Titanyum ve düşük karbonlu çelik çiftinin ara bağlayıcı kullanılarak difüzyon kaynağı ile birleştirilebilirliğinin araştırılması
Investigation of joinability of the titanium and low carbon steel using an interlayer by diffusion welding
- Tez No: 202914
- Danışmanlar: DOÇ. DR. NİZAMETTİN KAHRAMAN
- Tez Türü: Yüksek Lisans
- Konular: Teknik Eğitim, Technical Education
- Anahtar Kelimeler: Difüzyon kaynagı, titanyum, arabaglayıcı ve mikroyapı, Difüzyon kaynağı, Diffusion welding/bonding, titanium, interlayer and microstructure, Diffusion welding
- Yıl: 2007
- Dil: Türkçe
- Üniversite: Zonguldak Karaelmas Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Difüzyon kaynagı, birbirleriyle temasta olan yüzeyler arasında minimum deformasyon ile belirli bir süre ısı ve basınç uygulayarak kontrollü difüzyon ile olusturulan bir katı hal kaynak yöntemidir. Birbirinin aynı yada farklı birçok malzeme difüzyon kaynak yöntemi ile birlestirilebilmektedir. Bugün farklı metallerin birlestirilmesinde % 40 bu yöntem kullanılırken, bu yöntemle birlestirilmis malzemelerin yaklasık % 20'sini de titanyum ve alasımları olusturmaktadır. Difüzyon kaynagının uygulanmasında, özellikle farklı metal ve alasımlarının birlestirilmesinde kaynak bölgesindeki heterojenligi minimuma indirmek için genellikle bir arabaglayıcı kullanılır. Bu çalısmada, titanyum ve düsük karbonlu çelik levhalar gümüs bir arabaglayıcı kullanılarak farklı sıcaklık ve sürelerde birlestirilmislerdir. Elde edilen birlestirmelerin mukavemetini belirlemek için çekme-makaslama testi ve sertlik testi uygulanmıstır. Ayrıca baglantının arayüzey özelliklerinin belirlenmesi amacıyla optik mikroskop ve SEM çalısmaları ile SEM'e monte edilmis EDS ünitesinde element analizleri yapılmıstır. Yapılan çalısmalar sonucunda, bu çalısmada kullanılan kaynak parametreleri dahilinde, en yüksek arayüzey dayanımı 850 oC'de ve 90 dakika süre ile birlestirilen numunelerde elde edilmistir. Ayrıca artan sıcaklık ve süre ile birlikte mukavemetin bir noktaya kadar arttıgı, ancak bu noktadan sonra mukavemetin azaldıgı belirlenmistir. Yapılan sertlik ölçümleri sonucunda en yüksek sertlik degerinin arabaglayıcı malzemede oldugu ve ara baglayıcının her iki tarafındaki sertlik degerlerinin giderek azaldıgı tespit edilmistir. Makro ve mikroyapı çalısmaları sonucunda, farklı kaynak sartlarında birlestirilen numunelerin tümünde, artan sıcaklık ve süre ile birlikte birlesme bölgesinin (arabaglaycı) daraldıgı ve de tane irilesmesinin meydana geldigi gözlemlenmistir. EDS analiz çalısmalarında, sıcaklıgın artısına baglı olarak arabaglayıcıdaki gümüs miktarının % agırlık olarak belirgin sekilde azaldıgı, ancak difüzyon süre artısına baglı olarak çok az miktarda azaldıgı görülmüstür. Ayrıca, kaynak arayüzeyinden uzaklastıkça yayınım miktarının giderek azaldıgı tespit edilmistir.
Özet (Çeviri)
Diffusion welding is a solid state welding process in which heat and pressure are applied for some time to affect the bonding between the contacting surfaces through controlled diffusion with minimum deformation. Many similar or dissimilar materials can be bonded by diffusion welding process. Today, 40 % of dissimilar materials bonded to each other are joined with this method while 20 % of these joints consist of titanium and its alloys. In diffusion bonding applications, an interlayer is used in order to minimise the inconsistency in the weld zone especially when bonding different metals and their alloys. In this study, titanium and low carbon steel plates were joined using a silver interlayer at different temperatures for different durations. In order to determine the strength of joints, tensile-shear tests and hardness tests were applied. Additionally, optical and SEM microscopy examinations and EDS element analyses were carried out in order to determine the interface properties of the joint. The work carried out showed that the highest interface strength was obtained for the specimens joined at 850 °C for 90 min. In addition, it was determined that the strength increased with increasing temperature and time until a maximum value beyond which it decreased. The hardness measurements indicated that the highest hardness value was obtained for the interlayer material and the hardness values on the both sides of the interlayer decreased gradually. Macro and microstructural examinations results revealed that the joining area (interlayer) decreased and the grain size increased with increasing temperature and time for all the specimens joined at different welding conditions. In EDS analyses, it was seen that amount of silver in the interlayer decreased markedly as weight percentage depending on the temperature rise. In addition, it also decreased slightly with increasing diffusion time. The amount of diffusion showed a decreasing trend with increasing distance from the welding interface.
Benzer Tezler
- Düşük ve orta karbonlu çeliklerin yüzeyine TIG kaynak metoduyla kaplanan ostenitik paslanmaz çelik tozunun aşınma direncine karbür içeriğinin etkisinin araştırılması
Investigation into the effect of carbide content on wear resistance of austenitic stainless steel powder coated low and medium carbon steels by TIG method
MUSTAFA SABRİ GÖK
Doktora
Türkçe
2008
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
DOÇ. DR. MEHMET H. KORKUT
- Saf titanyum (GR2) ve ferritik (430) paslanmaz çelik levhaların difüzyon kaynağı ile birleştirilmesi
Pure titanium (GR2) and ferritic (430) stainless steel plates joining by diffusion welding
AYDA SELİN YEŞİLTAŞ
Yüksek Lisans
Türkçe
2022
Makine MühendisliğiDicle ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HALUK KEJANLI
- Sıcak daldırma yöntemi ile alüminyum kaplanan düşük karbonlu çeliğe uygulanan mikro ark oksidasyon işleminin karakterizasyonu
Characterization of micro-arc oxidized unalloyed low-carbon steel after hot-dip aluminizing process
MUSTAFA AÇIKSÖZ
Yüksek Lisans
Türkçe
2017
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
- Titanyum levhaların patlamalı kaynak yöntemi ile farklı metallere birleştirilmesi ve arayüzey özelliklerinin incelenmesi
Investigation of titanium plates of different metals by explosive welding method and investigation of their interface properties
NİZAMETTİN KAHRAMAN
Doktora
Türkçe
2003
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. BEHÇET GÜLENÇ
- Yüksek mukavemetli çökelti sertleşen ferritik perlitik çeliklerde mikroalaşım elementleri ve karbon miktarının mekanik özelliklere ve mikroyapıya etkisi
The effect of microalloying elements and carbon content on mechanical properties and microstructure of high strength precipitation hardened ferritic pearlitic steels
ERSOY ERİŞİR
Doktora
Türkçe
2010
Metalurji MühendisliğiKocaeli ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. MUSTAFA ÇÖL