en iyi direnci UK içeren harçların, özellikle de %10 UK içeren numunenin gösterdiği belirlenmiştir.
Özet (Çeviri)
In performed experimental study, performances of trouts producted with fly ash (UK) and silica fume (SD) used as mineral additives at sea water and sulfate envorinments were investigated. In this context, substituted with 10%, 20% and 30% UK; subsituted with 6%, 9%, 12% and 15% SD and substituted with 10%UK+6%SD, 10%UK+9%SD, 10%UK+12%SD, 10%UK+15%SD, 20%UK+6%SD, 20%UK+9%SD binary mixtures and with control trout, total of 14 series trout samples were produced. A total of 182 pieces of 40 × 40 × 160 mm trout specimens prepared and with different curing periods allowed to stand in city water, %10 magnesium sulfate and sea water obtained from Mediterranean, respectively. For all cure specimens, flexural strength and compressive strength of trout samples at different curing periods were measured and surface distortions occurred on samples in time also observed. As a result of study, substituted with %10 UK samples determined as has highest strength to standard curing procedures within all trout samples. In trout samples cured with magnesium sulfate attack, deteriorations like surface softening and formation of cracks were found. In trout samples kept in magnesium sulfate solutions, increased flexural strength observed but compressive strength was not changed significantly. In all of samples exposed to sea water, increased flexural strength was observed and as a result of compressive strength results, trout substituted with UK, especially substituted with 10% UK determined as has the best resistance.
Benzer Tezler
- Haliç dip tarama çamuru ve maden atığının geotekstil tüp ile susuzlaştırılması ve geoteknik mühendisliği açısından değerlendirilmesi
Dewatering of Golden Horn dredged sludge and mining waste using geotextile tubes and evaluation of these in terms of geotechnical engineering
ÜMİT KARADOĞAN
Doktora
Türkçe
2021
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BERRAK TEYMÜR
- Deniz suyunun çimento tipi farklı harçların mekanik ve durabilite özelliklerine etkisi
Sea water effect on the mechanical and durability properties of different types of cement mortars
EBRU ERTEN
Yüksek Lisans
Türkçe
2009
İnşaat MühendisliğiDokuz Eylül Üniversitesiİnşaat Mühendisliği Bölümü
DOÇ. DR. SELÇUK TÜRKEL
- Simultaneous salt and boron removal from seawater using reverse osmosis process
Ters osmoz prosesi kullanarak deniz suyundan eşzamanlı bor ve tuz giderme
SÜER KÜRKLÜ
Yüksek Lisans
İngilizce
2016
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ŞERİFE BİRGÜL ERSOLMAZ
- Sea ice observations & maritime meteorology records during Turkish antarctic expedition–I (TAE-I)
Ulusal antarktik bilim seferi–I (TAE-I)'de deniz buzu gözlemleri ve denizcilik meteorolojisi kayıtları
SİNAN YİRMİBEŞOĞLU
Yüksek Lisans
İngilizce
2018
Denizcilikİstanbul Teknik ÜniversitesiDeniz Ulaştırma İşletme Mühendisliği Ana Bilim Dalı
DOÇ. DR. BURCU ÖZSOY
- Çanakkale Boğazı, Gemlik körfezi ve İzmit körfezi'nin fiziko-kimyasal özelliklerinin Ulva rigida C. Agardh, 1823' nın biyokimyasal özelliklerine ve yetiştiricilik potansiyeline etkisi
Effects of physico-chemical properties of Çanakkale strait, Gemlik bay and İzmit bay on biochemical properties and aquaculture potential of Ulva rigida C. Agardh, 1823
DENİZ TAŞÇI
Yüksek Lisans
Türkçe
2022
Su ÜrünleriYalova ÜniversitesiSu Ürünleri Ana Bilim Dalı (disiplinlerarası)
PROF. DR. BETÜL GÜROY