Mechanical properties of plasma surface modified calcium carbonate/pp composites
Yüzey özellikleri plazma ile değiştirilmiş kalsiyum karbonat/pp kompozitlerinde kbazı mekanik davranışlar
- Tez No: 29411
- Danışmanlar: PROF. DR. GÜNERİ AKOVALI
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Plazma Polimerleşmesi, Dolgu Maddesi, Kalsiyum Karbonat, Polipropilen, Mekanik Özellikler, Kompozitler, Plasma Polymerization, Filler, Calcium Carbonate, Polypropylene, Mechanical Properties, Composites
- Yıl: 1993
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
oz YÜZEY ÖZELLİKLERİ PLAZMA İLE DE?İŞTİRİLMİŞ KALSİYUM KARBONAT/PP KOMPOZİTLERİNDE BAZI MEKANİK DAVRANIŞLAR AKMAN, M. Alper Yüksek Lisans Tezi, Kimya Anabilim Dalı Tez Yöneticisi: Prof. Dr. Güneri AKOVALI Mayıs 1993, 68 sayfa Bu çalışmada kalsiyum karbonatın yüzey modifikasyonu plasma tekniği ile polimerleştirilmiş asetilen ile yapılmış ve yüzey modifikasyonunun kalsiyum karbonat/PP kompozit sistemindeki mekanik özellikler üzerine olan etkisi incelenmiştir. İki değişik polimerleşme koşulu belirlenmiş ve uygulanmıştır. Örneklerin gerilim direnci ve uzama yüzdeleri İnstron Gerilim Test Cihazı ile ölçülmüştür. Young modulu ve loss modulu değerleri Du Pont 981 DMA cihazı ile test edilmiştir. PTIR spektrometresi ve CHN analiz cihazı ile, asetilenin plasma polimerleşmesi sonunda elde edilen ürünün yapısı incelenmiştir. Gerilim direnci örneklerinin kopma yüzeyleri SEM ile incelenmiştir. Bazı plazma polimerleşme koşullarında yapılmış yüzey modifikasyonlu kalsiyum karbonat içeren kompozitlerin daha fazla uzama yüzdelerine sahip olduğu gözlenmiştir.
Özet (Çeviri)
ABSTRACT MECHANICAL PROPERTIES OF PLASMA SURFACE MODIFIED CALCIUM CARBONATE/PP COMPOSITES AKMAN, M. Alper M.S. in Chemistry Supervisor: Prof. Dr. Güneri AKOVALI May, 1993, 68 pages In this study calcium carbonate was surface modified by using plasma polymerized acetylene and the effect of surface modification on mechanical properties of calcium carbonate/PP composites was investigated. Two different plasma polymerization conditions were selected and applied. Mechanical properties such as tensile strength and percent elongation were measured by Instron Tensile Testing Machine and Young's modulus and loss modulus measurements were done by Du Pont 981 DMA. FTIR spectrometer was used to get detailed information about the structure of polyacetylene which is produced by the plasma polymerization of acetylene. The tensile fracture surfaces of composites was investigated by SEM technique. It was observed that some composites which contain surface modified calcium carbonate have higher percent elongation.
Benzer Tezler
- Mechanical properties of plasma surface modifield carbon black/ SBR composites
Yüzey özellikleri plazma ile değiştirilmiş karbon siyahı/SBR kompozitlerinde bazı mekanik davranışlar
NOSRAT KAJOUEI
- Compatibilization studies of rf-plasma modified LDPE-PVC blends
RF-plazma ile modifiye edilmiş zope-pvc alaşımlarını uyumlaştırma çalışmaları
TAN TONGUÇ TORUN
- The Effects of plasma polymer modification of pvc surfaces on the properties of ABS/PVC blends
Yüzeyleri plazma ile modifiye edilmiş PVC kullanımının ABS/PVC karışımlarındaki özelliklere etkisi
SEPİDEH YADOLLAHİ
- Studies with epoxy modified by recyded rubber
Geri kazanılmış lastik ile modifiye edilmiş epoksi üzerine çalışmalar
ERAY SİPAHİ SAĞLAM
Yüksek Lisans
İngilizce
1999
Polimer Bilim ve TeknolojisiOrta Doğu Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. GÜNERİ AKOVALI
- Static and dynamic mechanical properties of (bauxite, and carbon black) filled SBR vulcanizates: Effects of filler surface modification on properties
Başlık çevirisi yok
İLHAN ÜLKEM
Doktora
İngilizce
1990
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. GÜNERİ AKOVALI