Klinoptilolit katkılı cam iyonomer simanın fluor salınımı ve antibakteriyel özelliklerindeki değişimin incelenmesi
Analysis of exchange in the fluoride release and antibacterial properties of clinoptilolite added glass ionomer cement
- Tez No: 281719
- Danışmanlar: PROF. DR. GÜLÜMSER EVLİOĞLU
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Antienfektif ajanlar, Cam iyonomer çimentoları, Dental cementum, Dental materyaller, Dental çimentolar, Flüor, Klinoptilolit, Lactobacillus casei, Streptococcus mutans, Anti infective agents, Glass ionomer cements, Dental cementum, Dental materials, Dental cements, Fluorine, Clinoptilolite, Lactobacillus casei, Streptococcus mutans
- Yıl: 2010
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Cam iyonomer simanlar fluor salınımı özellikleriyle önem kazanmaktadırlar. Klinoptilolit, alumünosilikat yapısında bir mineraldir. Absorban, iyon değiştirme, antibakteriyel özellikleriyle dikkat çekmektedir.Bu çalışmanın amacı, cam iyonomer simana klinoptilolit eklenerek ideal özelliklere sahip bir siman materyali oluşturmaktır. Bu amaçla kontrol grubu ve test grupları oluşturularak fluorid salınımı ve antibakteriyel etkinlik incelenmiştir. Test grupları cam iyonomer simana % 5 (Grup B), % 10 (Grup C) ve % 15 (Grup D) oranlarında klinoptilolit eklenerek hazırlanmıştır. Kontrol grubu olarak (Grup A) katkısız cam iyonomer siman kullanılmıştır. Fluorid salınımı ölçümü için her bir grup için 10'ar adet siman örneği hazırlanmıştır. Örneklerin 1., 2., 3., 4., 7., 14., 21., 28., 35. ve 42. günlerde Orion 720A+ marka iyon selektif elektrod cihazı ve Orion Fluorid elektrodu kullanılarak fluor salınımı ölçümleri yapılmıştır. Antibakteriyel etki direkt kontakt test yöntemi ile Streptococcus mutans ve Lactobacillus casei standart suşları kullanılarak yapılmıştır. 96 kuyucuklu mikropetrinin tabanında sertleştirilen siman örneklerinde başlangıç, 1., 2., 3., 17., 18.ve 24. saatlerde bakteri yoğunlukları 620 nm de mikropleyt spektrofotometrisinde değerlendirilmiştir.İstatistiksel analizler NCSS-PASS 2008 paket programı ile yapılmıştır. Verilerin değerlendirilmesinde Kruskal Wallis , Mann Whitney U, Friedman ve Wilcoxon testi kullanılmıştır.Bu çalışmanın sınırları içinde test gruplarının fluor salınımı ve antibakteriyel etkinlik açısından kontrol grubuna anlamlı olarak bir üstünlüğü saptanmamıştır. Sonuç olarak, klinoptilolit cam iyonomer simanın kimyasal yapısında pasif olarak kalmıştır. Cam iyonomer siman formülasyonun yeniden yapılandırılacağı çalışmalarda klinoptilolitin etkinliğinin değerlendirilmesine gereksinim vardır.
Özet (Çeviri)
Importance of glass ionomer cements are increased for their fluoride release. Clinoptilolite is an aluminosilicate structured mineral and is noticed with absorbent, ion change and antibacterial characteristics.The aim of this study is to make an ideal cement material with adding clinoptilolite to glass ionomer cement. By this aim, control groups and test groups were formed to analyse flouride release and antibacterial effects. Test groups were formed by adding %5 percent (Group B), %10 percent (Group C) and %15 percent (Group D)of clinoptilolite to glass ionomer cement. Pure glass ionomer cement were used as control group (Group A). For each group 10 pieces of cement specimen were prepared to measure fluoride release. Fluoride release of specimens were measured on the 1st, 2nd, 3rd, 7th, 14th, 21st, 28th, 35th and 42nd days using ion selective electrode device Orion 720A+ and Orion Fluoride electrode. The analysis of antibacterial properties was made by direct contact test method with using Streptococcus mutans and Lactobacillus casei strains of bacterium. The bacterial density in the cement specimens which were solidified on the floor of 96-well microtiter plates, were analysed with microplate spectrophotometer on the h-hour, 1st, 2nd, 3rd, 17th, 18th and 24th hours.Statistical analysis were made with NCSS-PASS 2008 programme. Data were analysed by Kruskal Wallis, Mann Whitney U, Friedman and Wilcoxon tests.In the limits of this study, test groups showed no significant advantage to the control group in terms of fluoride release and antibacterial properties. In conclusion, clinoptilolitine stayed passive in the chemical structure of glass ionomer cement. The effectiveness of clinoptilolitine has need to be analysed in the studies of restructuring glass ionomer cement formulation.
Benzer Tezler
- Zeolite filled polmeric gas separation membranes
Zeolit katkılı polimerik gaz ayırma membranları
ÇİĞDEM ATALAY
Yüksek Lisans
İngilizce
1994
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiDOÇ.DR. BİLGÜL TANTEKİN ERSOLMAZ
- Kuzeybatı Trakya'da (Lalapaşa-Pınarhisar) İslambeyli formasyonu'nun ve bentonit oluşumlarının jeolojisi, mineralojisi, jeokimyası ve teknolojik özellikleri
The geology, mineralogy, geochemistry and technological properties of İslambeyli formation and bentonite occurences in Northwest Thrace basin (Lalapaşa-Pınarhisar)
BALA EKİNCİ ŞANS
Doktora
Türkçe
2018
Jeoloji Mühendisliğiİstanbul Teknik ÜniversitesiJeoloji Mühendisliği Ana Bilim Dalı
PROF. DR. RECEP FAHRİ ESENLİ
- Çoklu metal ile kirlenmiş toprakların immobilizasyonunda nanozeolit kullanımının araştırılması
Study of using nanozeolite in immobilization of soil contaminated with multimetals
HASAN CANKUT ERGÜN
Yüksek Lisans
Türkçe
2019
Çevre MühendisliğiMersin ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. NURCAN KÖLELİ
- Kimyasal veya ısıl işlem görmüş klinoptilolit zeolitinin puzolanik aktivesinin ve katkılı çimentolardaki performansının incelenmesi
Investigation on pozzolanic activity of chemically or thermally treated clinoptilolite zeolite and its performance in blended cements
ENVER KÜÇÜKYILDIRIM
Yüksek Lisans
Türkçe
2013
İnşaat MühendisliğiNiğde Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. BURAK UZAL
- Zeolit katkılı kitosan esaslı yara örtücü membran karakterizasyonu
Characterization of zeolite enriched chitosan based wound dressing membrane
ARZU AKTEKİN
Yüksek Lisans
Türkçe
2012
Tekstil ve Tekstil MühendisliğiMarmara ÜniversitesiTekstil Eğitimi Ana Bilim Dalı
PROF. DR. ERHAN ÖNER
DOÇ. DR. FAİK NÜZHET OKTAR