Hidroksiapatit ve gümüş kaplanmış protez implantların in vivo antimikrobiyal etkinliğinin değerlendirilmesi, hayvanlarda deneysel çalışma
Evaluation of in vivo antimicrobial efficiency of hidroxyapatite- and silver-coated prothesis implants, an experimental animal study
- Tez No: 225870
- Danışmanlar: PROF. DR. NUSRET KÖSE
- Tez Türü: Tıpta Uzmanlık
- Konular: Ortopedi ve Travmatoloji, Orthopedics and Traumatology
- Anahtar Kelimeler: Antienfektif ajanlar, Dental implantasyon, Dental implantlar, Gümüş, Hidroksiapatitler, Metal iyonları, İn vivo, Anti infective agents, Dental implantation, Dental implants, Silver, Hydroxyapatites, Metal ions, In vivo
- Yıl: 2009
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Tıp Fakültesi
- Ana Bilim Dalı: Ortopedi ve Travmatoloji Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada amacımız gümüşlü hidroksiapatit kaplanmış basit bir protez şekli verilen titanyum implantların antimikrobiyal etkinliğini göstermek idi. Bu nedenle hayvanlarda deneysel bir çalışma planlandı. Ağırlıkları 3000-3500 gr arasında olan 27 adet tavşan çalışmaya alındı, dokuzarlı üç gruba ayrıldı. 1. gruba kaplamasız titanyum, 2. gruba hidroksiapatit kaplı titanyum, 3. gruba ise gümüş iyon katkılı antibakteriyel toz (ABT) ve biyocam kaplı titanyum implant, tavşanların dizinden femurun intramedüller kanalına yerleştirildi. Öncesinde femoral kanala 5x 10² CFU S. aureus inoküle edildi. Haftalık rektal ateş ölçümü yapıldı. Altı hafta sonra tavşanlar öldürüldü, diz yan grafileri çekildi, medüller kanal, implant sürüntü, kemik ve implantın mikrobiyolojik incelemesi yapıldı ayrıca implant çıkarıldıktan sonra implant çevresi kemiğin histopatolojik değerlendirilmesi de yapıldı. Yapılan mikrobiyolojik incelemede tüm kültürlerde gümüşlü hidroksiapatit kaplı grupta enfeksiyon diğer iki gruba oranla anlamlı derecede düşüktü.(p=0,005) 1. grupta 9 tavşanın 8'inde, 2. grupta 9 tavşanın 5'inde üreme olurken, 3. grupta 9 tavşanın sadece 1'inde üreme oldu. Histopatolojik incelemede 1. ve 2. grupta implant çevresi ve trabeküller arasında yoğun inflamatuar hücreler görülürken, 3. grupta inflamatuar hücreler izlenmedi, ayrıca bu grupta implant çevresi kemikte aşınma ve gümüş partikülleri izlenmedi. Gümüşün osteoblastlar üzerine toksik etkisi, yabancı cisme bağlı granülasyon dokusu da izlenmedi. Normal kemik hücreleri ve trabeküller izlendi. Çekilen düz grafilerde, üç grupta da implant çevresindeki kemikte enfeksiyonu düşündürecek bulgular (osteoliz) görülmedi.
Özet (Çeviri)
The aim of this study was showing the antimicrobial efficiency of silver dopped hydroxyapatite-coated titanium implant that formed as a simple prothesis. An experimental animal study was planned. 3 equal groups formed from 27 rabbits that weighted between 3000-3500 gr each. In the first group uncoated titanium, in the second group hidroxyapatite-coated titanium and in the last group silver ion dopped antibacteriel powder (ABT) (hydroxyapatite) coated titanium implants were inserted from the rabbits? knees to femoral intramedullary canal. Prior to this application, 5 x 102 CFU S. aureus was inoculated to femoral canal. Rectal temperature was measured weekly. After 6 weeks rabbits are killed, knee lateral radiographs are obtained, microbiological analysis of meduller canal, implant smear, bone and implant are done. also After removal of implant, histopathologic evaluation of bone around implant was done. The statistical analysis of microbiological results showed that infection rate in silver dopped hidroxyapatite-coated group is significantly lower compared to other two groups (p=0,005). 8 rabbits in the first group, 5 rabbits in the second group and only one rabbit in the third group had positive culture results. While there were intensive inflammatory cells in the histopatologic examination of the bone around implant and between trabecules in the first and second groups, no inflammatory cells in the third group were seen. Also in this group there were no erosion in the bone around implant and any silver particules were seen. Toxic effects of silver to osteoblasts and granulation tissue related to foreign body was not seen. Bone cells and trabecules were normal. In plain radiographs, there were no signs of bone infection around implant (osteolisis) in all groups.
Benzer Tezler
- Hafif antibakteriyel seramik ve antibakteriyel seramik filtre üretimi
Light weight antibacterial ceramic and antibacterial ceramic filter production
SÜMERAY KOYAŞ
Yüksek Lisans
Türkçe
2006
Seramik MühendisliğiAfyon Kocatepe ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ATİLLA EVCİN
- Synthesis and characterization of hydroxyapatite-alumina-zirconia biocomposites
Hidroksiapatit-alumina-zirkonya biokompozitlerinin sentezi ve karakterizasyonu
ERDEM ŞAHİN
Yüksek Lisans
İngilizce
2006
Biyomühendislikİzmir Yüksek Teknoloji EnstitüsüMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ.DR. SEDAT AKKURT
PROF.DR. MUHSİN ÇİFTÇİOĞLU
- Manifacture of macroporous calcium hydroxyapatite (HA) and tri calcium phosphate (TCP) bioceramics
Makro gözenekli kalsiyum hidroksiapatit (HA) ve TRİ-kalcium fosfat (TCP) biyoseramiklerinin üretimi
NEDİM ÖZGÜR ENGİN
Yüksek Lisans
İngilizce
1999
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. A. CÜNEYT TAŞ
- Hidroksiapatit denetimli fluorid salımının tükürük-üre fluorid konsantrasyonu ve demineralize mineye etkisinin değerlendirilmesi
Evaluation of the effect of hydroxyapatite controlled release fluoride on the saliva-ürine fluoride concentration and demineralized enamel
BANU YEL ALTINOVA
- Preparation and characterization of chitosan/calcium phosphate based composite biomaterials
Kitosan/kalsiyum fosfat bazlı kompozit biyomalzemelerin hazırlanması ve karakterizasyonu
OKTAY YILDIRIM
Yüksek Lisans
İngilizce
2004
Metalurji Mühendisliğiİzmir Yüksek Teknoloji EnstitüsüMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. MUHSİN ÇİFTÇİOĞLU