Tekrarlanan fırınlama işlemleri uygulanan farklı yapıdaki dental seramiklerde, değişik parlatma yöntemlerinin yüzey pürüzlülüğüne etkisinin, atomik kuvvet mikroskobu ve profilometre ile değerlendirilmesi
The evaluation of the effect of different polishing techniques on the surface roughness of dental ceramics subjected to repeated firings by atomic force microscope and profilometer
- Tez No: 203128
- Danışmanlar: DOÇ.DR. PELİN ÖZKAN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Atomik Kuvvet Mikroskobu, dental seramik, glaze, tekrarlanan fırınlamalar, yüzey pürüzlülügü, Dental porselen, Yüzey pürüzlülüğü, Atomic Force Microscope, dental ceramic, glaze, repeated firings, surface roughness, Dental porcelain
- Yıl: 2007
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalısmanın amacı, degisik parlatma yöntemleri uygulanmıs, farklı yapıdaki dental seramiklerde, tekrarlanan fırınlamalar boyunca, yüzey pürüzlülügünde meydana gelen degisimin degerlendirilmesidir. Çalısmamızda; dental seramiklerde yüzey pürüzsüzlügü saglamak için en uygun yöntemin ne oldugunu ortaya çıkarmak, mekanik parlatmayı diger yöntemlerle kıyaslamak, farklı yapıdaki dental seramiklerde yüzey pürüzlülügünün ne ölçüde degistigini bulmak, tekrarlanan fırınlamaların yüzeye etkisini incelemek ve son olarak, AFM'nun dental seramiklerde yüzey pürüzlülügü degerlendirme yöntemi olarak ne ölçüde kullanılabilecegine ısık tutmak hedefleri amaçlanmıstır. Çalısmada, farklı yapıdaki üç seramikten (feldspatik, lösitle güçlendirilmis feldspatik ve lityum disilikatla güçlendirilmis feldspatik) toplam 63 örnek hazırlandı. Örnekler, 10 mm çapında ve 2 mm kalınlıgında disk seklinde yapıldı. Üç ana grup olusturuldu. Her grupta esit sayıda (21 adet) porselen örnegi mevcuttu. Birinci gruptaki porselen örneklere glaze, ikinci gruptakilere natural glaze ve üçüncü gruptakilere mekanik parlatma islemleri uygulandı. Her alt gruptaki örnek sayısı (n) 7'dir. Örneklerde kontrol amaçlı yüzey pürüzlülügü ölçümleri alındıktan sonra, tekrarlanan fırınlamalar uygulandı. 1. ve 2. grupta, 1., 3., 5. ve 7. ek fırınlama; 3. grupta ise kontrol + parlatma, 1. ek fırınlama + parlatma, 3. ek fırınlama + parlatma, 5. ek fırınlama + parlatma ve 7. ek fırınlama + parlatma asamalarında tekrar yüzey pürüzlülügü ölçümleri alındı. Bu amaçla, Perthometer M2 profilometre ve Solver Pro AFM cihazları kullanıldı. Bütün örneklerde profilometre ile ortalama yüzey pürüzlülügü degeri olan Ra saptandı. Her alt gruptan bir örnek seçildi ve her asamada aynı örnek üzerinden AFM ile 3 boyutlu topografik görüntüler kaydedildi. Profilometre incelemesinin istatistiksel analizi tekrarlanan ölçümlü varyans analizi teknigiyle gerçeklestirildi. Ortalamalar arasındaki farkların tesadüften ileri gelmedigi ise Duncan testi ile belirlendi. Profilometre testi sonucunda, yüzey pürüzlülügü bakımından, materyal, yöntem ve zaman arasındaki interaksiyonun istatistiksel olarak önemli oldugu saptanmıstır (p<0,05). En basarılı materyal feldspatik yapılı metal destekli seramik IPS Klasik, en iyi yöntem ise glaze yöntemidir. IPS Empress2 tam seramigi IPS Empress Estetik'e kıyasla daha pürüzlü bulunmustur. Yöntem olarak glaze yöntemini, materyal olarak feldspatik yapılı, metal destekli dental seramikleri öneriyoruz. Herhangi bir nedenle, glaze yapılamadıgında natural glaze yöntemini, metal destekli seramik kullanılmadıgında ya da bunun yerine tam seramik tercih edildiginde ise Empress Estetik tam seramigini öneriyoruz. Çalısmamız sonucu ortaya çıkan verilere dayanarak, mekanik parlatma isleminden kaçınmak gerektigini düsünüyoruz. Fırınlama sayısı arttıkça düzenli bir sekilde yüzey pürüzlülügü azalmıstır. Tekrarlanan fırınlamalar boyunca, yüzey pürüzlülügünün azalmasını ve parlaklıgın artmasını ek fırınlamaların porselen yüzeyini eriterek glaze ya da natural glaze tabakasını kaldırmasına baglıyoruz. Dental seramik üzerindeki glaze tabakasının bozulmasını ve yüzey seklinin degismesini önlemek için mümkün oldugunca tekrarlanan fırınlamalardan kaçınılmalıdır. AFM, profilometre ölçümlerini destekleyici ve gelistirici sonuçlar ortaya çıkarmıstır. Bu nedenle, çalısmamızın, dental restorasyonlarda yüzey pürüzlülügünü degerlendirmede, AFM cihazının kullanılmasına dair yapılacak baska yüzey pürüzlülügü çalısmalarına da, ısık tuttugu ve rehber oldugu düsüncesindeyiz.
Özet (Çeviri)
The aim of this study is to evaluate the change in surface roughness of different dental ceramics polished with different polishing techniques during repeated firings. In our study, to find the most accurate method for obtaining surface smoothness of dental ceramics, to compare the advantages of mechanical polishing rather than other methods, to evaluate the difference of surface roughness of different dental ceramics, to examine the effect of repeated firings on surface of ceramics and lastly, to determine the use of Atomic Force Microscope for evaluating the surface roughness of dental ceramics were studied. In this study 63 samples of different ceramics (feldspathic, leucite reinforced feldspathic and lithium disilicate reinforced feldspathic) were prepared. The samples were 10 mm in radius and 2 mm wide. 3 main groups were accustomed. Each group had 21 samples. First group of samples were glazed, second group of samples were natural-glazed and third group of samples were mechanically polished. Each group is then divided to 3 subgroups of 7 samples (n=7). Surface roughness was measured before the process as control. Then repeated firings were carried on. In 1st and 2nd group surface roughness was measured after 1., 3., 5. and 7. firings and in 3rd group surface roughness was measured after control + polishing, 1. firing + polishing, 3. firing + polishing, 5. firing + polishing and 7. firing + polishing. Perthometer M2 profilometer and Solver Pro Atomic Force Microscope devices were used. Average surface roughness value Ra is calculated for every sample by profilometer. Statistical analysis was done by repeated measures of variance analysis. Coinsideces between mean values are eleminated by Duncan test. As a result of profilometer test, the interaction between material, method and time was found statistically important (p<0.05). In general, the most successful material was found metal fused feldspathic ceramic IPS Classic and the best method was glazing. IPS Empress2 all ceramic was found to have more surface roughness than IPS Empress Esthetic. We recommend glaze as polishing technique and metal fused feldspathic ceramics as material. If it is not possible to glaze we recommend natural glazing as polishing technique and if it is not possible to use metal fused ceramics, we recommend Empress Esthetic all ceramic as material. According to the results of our study we believe that mechanical polishing should be the last choice for polishing. As the number of firings increased, surface roughness was decreased systematically. We believe that the surface was softened by repeated firings and glaze or natural glaze layers were removed and as a result, surface roughness was decreased. To prevent the corruption of glaze on dental ceramics and the chance of surface shape, we recommend not doing any repeated firings if possible. Atomic Force Microscope supported and improved the results of profilometer. Because of this we believe that our study will be a guide for studies for evaluating the surface roughness of dental restorations by the use of AFM.
Benzer Tezler
- Zirkonyum dioksit alt yapı üzerine uygulanan farklı yüzey işlemlerinin ve tekrarlanan fırınlamanın üst yapı porseleninin bağlanma dayanımına etkisinin in-vitro olarak incelenmesi
In-vitro evaluation of the effect of different surface treatments and repeated firing on their bond strength to two veneer ceramics to zirconia
SİNEM SAVRAN ÇAKIR
Doktora
Türkçe
2011
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. BÜLENT ŞERMET
- Çoklu fırınlama uygulamasının farklı zirkonya esaslı alt yapı sistemlerinin mekanik özelliklerine etkisi
Effect of repeated firing on mechanical properties of different zirconia based ceramic core systems
BEHİYE DABAKOĞLU
Doktora
Türkçe
2009
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU
- Farklı zirkonya sistemlerinde glazür ve termal siklus uygulamalarından sonra kırılganlık ve mikrosertlik değişimleri
A comparative study of biaxial flexural strength and vickers microhardness of different zirconia materials after glazing and thermal cycling
ESRA SALİHOĞLU
Doktora
Türkçe
2009
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU
- Tekrarlanan döküm işleminin temel metal alaşımında biyouyumluluk üzerindeki etkisinin in vitro değerlendirilmesi
In vitro evaluation of the effect of recasting on biocompatibility of base metal alloy
PINAR DURKAYA
Doktora
Türkçe
2013
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÜLAY KANSU
- Farklı prosedürlerle sinterlenen Y-TZP altyapıların fırınlama işlemleri karşısındaki boyutsal stabilitelerinin ve marjinal uyumlarının invitro olarak karşılaştırılması
Invitro comparison of dimensional stability and marginal fits of Y-TZP frameworks which are sintered with various procedures and consequently subjected to firing cycles
HASAN MURAT AYDOĞDU
Doktora
Türkçe
2015
Diş HekimliğiYüzüncü Yıl ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. MURAT ESKİTAŞCİOĞLU