Kükürt dioksitin sulu çözeltileriyle üleksit' ten borik asit ve sodyum sülfit üretiminin incelenmesi
İnvesitgation of production of boric acid and sodium sulfite from ulexite by aqueous sulfur dioxide solutions
- Tez No: 322574
- Danışmanlar: PROF. DR. M.MUHTAR KOCAKERİM
- Tez Türü: Doktora
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Borik asit, Kükürt dioksit, Optimizasyon, Sodyum sülfit, Taguchi yöntemi, Üleksit, Boric acid, Sulfur dioxide, Optimization, Sodium sulfite, Taguchi method, Ulexite
- Yıl: 2012
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Uleksit Türkiye'de bol miktarda bulunan bir bor mineralidir ve dünya çapında büyük bir endüstriyel ve ekonomik değere sahiptir. Bu çalışmanın amacı, Taguchi metodunu kullanarak, sulu çözeltilerde kükürt dioksit gazı ile üleksitten borik asit ve sodyum sülfit üretiminde en uygun çalışma şartlarının belirlenmesidir. Sodyum sülfit üretmek için iki farklı çözündürme prosesi uygulanmıştır. İlk proseste sıcaklık, katı sıvı oranı, tane boyutu, karıştırma hızı ve zaman parametreler olarak belirlenmiş ve kükürt dioksit ile doyurulmuş sularda borik asit ve sodyum sülfit üretiminin optimum şartları belirlenmiştir. Bu parametreler için sıcaklık (90°C), katı/sıvı oranı (0.25 g/mL), tane boyutu (150 µm), karıştırma hızı (600 dev/dak) ve zaman (30 dak) optimum şartlar olarak belirlenmiştir. Bu şartlarda yapılan üretim çalışmalarında %99 saflıkta borik asit ve %85 saflıkta sodyum sülfit üretilmiştir.İkinci proseste pH, sıcaklık, katı sıvı oranı, tane boyutu, karıştırma hızı ve zaman parametreler olarak belirlenmiş Kükürt dioksit le pH kontrol edilerek borik asit ve sodyum sülfit üretimi denemeleri yapılmıştır. Bu parametreler için pH (4,5), sıcaklık (90°C), katı/sıvı oranı (0.25 g/mL), tane boyutu (150 µm), karıştırma hızı (600 dev/dak) ve zaman (30 dak) optimum şartlar olarak belirlenmiştir. Bu şartlarda yapılan üretim çalışmalarında %99 saflıkta borik asit ve %95 saflıkta sodyum sülfit üretilmiştir.
Özet (Çeviri)
Ulexite (Na2O.2CaO.5B2O3.16H2O), which is boron mineral, is abundant in Turkey, has a high industrial and economical value in worldwide. The aim of this study is to determine some optimum operating conditions for production of boric acid and sodium sulfite from ulexite by using sulfur dioxide gas in aqueous media by using Taguchi method. Two different dissolution processes were applied to produce boric acid and sodium sulfite. In the first process temperature, solid to liquid ratio, particle size and stirring speed were chosen as parameters and optimum requirements of boric acid and sodium sulfite production were determined in SO2 saturated water. The optimum conditions for these parameters were determined as reaction temperature (90°C), solid to liquid ratio (0.25 g/mL), reaction time (30 min), stirring speed (600 rpm) and particle size (150 µm). In these conditions, boric acid and sodium sulfite are produced in purity of 99 and 85 percent.In the second process, pH, temperature, solid to liquid ratio, particle size, stirring speed and time were chosen as parameters, and production of boric acid and sodium sulfite attempts have been made by keeping pH under control with dosage of SO2. Optimum conditions for these parameters were determined as reaction temperature (90°C), solid to liquid ratio (0.25 g/mL), reaction time (30 min), stirring speed (600 rpm) and particle size (150 µm), respectively. In these conditions, boric acid and sodium sulfite are produced in purity of 99 and 95 percent.
Benzer Tezler
- Tronanın farklı sistemlerdeki sülfatasyon kapasitesinin belirlenmesi
Determination the sulfation capacity of torona in different systems
GÜL ŞENTÜRK
Yüksek Lisans
Türkçe
2002
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. AYŞEGÜL ERSOY MERİÇBOYU
- Kalsiyum hidroksitin hidratasyon yoluyla aktivasyonu
Activation of calcium hydroxide by hydration
NİLÜFER ERDOĞAN
Yüksek Lisans
Türkçe
1997
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. AYŞEGÜL ERSOY (MERİÇBOYU)
- Alkali ortamda hidratlanarak aktiflenmiş uçucu Kül-Ca(OH)2 sorbentlerinin sülfatasyonu
Sulphation of fly ASH-Ca(OH)2 sorbents activated by hydration in an alkali media
ESRA GÜMÜŞKILIÇ
Yüksek Lisans
Türkçe
1999
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. AYŞEGÜL ERSOY-MERİÇBOYU
- Burdur ili mermer sektörünün kurumsal ve ekonomik yapısı
İnstitutional and economic structure of marble sector in burdur
AHMET SARITAŞ
- Investigation of capacitive behaviour of emulsion polymerized pedot and its nanocomposites
Emülsiyon polimerizasyonu ile sentezlenen pedot ve nanokompozitlerinin kapasitif özelliklerinin incelenmesi
DENİZ GÜLERCAN
Doktora
İngilizce
2019
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. ABDÜLKADİR SEZAİ SARAÇ