Determination of the particle interactions-rheology-surface roughness relationship for dental ceramics
Dental seramiklerin taneler arası ilişkiler-reoloji-yüzey pürüzlülüğü ilişkisinin belirlenmesi
- Tez No: 202152
- Danışmanlar: DOÇ. DR. HÜRRİYET POLAT
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Dental porselen, Reoloji, Yüzey pürüzlülüğü, Dental porcelain, Rheology, Surface roughness
- Yıl: 2007
- Dil: İngilizce
- Üniversite: İzmir Yüksek Teknoloji Enstitüsü
- Enstitü: Mühendislik ve Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalımada dental seramiklerin taneler arası ilikiler ? reoloji - yüzey pürüzlülüü ilikisi incelenmitir. Taneler arası ilikiler saf su ve deiik konsantrasyonlardaki (0.1, 0.25, 0.5, 0.75, 1M NaCl ve CaCl2) elektrolit çözeltileri için DLVO Teorisi kullanılarak belirlenmitir. Elde edilen veriler taneler arası ilikilerin elektrolit konsantrasyonu ve deerlii ile deitiini göstermitir. Elektrolit konsantrasyonu ve deerlii arttıkça Elektriksel Çift Tabaka (Debye Uzunluu) bastırılmakta ve Enerji Bariyer Yükseklii dümektedir bu da taneler arasında aglomerasyon olduunu göstermektedir. Saf su ve deiik konsantrasyonlardaki elektrolit çözeltilerindeki seramik toz reoloji grafikleri çizilerek sistemin reolojik özellikleri anlaılmaya çalıılmıtır. Düük elektrolit konsantrasyonlarında tanelerin aglomere olduu gözlenirken belli bir konsantrasyondan sonra dengeye ulatıı ve jellemenin olduu gözlenmitir. Reoloji ölçümlerinden elde edilen sonuçlar ile seramik yüzeylerin AFM, profilometre ve SEM ölçümleri sonucunda elde edilen sonuçlar karılatırılmı ve elektrolit ortamında yüzey pürüzlülüünün düük konsantrasyonlarda tanelerin aglomere olmasından dolayı arttıı ancak yüksek konsantrasyonlarda sistemdeki jellemeden dolayı yüzey pürüzlülüünün azaldıı belirlenmitir. Ayrıca bu durum kontak açısı ölçümleriyle de desteklenmitir. Düük elektrolit konsantrasyonlarında ortalama kontak açısı deerleri yüksek ve daılımı geni iken yüksek elektrolit konsantrasyonlarında ortalama kontak açısı deerleri düük ve daılımı dar olarak gözlemlenmitir.
Özet (Çeviri)
In this study, relationship between particle interactions, rheology and surface roughness for dental ceramics was determined. For this purpose IPS Empress 2 veneer powder was chosen and characterized with XRD, SEM, EDS, Zeta Potential and Particle Size measurements. Particle interactions have been interpreted in the light of DLVO Theory for distilled water and electrolyte solutions at different concentrations (0.1, 0.25, 0.5, 0.75, 1 M NaCl and CaCl2). The results indicated that interactions between particles change with electrolyte concentration and valency. Electrical Double Layer Thickness (Debye Length) compresses and Energy Barrier height decreases as electrolyte concentration and valency increase mean that there is agglomeration between particles. In order to understand the rheological properties of the system shear rate versus shear stress and shear rate versus viscosity graphs were interpreted for the same environmental conditions, distilled water and electrolyte solutions at different concentrations. It was obtained that at low electrolyte conditions particles formed agglomerates, however at high electrolyte conditions the system reached equilibrium where particles formed gel structures due to their non-Newtonian behaviour. The results obtained from rheological measurements were compared with the results obtained from AFM, profilometer and SEM measurements for the surfaces prepared with IPS Empress 2 veneer powder and it was concluded that in the presence of electrolytes (Na+ and Ca2+) surface roughness increased at low concentrations due to agglomeration of particles whereas surface roughness decreased at high concentrations most probably due to gelation in the system. Moreover, this situation was supported with contact angle measurements where contact angle mean values are high and ditributions are wide at low electrolyte concentrations while contact angle mean values are small and distributions are narrow at high concentrations
Benzer Tezler
- Bentonit ve montmorillonit dispersiyonlarının reolojik, viskoelastik ve kolloidal özellikleri üzerine organik ve inorganik tuzların etkisi
The effect of organic and inorganic additivies on the rheological, viscoelastic and colloidal properties of bentonite and montmorillonite dispersions
AYŞE ALEMDAR
- Bentonit dispersiyonlarına organik ve inorganik katkıların adsorbsiyonunun reolojik özellikleri üzerine etkisi
The Effect of adsorption of organic and inorganic additivies on reological properties of bentonite dispersions
SEVİM İŞÇİ
Yüksek Lisans
Türkçe
2002
Fizik ve Fizik Mühendisliğiİstanbul Teknik ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
PROF. DR. NURFER GÜNGÖR
- Determination of energy dependent total macroscopic cross-sections of different materials using the Monte Carlo method
Farklı materyallerin enerjiye bağlı toplam makroskopik tesir kesitlerinin Monte Carlo yöntemiylebelirlenmesi
DENİZ ATLI
Yüksek Lisans
İngilizce
2023
Nükleer MühendislikMarmara ÜniversitesiFizik Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TAYFUN AKYÜREK
PROF. DR. KADİR ESMER
- Effect of hydrodynamic parameters on particle-bubble interactions in flotation
Flotasyonda hidrodinamik parametrelerin tane-kabarcık üzerine etkisi
AHMAD HASSANZADEHMAHALEH
Doktora
İngilizce
2018
Maden Mühendisliği ve Madencilikİstanbul Teknik ÜniversitesiCevher Hazırlama Mühendisliği Ana Bilim Dalı
Prof. Dr. MEHMET SABRİ ÇELİK
- Determination of factors affecting the fate of microplastics in rivers
Mikroplastiklerin Nehirlerdeki davranışlarını etkileyen faktörlerin belirlenmesi
CUMANA ALPERGÜN
Yüksek Lisans
İngilizce
2025
Çevre MühendisliğiDokuz Eylül ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. NEVAL BAYCAN
PROF. DR. ORHAN GÜNDÜZ