Bor fosfat katkılı termal şoka dayanıklı seramikler
Thermal shock resistant ceramic with borane phosphote addetive
- Tez No: 212770
- Danışmanlar: PROF. DR. METİN GÜRÜ, YRD. DOÇ. DR. BÜLENT BARAN
- Tez Türü: Yüksek Lisans
- Konular: Seramik Mühendisliği, Kimya Mühendisliği, Ceramic Engineering, Chemical Engineering
- Anahtar Kelimeler: Kordierit, Anorthite, BPO4, Termal şok, Genleşme katsayısı, Hızlı pişirim, Sıvı faz sinterleşmesi, Ötektik, Anortit, Cordierite, Anorthite, BPO4, Thermal shock, Expansion Coefficient, Fast Firing, Liquid Phase Sintering, Eutectic
- Yıl: 2007
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İleri Teknolojiler Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışma; 2003K120470?07 kodlu, ?Termal şoka dayanıklı, bor fosfat katkılı, hızlı pişirimle elde edilen seramiklerin üretimi? adlı DPT tarafından desteklenen projeye katkı amacıyla çalışılmıştır. Bu çalışmada termal şoka dayanabilen seramik türü olarak kordierit ve anorthit fazları seçilmiştir. İlk olarak daha sonra hazırlanacak karışımlarda kullanılmak üzere borofosfat sentezi gerçekleştirilmiştir. Elde edilen bor fosfat 1000oC `da kalsine edilmiş ve XRD, Kimyasal Analizleri ile karekterize edilmiştir. Diğer yandan (MgO, Al2O3, SiO2) faz diyagramında kordierit fazını en çok kapsayan ve kordieritin oluşabildiği en düşük sıcaklıktaki uygun ötektik noktalar seçilmiştir. Seçilen bu noktaların bileşimleri kaolin, talk, alumina hammaddelerine göre hesaplanmış ve karışımlar hazırlanmıştır. Kordierit için hazırlanan 7 adet karışım iki eşit kısma ayrılmış ikinci kısımlarına %10 BPO4 ilavesi yapılmıştır. Benzer çalışma (CaO, Al2O3,SiO2) faz diyagramında anorthit fazı için de yapılmış ve wollastonit, kaolinit, kalsit kullanılarak 6 adet karışım hazırlanmıştır. Elde edilen 6 adet karışım iki kısma ayrılmış ve yine ikinci kısımlara % 10 BPO4 ilavesi yapılmıştır. Karışımlar presle aynı basınçta şekillendirilmiş ve aynı koşullarda ve aynı ısıtma hızıyla v elektrikli fırında kordierit için 1100, 1150, 1200, 1250, 1300, 1350 anorthit için 1000, 1050, 1100, 1150, 1200,1250 oC'a pişirmiştir. Örneklere pişmeden önce DTA ve TG analizleri pişen örneklere ise X ışını kırınımı analizleri uygulanmıştır.
Özet (Çeviri)
This study was performed for 203K120470-07 coded, ?Manufacture of ceramic that has thermal shocked strength, boron fosfat additive, formed according to fast firing? named DTP supported Project. Kordierite and anorthite phases was choosen as thermal shocked strength ceramic types. First of all, boronfosfat was synthesised to use following step. Synthesised boronfosfat was calcined at 1000 OC and its charactarization analysis were performed using XRD and Chemical Analysis. On the other hand, suitable eutectic point of minimum temperature that is the most inclued the kordierte phase and forming cordierte at (MgO, Al2O3, SiO2) phase diagram was choosen. Composition of these choosen points are calculated according to kaoline, talc, alumina raw materials and mixtures are prepared. 7 mixtures that prepared for kordierte, were splited in two equal parts, for its second part %10 BPO4 was added. Likeness study was performed for anorhite phase at (CaO, Al2O3, SiO2) phase diagram and using wallostonite, kaolinit, calsite, 6 mixture was formed. Prepared 6 mixture were splited two parts and %10 BPO4 was added again in vii second part. Mixture was shaped with pressing at the same pressure and fired using electric furnace at and same condition and the same heating shedule for cordieritre 1100, 1150, 1200, 1250, 1300, 1350 and for anorthite 100, 1050, 1100, 1150, 1200, 1250 OC. Before firing DTA and TG analysis were applied for samples and X-ray diffraction analysis were applied for firing samples.
Benzer Tezler
- Burdur ili mermer sektörünün kurumsal ve ekonomik yapısı
İnstitutional and economic structure of marble sector in burdur
AHMET SARITAŞ
- Sodyum-kalsiyum borfosfat malzemelerinin sentez ve karakterizasyonu
The synthesis and the characterization of sodium calcium borophosphate materials
NURDAN YAVUZ
- Bazı bor içeren apatit malzemelerin sentezi ve karakterizasyonu
Synthesis and characterization of some types of boron containing apatites
GÜLNAZ GÜNDOĞMAZ
- Hidrotermal ve mikrodalga enerjiyle lityum içeren boratlı, fosfatlı ve borfosfatlı bileşiklerin sentezlenmesi, kristal yapı ve termokimyasal özelliklerinin incelenmesi
Synthesis of compounds which type of borate, phosphate and borophosphates including the lithium element by using hydrothermal and microwave energy methods, investigations of crystal structure and thermochemical properties
ELİF DEMİR BAYKAL
- Synthesis and characterizations of alkaline, alkaline earth and transition metal borophosphate compounds
Alkali, toprak alkali ve geçiş metalleri borfosfat bileşiklerinin sentez ve karakterizasyonları
AYŞEN YILMAZ
Doktora
İngilizce
2000
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MERAL KIZILYALLI
PROF. DR. RUDİGER KNİEP