Pcessureless sintering of silcon nitride with yttrium oxide as sintering additives
Silisyum nitrür tozlarının ytrium oksit ve aluminyum oksit katkıları ile basınçsız sinterlenme özellikleri
- Tez No: 29251
- Danışmanlar: PROF. DR. MUHARREM TİMUÇİN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Silisyum Nitrür, Sinterlenme, Katkı Malzemeleri, Çöktürme, Alüminyum oksit, Silisyum, Sinter, İtriyum oksit, Silicon Nitride, Sintering, Sintering Additives, Coprecipitation, Aluminum oxide, Silicon, Sinter, Yttrium oxide
- Yıl: 1993
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
oz SİLİSYUM NİTRÜR TOZLARININ YTTRİUM OKSİT VE ALÜMİNYUM OKSİT KATKILARI İLE BASINÇSIZ SiNTERLENME ÖZELLİKLERİ SİLAN, Murat Yüksek Lisans Tezi, Metalürji Mühendisliği Ana Bilim Dalı Tez Yöneticisi: Prof. Dr. Muharrem Timuçin Mayıs, 1993, 107 sayfa. Sinterleme sıcaklığı., katkı, malzemesi kompozisyonu ve hazıırlama yönteminin silisyum nitrür tozlarının yoğunlaştırma davranışı üzerine etkileri araştırılmıştır. Gerek mekanik olarak karıştırılmış, gerekse“beraber”çöktürülmüş, ağırlıkça % 10 sabit miktarda Y2O3, AI2O3 ve Y203-Aİ203 karışımları, sinterleme katkıları olarak kullanılmıştır. Tek oksit katkılı sistemlerde kötü sinterlenme elde edilmesine rağmen, Y2O3-AI2O3 karışık oksit katkısı için 1700° C sıcaklıkta teorik değerin %95* ine varan yoğunluklar bulunmuştur. Yttrium ve alüminyum nitrat solüsyonlarından hidroksit çöktürülmesi ile hazırlanan numunelerin sinterlenmiş yoğunluklarını %97.5'e çıkaran, düzgün sinterleme katkı malzemesi dağılımları sağlamıştır. Yüksek pişirme sıcaklıklarının sinterlenmiş yoğunluklarını geliştirdiği bulunmuştur.
Özet (Çeviri)
ABSTRACT PRESSURELESS SINTERING OF SILICON NITRIDE WITH YTTRIUM OXIDE AND ALUMINUM OXIDE AS SINTERING ADDITIVES SİLAN, Murat M.S. in Metallurgical Engineering Supervisor: Prof. Dr. Muharrem TİMUÇİN July, 1993, 107 pages. The effect of sintering temperature, additive composition and processing route, on the densification behavior of silicon nitride powders were investigated. Either mechanical mixing or coprecipitation of a constant amount of 10 wt% of Y203, AI2O3 and Y2O3-AI2O3 mixtures were used as sintering additives. Although poor sinterability was found for single oxide addition, densities up to 95% of the theoretical were achieved at 1700 °C for mixed Y2O3-AI2O3 oxide additives. By the coprecipitation of yttrium and aluminum hydroxide from their nitrate solution, a uniform distribution of the sintering additives was accomplished, which upgraded the sintered densities of the compacts to 97.5%. High sintering temperatures were found to be effective to improve sintered densities.
Benzer Tezler
- Pressureless sintering of single B-and (?-B) sialons with the aid of oxynitride glasses
B-sialon ve (?-B)-sialon seramiklerinin oksinitrür katkıları ile basınçsız sinterleme örnekleri
İLKSEN HİLAL YILDIR
Yüksek Lisans
İngilizce
1996
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUHARREM TİMUÇİN
- Effect of carbon and boron additions on pressureless sintering of sılıcan carbide
Karbon ve Boron katkılarının silüsyum karbürün basınçsız sinterlenmesine olan etkisi
CUMHUR YAĞCI
Yüksek Lisans
İngilizce
1993
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ABDULLAH ÖZTÜRK
- Metal infiltre edilmiş mikro poroz karbon kompozitlerin aşınma ve sürtünme davranışının karakterizasyonu
Başlık çevirisi yok
GÜLTEKİN GÖLLER
Doktora
Türkçe
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. ADNAN TEKİN
- Tane sınırı fazı azaltılmış alfa-beta sialon seramikleri
Alfa-beta sialon ceramics with reduced amount of grain boundry phase
EMRAH DÖLEKÇEKİÇ
Yüksek Lisans
Türkçe
1999
Seramik MühendisliğiAnadolu ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
DOÇ. DR. HASAN MANDAL
- Mo-Si-B esaslı intermetalik plasma sprey kaplama malzemesinin yapı ve özelliklerinin incelenmesi
Investigation on the structure and properties of Mo-Si-B based intermetallic plasma sprayed material
S. CEM OKUMUŞ