Hücresel-ötektik katılaşma
Cellular-eutectic solidification
- Tez No: 23193
- Danışmanlar: Belirtilmemiş.
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Alüminyum, Bakır, Hücresel katılaştırma, Katılaştırma, Metal alaşımlar, Organik maddeler, Ötektik katılaştırma, Aluminum, Copper, Cellular solidification, Solidification, Metal alloys, Organic matters, Eutectic solidification
- Yıl: 1992
- Dil: Türkçe
- Üniversite: Erciyes Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET HÜCRESEL - ÖTEKTÎK KATILAŞTIRMA Emin ÇADIRLI E.Ü. Fen Bilimleri Enstitüsü Fizik Anabilim Dalı KAYSERİ Bu çalışmanın amacı saydam organik maddeler ve metal alaşımları ile yapılan kontrollü katılaştırmada, katılaştırma parametreleri (G, V ) ile yapısal parametrelerinin ( X, Xp R ) ilişkilerini incelemektir. İlk olarak Succinonitrilenin yönlendirilmiş olarak karşılaştırılması ve G, V ' yü kontrol etme ye yarayan yatay bir sıcaklık gradyenti sistemi yapıldı. Sabit bir sıcaklık gradyentinde katı-sıvı denge durumu elde edildikten sonra sabit V ile yönlendirilmiş katılaştırma başlatıldı ve deneyler farklı G ve V değerleri için tekrarlandı. Katılaştırma esnasında hücre ve dentritlerin fotoğrafları çekildi ve çekilen fotoğraflardan X, Xp R ölçümleri yapıldı. İkinci olarak yönlendirilmiş katılaştırma fırını yapıldı ve Al-Cu ötektik alaşımı için hücresel ötektik katılaştırma deneyleri yapıldı. Farklı G ve V değerlerinde Al-Cu ötektik numuneleri kontrollü olarak katılaştırıldı. Katılaşan Al-Cu numuneleri kesilip taşlanıp, parlatıldıktan sonra Keller dağlama sıvısı ile dağlandı ve sonra fotoğrafları çekildi. Fotoğraf negatiflerinden hücreler arası mesafeler ölçüldü ve X run G ve V 'ye karşılık değişimi incelendi. Deneysel sonuçlar Succinonitrile ve ötektik Al-Cu alaşımının her ikisinin de büyüme parametrelerini (G, V ) azalmasına karşılık yapı parametrelerinin (X, X^ R) arttığını göstermektedir.
Özet (Çeviri)
ABSTRACT CELLULAR - EUTECTIC SOLIDIFICATION Emin ÇADIRLI E.Ü. Fen Bilimleri Ensütüsü Fizik Anabilim Dalı KAYSERİ The goal of this work is to investigate the relationship between growth parameters, (G,V) and structure parameters (A, Ay R) for directionally solidified transparent organic meteri- als and metal alloys. Firstly, a horizontal temperature gradient system was constructed to directionally solidify succinonitrile and controll G and V values. After the stady-state solid-liquid interface observed in a stable temperature gradient, directional solidification has been started with constant V value and experments were repeated for different G and V values. During the solidification, photog- raphes of the cells and dentrits were taken and A, Ay R, values were measured from the pho- tographes. Secondly, a directional solidification apparatus was constructed and cellular-eutectic soli dification experiments were carried out for Al-Cu eutectic alloys. Al-Cu eutectic samples were di rectionally solidified for different G and V values. The solidified Al-Cu samples were cut, grin ded, polished and etched with keller's regent then photographes of the photographes and variati on of A aganist to G and V was investigated. The experimental results are showed that, when the growth parameters (G, V ) decrease, structure parameters (A, Ay R) increase for both succinonitrile and eutectic Al-Cu alloys. VI
Benzer Tezler
- Kararlı şartlarda kontrollu katılaştırılmış Zn+%4A1 ve Zn+%4A1 (Cu, Fe ve Mg ilaveli) alaşımlarında mikroyapı ve bileşen dağılımı
Başlık çevirisi yok
AHMET ALTMIŞOĞLU
- Hücresel ve dendiritk katılaşma
Başlık çevirisi yok
BENGÜ KAPLAN(ÜN)
Yüksek Lisans
Türkçe
1987
Fizik ve Fizik MühendisliğiErciyes ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. MEHMET GÜNDÜZ
- Analog CMOS implementation of cellular neural networks
Başlık çevirisi yok
İZZET ADİL BAKTIR
Yüksek Lisans
İngilizce
1991
Elektrik ve Elektronik Mühendisliğiİhsan Doğramacı Bilkent ÜniversitesiDOÇ.DR. MEHMET ALİ TAN
- Hücresel nöral ağlar ve uygulamaları
Cellular neural networks and applications
SEVİLAY ÖZDEMİR
Yüksek Lisans
Türkçe
1991
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik ÜniversitesiPROF.DR. I. CEM GÖKNAR
- Hücresel imalat sistemlerinin tasarımı ve kontrolü için benzetim amaçlı bir üreteç
A Simulation generator for cellular manufacturing systems design and control
MUSTAFA AKHUN
Yüksek Lisans
Türkçe
1992
Endüstri ve Endüstri Mühendisliğiİstanbul Teknik ÜniversitesiEndüstri Mühendisliği Ana Bilim Dalı
DOÇ. DR. M. BÜLENT DURMUŞOĞLU