Fracture toughness properties of welded low alloy and austenitic stainless steel plates with austenitic comsumable
Ostenitik elektrotla kaynaklanmış düşük alaşımlı ve paslanmaz çelik plakaların kırılma tokluğu özellikleri
- Tez No: 213192
- Danışmanlar: PROF. DR. TEVFİK AKSOY
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Kaynak bağlantısı, Kırılma tokluğu, Plastik deformasyon, Uyumsuzluk, Weld joint, Fracture toughness, Plastic deformation, Mismatch
- Yıl: 2007
- Dil: İngilizce
- Üniversite: Dokuz Eylül Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Bölümü
- Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada; 17Mn4 (P295GH) kazan çeliği ve AISI304 paslanmaz çelik, ER309L östenitik kaynak dolgu malzemesi kullanılarak kaynaklanmıştır. Kaynak yöntemi olarak gaz tungsten ark kaynağı seçilmiştir (TIG (GTAW)). Kaynaklı levhalardan çıkarılan numuneler üzerinde sertlik taraması ve çekme deneyi yapılmıştır. Kaynak bölgesinde kırılma tokluğu davranışını incelemek için tek taraftan çentikli eğme deney numuneleri ile J-integrali değerleri ASTM E 1737-96 ya göre hesaplanmıştır. Kaynaklı numune üzerinde değişik bölgelere strain-gage yapıştırılarak tek eksenli çekme yapılmış ve plastik deformasyonun başlamasının engellendiği bölgeler tespit edilmiştir.Çalışmanın sayısal kısmında, sonlu elemanlar analizleri farklı bölgelerin ön çatlaklar içeren 2 boyutlu modeller oluşturularak gerçekleşmiştir. Bu modellerde, gerilme şekil değiştirme analizlerinden sonra çatlak civarındaki üç eksenli gerilme ve plastik deformasyon karakteristikleri her bir çatlak bölgesi için belirlenmiştir. J ? integrali değerleri bütün çatlak bölgeleri için sonlu elemanlar metodu ile hesaplanmıştır. Plastik deformasyon ilerlemesinin ısı tesiri altında kalmış bölgede ve difüzyon çizgisinde engellenmesi çatlak ucunda fazladan bir üç eksenli gerime artışına neden olmaktadır.
Özet (Çeviri)
In this study, 17Mn4 (P295GH) pressure vessels steel and AISI304 stainless steel are welded with ER309L austenitic consumable. GTAW, Gas Tungsten Ark Welding was selected as a method of welding. Hardness and tensile tests were done on welded plates. J - Integral fracture toughness values are calculated according to the ASTM E1737-96 with Single-Edge bend specimen, to investigate fracture toughness characteristics on weld region. In order to detect the regions where plastic deformation did not take place, uni-axial tensile test was performed on welded tensile specimen after attaching strain gages.In numerical part of the study, finite element (FE) analyses were conducted by fixing 2-D models precracked on different locations. In these models, stress triaxiality and plastic deformation characteristics around crack tip were determined for each crack locations after stress ? strain analyses. J ? Integral values were calculated for all crack locations with finite element method. The limitation on the extension of plastic deformation at HAZ and diffusion line causes extra increase in stress triaxiality at crack tip.
Benzer Tezler
- Kaynak kabiliyeti ve bilgisayar yardımı ile karbon eşdeğeri hesapları
Weldability and computerizing of carbon equivalents
ALİ ZİYA
- Dar aralık kaynağında dikiş formuna kaynak parametrelerinin etkisi ve bilgisayar yardımı ile tayini
Computer aided determination of the welding parameters in narrow GAP welding and their effects on the weld
CEM AKBAŞ
- Strength mis-match effects on fracture behavior of structural steel welds
Yapısal çeliklerin kaynağında mukavemet uyuşmazlığının kırılma davranışı üzerindeki etkisi
ÇINAR EMİNE YENİ
Doktora
İngilizce
1998
Makine MühendisliğiDokuz Eylül ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ.DR. SEÇİL ERİM
- Eğme gerilmesi altındaki muhtelif tip kaynaklı bölgelerde uyumsuzluk (MIS-MATCH) araştırması
Başlık çevirisi yok
AHMET OKUR
Doktora
Türkçe
1999
Makine MühendisliğiCelal Bayar ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. CEVDET MERİÇ
- Kaynak ısı girdisinin soğuk şekillendirilmiş S700 MC çeliğinin mekanik özelliklerine etkisi
Effect of weld heat input on mechanical properties of cold formed S700MC steel
ÖZKAN ESKİ