Alümina-spinel-zirkonya ile çimentosuz kendi kendine akabilen dökülebilir refrakter geliştirilmesi
Development of the zero-cement self-flow castable refractory based on alumina-spinel-zirconia
- Tez No: 223165
- Danışmanlar: PROF.DR. M. LÜTFİ ÖVEÇOĞLU, Y.DOÇ.DR. YASEMEN K. KALPAKLI
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Seramik Mühendisliği, Mühendislik Bilimleri, Metallurgical Engineering, Ceramic Engineering, Engineering Sciences
- Anahtar Kelimeler: Dökülebilir refrakter, çimentosuz, kendi kendine yayılabilen, alümina, spinel, zirkonya, Zirkonyum oksit, Castable refractories, self-flow, zero-cement, alumina, zirconia, spinel, Zirconium oxide
- Yıl: 2007
- Dil: Türkçe
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Çimentosuz dökülebilir refrakter, kalsiyum oksitin yüksek sıcaklıklarda yarattığı olumsuz etkilerinden kaçınmak için son dönemlerde üzerine araştırmalar yapılan önemli bir refrakter çeşididir. Bu tez çalışmasında, son yıllarda refrakter sanayinde trend olan çimento içermeme ile kendi kendine yayılabilme özellikleri birleştirilmiştir. Bu çalışmanın ilk bölümünde alfabond 300 hidratlanabilir alümina bağlayıcının kullanıldığı tabular alümina esaslı kendi kendine akabilen dökülebilir refrakterde partikül boyut dağılmının ürün özellikleri üzerindeki etkisi incelenmiştir. Kendi kendine akabilen dökülebilir refrakterlerin hazırlanması Andreassen Denklemi'e göre olmuştur. İkinci aşamada ise, birinci bölümde optimum olarak bulunan partikül boyut dağılım parametresine göre hazırlanan tabular alumina esaslı komposizyona çeşitli oranlarda MgO ilavesi yapılarak yerinde spinel oluşturulmuş, bunun özellikler üzerindeki etkileri bulunmuştur. Bundan sonraki aşamada, optimum partikül boyut dağılım parametresine göre hazırlanan komposizyona çeşitli oranlarda sentetik spinel ilavesi yapılarak bunun özellikler üzerindeki değişimi izlenmiştir. Son aşamada ise, ikinci kısımda bulunan optimum MgO miktarı katkısı ile hazırlanan sisteme belli oranlarda zirkonya ilavesi yapılarak bunun refrakter özellikler üzerindeki etkileri incelenmiştir. Daha sonra her aşamada elde edilen en iyi özelliklere sahip refrakter malzemenin bulunup bu refrakterlerin birbiri ile kıyaslamaları, özelliklerine göre yapılmıştır.
Özet (Çeviri)
Zero-cement castable refractory is one of the most important refractory type which is under investigation in recent years for preventing negative effects of calcium oxide In this study, the cement free and self-flow properties which are currently popular in refractory industry were combined together. In the first stage of this study, the effect of the particle size distribution on the refractory properties of cement free self-flow castables based on tabular alumina and consisting of alphabond 300 hydratable alumina binder, was investigated. The preperations of the self-flow castables were done according to Andreassen Equation. In the second stage, the addition of magnesia with different proportions was done to the compositions including tabular alumina which prepared with optimum q value determined in the first stage. Spinel particles formed in the refractories during sintering and the effects of the spinel particles on the refractory properties was investigated. In the third stage, the addition of synthetic spinel with different proportions was done into the compositions prepared via optimum q value and then the effects of spinel particles on the refractory properties was investigated. In the final stage, the additions of zirconia with different proportions was done into the compositions prepared with optimum q value and optimum MgO content. Namely zirconia powders were added to the best composition in the second stage. Then the effects of zirconia particles on the refractory properties were investigated. Finally the best refractory material was determined in each stage and they were compared with each other.
Benzer Tezler
- Farklı kor seramiklerin ışık geçirgenliğinin incelenmesi
Examination of the light transmission of different ceramic cores
ÖZLEM CEYLAN
Doktora
Türkçe
2007
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. FİLİZ AYKENT
- Çeşitli yüzey şartlandırma işlemlerinin üç farklı in-ceram kor yapısı ile bir dual-cure rezin siman arasındaki bağlanmaya etkisinin incelenmesi
The effect of different surface treatments on the bond strength of a dual cure resin cement to three various in-ceram ceramic
SEMİH TAŞVEREN
Doktora
Türkçe
2004
Diş HekimliğiCumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ.DR. ALİ KEMAL ÖZDEMİR
- 1960'dan günümüze çağdaş sanatta heykelin konumu
The prospective of contemporary sculpture from 1960 to our day
YASEMİN ÖZKAYA
Yüksek Lisans
Türkçe
2007
Güzel SanatlarMarmara ÜniversitesiHeykel Ana Sanat Dalı
YRD. DOÇ. DR. NURETTİN BEKTAŞ
- Magnezya-Alumina spinel dökülebilir refrakterlerin sentezlenmesi
Magnesia-Alumina spinel castable refractories
ÖZGÜR ERYILMAZ
- Spinel refrakterlerde proses parametrelerinin özellikler üzerindeki etkileri
The Effects of process parameters on the properties of spinel refractories
CENGİZ HAMZAÇEBİ