Yüzey çatlaklı cam takviyeli plastiklerde gerilmeli korozyon
Stress corrosion of glass reinforced plastic with surface crack
- Tez No: 24874
- Danışmanlar: PROF.DR. TEVFİK AKSOY
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Cam elyaf kompozitler, Gerilme korozyonu, Plastikler, Yüzey çatlağı, Çatlak büyüme, Composite Materials, Glass Fibre Polyester Composites, S tress Corrosion, Environmental Stress Carcking, Surface Crack, Glass fiber composites, Stress corrosion, Plastics, Crack growth
- Yıl: 1992
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Doktora Tezi YÜZEY ÇATLAKLI CAM TAKVİYELİ PLASTİKLERDE GERÎLMELÎ KOROZYON Ahmet AKDEMİR Selçuk Üniversitesi Fen Bilimleri Enstitüsü Makina Mühendisliği Anabilim Dalı Danışman: Prof.Dr. Tevfık AKSOY 1992, Sayfa: 113 Jüri : Filaman sarma metoduyla üretilmiş cam elyaf takviyeli plastikler (CTP) sürekli elyaf ve yüksek elyaf hacımsal oranlarından dolayı gerilmeli korozyona karşı birçok kompozit malzemelere göre daha duyarlıdır. Bu tezde, 0.6 N seyreltilmiş HC1 asite maruz eş yönlü cam/polyester kompozitlerde yüzey çatlağının gerilmeli korozyon ve çatlak büyüme hızı davranışları kırılma mekaniği deneyleriyle incelendi. Cam/polyester kompozitler filaman sarma metoduyla sürekli elyaftan elde edildi. Test numuneleri üzerine değişik a/c ve a/t oranlarında sığ yüzey çatlakları açılarak eksenel çekme altında tek taraflı gerilmeli korozyona tabii tutuldu. Yüzey çatlaklı CTP için gerilme şiddet faktörleri Newman-Raju, Nishioka ve SEN denklemlerinden elde edildi. Çatlak büyüme hızı ve gerilme şiddet faktörleri ile alakalı A ve n malzeme sabitleri test şartlarında tesbit edildi. Test sonuçlan literatürde verilen sonuçlarla karşılaştırıldığında, yüzey çatlaklı CTP'lerde kullanılan gerilme şiddet faktörü denklemleri ile çatlak büyüme hızı davranışlarının uygun olduğu görülmüştür.
Özet (Çeviri)
ABSTRACT Doctora Thesis STRESS CORROSION OF GLASS REINFORCED PLASTIC WITH SURFACE CRACK Ahmet AKDEMİR Selçuk University Graduate School of Natural and Applied Sciences Department of Mechanical Engineering Supervisor : Prof.Dr. Tevfik AKSOY 1992, Page: 113 Jury : Because of continuous fibers and high fiber volume fraction, filament winding glass fiber reinforced plastics (GRP) are more sensitive to stress corrosion than other composite materials. In this thesis the propagation behaviour of stress corrosion surface cracks and crack growth rates in a range of unidirectional glass fiber/polyester composites exposed to 0,6 N dilute HC1 acid has been examined using a fracture mechanics tests. Glass/polyester composites were produced from continuous rowings by filament winding. Tha shallow surface crack with various a/c and a/t ratios were machined on the specimen and under uniaxial tension were exposed to one side stress corrosion. The stress intensity factors for GRP with surface cracks are obtained from Newman-Raju, Nishioka and SEN expressions. The material constants such as A and n which related crack growth rate and stress intensity factors were obtained for the test conditions. The test results were compared with the literature. It was shown that stress intensity factor expressions and crack growth rate behaviour are suitable for GRP with surface cracks.
Benzer Tezler
- Yüzey çatlaklı kompozit malzemelerde yorulma çatlak büyümesi ve tabaka ayrılması
Surface crack propagation of composite plates with axial fatique
İBRAHİM ALDENİZ
Yüksek Lisans
Türkçe
1992
Makine MühendisliğiSelçuk ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. AHMET AVCI
- Computer aided fatique crack growth and analysis
Başlık çevirisi yok
MUSTAFA İLHAN ÖZDENER
Yüksek Lisans
İngilizce
1991
Makine MühendisliğiOrta Doğu Teknik ÜniversitesiPROF.DR. ÖMER GÜNDÜZ BİLİR
- Infinite cylinder with a transuerse crack and teo rigid inclusions under axial tension
Çekmeye maruz çatlaklı ve rijit enklozyonlar içeren sonsuz silindir problemi
MELTEM EVREM TOYGAR
Doktora
İngilizce
1998
Mühendislik BilimleriOrta Doğu Teknik ÜniversitesiMühendislik Bilimleri Ana Bilim Dalı
PROF. DR. M. RUŞEN GEÇİT
- Kılcal emme mekanizmasının statik ve dinamik koşullarda deneysel incelenmesi
Experimental study of capillary imbibition under static and dynamic conditions
AYŞE DÖNMEZ
Yüksek Lisans
Türkçe
1995
Petrol ve Doğal Gaz Mühendisliğiİstanbul Teknik ÜniversitesiY.DOÇ.DR. TAYFUN BABADAĞLI
- Batı Raman petrol sahasına CO2-köpük yönteminin uygulanabilirliği üzerine deneysel araştırmalar
Laboratory investigations on the applicability of CO2-foam method to Batı Raman oil field
K.HAKAN ALKAN
Doktora
Türkçe
1990
Petrol ve Doğal Gaz Mühendisliğiİstanbul Teknik ÜniversitesiPROF.DR. AYTİN GÖKTEKİN