Farklı karıştırma tekniklerinin mineral trioksit agregatının bazı fiziksel özelliklerine etkisi
The effect of various mixing techniques on some physical properties of mineral trioxide aggregate
- Tez No: 282342
- Danışmanlar: PROF. DR. MAHİR GÜNDAY
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Eğilme dayanımı, Kök kanal dolgu materyalleri, Sıkıştırma dayanımı, Tomografi, Ultrasonik dalgalar, X ışını kırınımı, Dental materials, Bending strength, Root canal filling materials, Compressive strength, Tomography, Ultrasonic waves, X ray diffraction
- Yıl: 2011
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Diş Hastalıkları ve Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
1990'ların ortalarında piyasaya sürülen mineral trioksit agregatı (MTA) cerrahi olan veya olmayan endodontik girişimlerde yaygın kullanım alanına erişmiş bir materyaldir. Bu tez çalışmasının amacı, mineral trioksit agregatının değişik karıştırma teknikleriyle karıştırılıp, ultrasonik vibrasyon kullanılarak yerleştirilmesinin, materyalin sıkıştırma ve eğilme dayanımı, porözitesi ve hidrasyonuna etkilerinin araştırılmasıdır. Çalışmamızda, ProRoot MTA ve MTA Angelus kullanılmıştır. Örnekler, 1 gr toza 0.34 gr distile su eklenerek, 3.22 MPa sabit basınç altında 1 dk boyunca konvansiyonel kondensasyon uygulanarak veya kapsüller içerisinde 30 sn boyunca 4500 rpm hızda mekanik karıştırma metodu kullanılarak karıştırılmıştır. Karıştırılan örneklerin yarısı 30 sn boyunca indirekt ultrason uygulanarak yerleştirilmiştir. Hazırlanan örneklere Universal test cihazı ile sıkıştırma dayanımı ve eğilme dayanımı testleri uygulanmıştır. Porözite tayini üç boyutlu olarak mikro bilgisayarlı tomografi kullanılarak, materyalin hidrasyon özellikleri X-ışını kırınım analizi (XRD) uygulanarak incelenmiştir.Çalışmamızda, sıkıştırma ve eğilme dayanımı açısından ProRoot MTA, MTA Angelus'tan daha yüksek değerler göstermiştir (p<0.05). Sıkıştırma dayanımı açısından mekanik karıştırma tekniği, konvansiyonel kondensasyondan daha yüksek değerler göstermiştir (p<0.05). Gruplar arasında porözite açısından anlamlı bir fark bulunmamasına rağmen eğilme dayanımı ile orta, sıkıştırma dayanımı ile zayıf dereceli negatif korelasyon görülmüştür. Kalsiyum hidroksit faz formasyonu ProRoot MTA gruplarında karıştırma ve yerleştirme tekniklerinden etkilenmezken, MTA Angelus için sadece mekanik karıştırma uygulanan gruplarda görülmüştür. Çalışmamızın sonuçları ışığında, ProRoot MTA'nın, MTA Angelus'tan daha üstün sıkıştırma ve eğilme dayanımı gösterdiği ve her iki MTA çeşidi için mekanik karıştırma tekniğinin materyalin sıkıştırma dayanımını ve kalsiyum hidroksit faz formasyonunu olumlu yönde etkilediği bulunmuştur.
Özet (Çeviri)
Introduced into the dental field in the mid 1990s; mineral trioxide aggregate (MTA) has gained widespread use for both surgical and non-surgical endodontic treatments. The purpose of this study was to evaluate the effect of trituration of encapsulated MTA and conventional condensation as mixing techniques and indirect ultrasonic activation as a placement technique on compressive strength, flexural strength, porosity and hydration of mineral trioxide aggregate. In this study, ProRoot MTA and MTA Angelus were used. One gram of each powder was mixed with a 0.34 g aliquot of distilled water. Samples were mixed by using either trituration of capsules for 30 sec at 4500 rpm or application of condensation pressure of 3.22 MPa for 1 min. Half of the samples were placed using indirect ultrasonic vibration. Compressive strength and flexural strength tests were applied using Universal testing machine. Porosity evaluation was made using micro-computed tomography. Hydration characteristics were identified using X-ray diffraction analysis (XRD).The mean compressive strength and flexural strength values of ProRoot MTA were higher than those of MTA Angelus regardless of the mixing and placement techniques applied (p<0.05). Compressive strength values of trituration technique were higher than those of conventional condensation technique (p<0.05). Although the results of porosity analysis were not statistically significant, a medium negative correlation was found between porosity and flexural strength and a weak negative correlation was found between porosity and compressive strength. According to the findings of XRD, calcium hydroxide phase formation was not effected in ProRoot MTA groups whereas it was observed only in trituration groups of MTA Angelus. According to our results ProRoot MTA showed better compressive and flexural strength than MTA Angelus. Preparing MTA slurry using trituration enhanced the compressive strength and calcium hydroxide phase formation of the material.
Benzer Tezler
- Apeksifikasyon tedavisinde farklı tekniklerle yerleştirilen MTA apikal tıkacının dolgu kalitelerinin mikro BT yöntemi ile karşılaştırmalı olarak incelenmesi
Comparative micro-CT evaluation of the sealing quality of MTA apical plug placed with various techniques in apexification therapy
SELEN NİHAL SARAÇ
- Comparison of beta, neutron and gamma attenuation properties of pmma/colemanite composites
Pmma/kolemanit kompozitlerin beta, nötron ve gamma zayıflatma özelliklerinin karşılaştırılması
SHIMA MEHRANPOUR
Yüksek Lisans
İngilizce
2020
Nükleer Mühendislikİstanbul Teknik ÜniversitesiEnerji Bilimi ve Teknolojileri Ana Bilim Dalı
PROF. DR. NİLGÜN BAYDOĞAN
- Controlled temozolomide release with HPMC modified montmorillonite
HPMC modifiyeli montmorillonit ile kontrollü temozolomit salımı
FIROOZEH PANAHIANLARKEY
Yüksek Lisans
İngilizce
2024
Eczacılık ve FarmakolojiAfyon Kocatepe ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
DOÇ. DR. HAKAN ÇİFTÇİ
- Çevresel koşulların bazı mikroalg türlerinin büyümesi üzerine etkisinin araştırılması
The Investigate of environmental factors on growth of some microalgae
DENİZ TAPAN
Yüksek Lisans
Türkçe
2006
Su ÜrünleriEge ÜniversitesiSu Ürünleri Yetiştiriciliği Ana Bilim Dalı
PROF. DR. ŞEVKET GÖKPINAR
YRD. DOÇ. DR. ALİ YILDIRIM KORKUT
- Biyokütle kaynaklarının tavuk gübresinin yanma kalitesine etkisi
Fuel properties and incineration behavior of poultry litter blended with sweet sorghum bagasse and pyrolysis oil
ÜMİT PEHLİVAN
Yüksek Lisans
Türkçe
2024
EnerjiSakarya ÜniversitesiYenilenebilir Enerji Sistemleri Ana Bilim Dalı
PROF. DR. SAİM ÖZDEMİR