Tek katlı poli (etilen teraftalat) liflere vinil monomerlerinin aşılanması
The Grafting of vinil monomers to monofilament poli (etilen terephthalate) (pet) fibers
- Tez No: 23002
- Danışmanlar: PROF. DR. EMSAL PULAT
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Aşılama-bitki, Etil akrilat, Etilen teraftalat, Stiren, Vinil monomerler, Grafting, Ethyl acrylate, Ethylene terephthalate, Styrene, Vinyl monomers
- Yıl: 1992
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
IV ABSTRACT Masters Thesis THE GRAFTING OF VINYL MONOMERS TO MONOFILAMENT POLIC ETİLEN TEREPHTHALATED CPETD FIBERS Meral KARAKIŞLA Ankara University Graduate School of Natural and Applied Sciences Department of Chemistry Supervisor : Prof. Dr. Emsal PULAT 1992, Page : 65 Jury : Prof. Dr. Emsal PULAT Prof. Dr. Celal TÜZÜN Prof. Dr. Nermin UYSAL In this study, the grafting of ethyl acrylate CEAD, styrene CStD, ethyl -acrylate CEA-StD mixture on pol yC ethyl ene terephthalateD CPETD fibers, using benzoyl peroxide as initiator, was investigated. The monof i lament CPETD fibers used in this study were O. 40 mm and O. 35 mm in diameter. Furthermore, the mechanical properties C tensile strength, elongation percentage!) and adhesion of grafted fibers to styrene butadiene rubber was investigated. In the grafting of EA, St and EA-St mixture, the increase in temperature caused the increase in graft yield. The maximum grafting yield was obtained at 70 C. The effect of, the swelling agents, the swelling time, monomer concentration and relaxation time in monomer, upon the graft yield was also investigated. When styrene was added to EA media the graft yield was found to increase. The densities of the fibers, grafted with EA and EA-St mixtures, were seen to decrease with the graft yield while their tensile strength and elongation percentage increased. The adhesion test of PET fibers grafted by EA-St mixture on SBR at 150 °C and under a pressure of lOO bar was investigated using styrene monomer but the development of the adhesion property was not observed KEY WORDS î Graft, graft copolymerization reaction, pol i C ethyl ene terephthalateD, ethyl acrylate, styrene, styrene butadiene rubber CSBRD.
Özet (Çeviri)
IV ABSTRACT Masters Thesis THE GRAFTING OF VINYL MONOMERS TO MONOFILAMENT POLIC ETİLEN TEREPHTHALATED CPETD FIBERS Meral KARAKIŞLA Ankara University Graduate School of Natural and Applied Sciences Department of Chemistry Supervisor : Prof. Dr. Emsal PULAT 1992, Page : 65 Jury : Prof. Dr. Emsal PULAT Prof. Dr. Celal TÜZÜN Prof. Dr. Nermin UYSAL In this study, the grafting of ethyl acrylate CEAD, styrene CStD, ethyl -acrylate CEA-StD mixture on pol yC ethyl ene terephthalateD CPETD fibers, using benzoyl peroxide as initiator, was investigated. The monof i lament CPETD fibers used in this study were O. 40 mm and O. 35 mm in diameter. Furthermore, the mechanical properties C tensile strength, elongation percentage!) and adhesion of grafted fibers to styrene butadiene rubber was investigated. In the grafting of EA, St and EA-St mixture, the increase in temperature caused the increase in graft yield. The maximum grafting yield was obtained at 70 C. The effect of, the swelling agents, the swelling time, monomer concentration and relaxation time in monomer, upon the graft yield was also investigated. When styrene was added to EA media the graft yield was found to increase. The densities of the fibers, grafted with EA and EA-St mixtures, were seen to decrease with the graft yield while their tensile strength and elongation percentage increased. The adhesion test of PET fibers grafted by EA-St mixture on SBR at 150 °C and under a pressure of lOO bar was investigated using styrene monomer but the development of the adhesion property was not observed KEY WORDS î Graft, graft copolymerization reaction, pol i C ethyl ene terephthalateD, ethyl acrylate, styrene, styrene butadiene rubber CSBRD.
Benzer Tezler
- Scanning tunneling microscope ; design, construction and applications
Taramalı tünelleme mikroskobu ; tasarımı, imalatı ve uygulamaları
M.HADI ZAREIE
- EGF'nin dental implant materyali üzerindeki kesi yarası iyileşmesine etkisi
Effect of EGF on the healing of incision wound on the dental implant material
FEHMİ KARATAŞ
- Preparation of pol (vinly chloride) blends: spect ruscopic, thermal, viscosimetric, mechanical and surface characterizations
Poli (Vinil klorür) karışımlarının hazırlanması: Spektroskopik, ısıl, viskonimetrik, mekanik ve yüzey karakterizasyonları
OKŞAN KARAL
Doktora
İngilizce
1998
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. BAHATTİN M. BAYSAL
- Fairing of two dimensional ship lines
İki boyutlu tekne form eğrilerinin düzgünleştirilmesi
EBRU NARLI