The effect of hot-deformation on mechanical properties and age hardening characteristics of Al-Mg-Si based wrought aluminum alloys
Sıcak şekillendirmenin Al-Mg-Si bazlı işlenik alüminyum alaşımlarının mekanik özelliklerine ve yaşlanma karakteristiğine etkisi
- Tez No: 199070
- Danışmanlar: PROF. DR. BİLGEHAN ÖGEL
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Al 6xxx, ısıl işlem, sıcak-deformasyon, tane boyutu, içyapıkarakterizasyonvii, Al 6xxx, heat treatment, hot-deformation, grain size, microstructuralcharacterizationv
- Yıl: 2006
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Isıl işlem uygulanabilir Al-Mg-Si-Cu bazlı alüminyum alaşımlarının iç yapı vemekanik karakterizasyonu inceleme konusudur. Bu çalışmanın amacı; deformasyon,çözeltiye alma ve yaşlandırma gibi üretim ve ısıl işlem parametrelerinin ayarlanmasıile küçük taneli, yüksek mukavemete sahip 6066 serisi alüminyum alaşımlarınınüretimidir.İlk olarak, ön karakterizasyon amacıyla taramalı elektron mikroskopisi (SEM), enerjidağılımlı x-ışını spektroskopisi (EDS) ve çekme testleri yapılmıştır. Daha sonra,geniş kapsamlı deneysel çalışmalar iki seri numunelerle yürütülmüştür. Birinci seri,çözeltiye alma ve yaşlandırma işlemlerinin ideal koşullarının bulunması amacıyla;farklı zaman ve sıcaklıklarda çözeltiye alınmış ve yaşlandırılmış numunelerikapsamaktadır. Bu bağlamda, sertlik değişiminin ısıl işlem süresi ve sıcaklığına bağlıvideğişimi incelenmiştir. İkinci seri numuneler ise; önce dört farklı sıcaklık ve orandadövücü yardımıyla mekanik deformasyona (şekillendirme) maruz bırakılmış; dahasonra çözeltiye alınarak yaşlandırılmıştır. İşlem aralarında alınan sertlikölçümleriyle; alaşımın mekanik özelliklerindeki gelişim takip edilmiştir. Son olarak;yeniden kristallenme davranımı, çözeltiye alma işlemi öncesi ve sonrası yapılan taneboyu ölçümleriyle incelenmiştir.Ön karakterizasyon çalışmalarıyla α-Al matrisin içinde Mg2Si ve kompleks demir,mangan intermetalikleri tespit edilmiştir. Yaklaşık 140HB sertlik; optimum işlemolan 530ºC de çözeltiye alınmayı takiben 175ºC de 8 saat yaşlandırmayla eldeedilmiştir. Şekillendirme (deformasyon) düşünüldüğünde; çözeltiye alma öncesiuygulanan sıcak ya da soğuk deformasyonun mukavemet düşüşüne sebebiyet verdiğisaptanmıştır. Bu uygulamanın iyi yönü yüzde uzamadaki gelişmedir. Yapılan çalışmamukavemet kaybının yüksek sıcaklıklardaki yüksek deformasyon oranlarındaarttığını göstermiştir.
Özet (Çeviri)
Microstructural and mechanical characterizations of heat treatable Al-Mg-Si-Cubased wrought aluminum alloys have been studied. The aim of this work was toproduce fine grained, high strength alloy by adjusting processing conditions:deformation, solutionizing and aging.First, primary characterization was carried out via SEM-EDS analyses and tensiletests. Then an extensive experimental study has been carried out on two sets ofsamples. The first set has been studied to determine the ideal conditions forsolutionizing and aging processes by analyzing the variation of hardness withdifferent solutionizing and aging time and temperature. The second set, have firstbeen mechanically deformed by swaging at four different deformations and fourdifferent temperatures, then heat treated. The hardness measurements have beenivcarried out before and after solutionizing and also after aging. Finally,recrystallization behavior has been investigated by measuring grain size before andafter solutionizing treatment using image analyzer software.The initial characterizations showed that Mg2Si and complex iron, manganesebearing intermetallics were the primary particles observed in the α-Al matrix. Nearly140HB hardness could be obtained with solutionizing at 530ºC and aging at 175ºCfor 8 hours which was determined as the optimum treatment for obtaining peakhardness. When shaping (deformation) was concerned; strength loss was the overalloutcome of any hot or cold deformation before solutionizing; which was mostprobably due to the destruction of the initial microstructure. Improvement in thepercent elongation was the promising aspect of this application. Strength loss wasincreased for samples deformed at higher temperatures and higher reductions.
Benzer Tezler
- A1-%3 Li-%0.15 Zr alaşımının mekanik davranışına yaşlanmanın etkisi
The Effect of ageing on the mechanical behavior of A1-3% Li-0.15% Zr alloy
JAFAR GHAEMİ GUİVİ
- Effect of aging on the mechanical properties of boron carbide particle reinforced aluminum metal matrix composites
Bor karbür parçacık takviyeli alüminyum metal anayapılı kompozitlerin mekanik özelliklerine yaşlandırmanın etkisi
MUSTAFA SERDAR KARAKAŞ
Doktora
İngilizce
2007
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. BİLGEHAN ÖGEL
PROF. DR. RAİF ORHAN YILDIRIM
- The Effect of forging on the properties of Al-Sic composites
Al-Sic kompozitlerin özelliklerine dövmenin etkisi
İSMAİL ÖZDEMİR
- Çeliklerin ısı iletim katsayısının belirlenmesi
Determination of the thermal condictivities of the steels
BUKET YARDIMCI
- Southwire sürekli döküm yöntemi ile üretilmiş bakır çubuklardan çekilen tellerin mekanik özellikleri ve iletkenliğine oksijen ve empürite içeriğinin etkisi
The Effects of oxygen and impurity content on the mechanical properties and conductivity of the copper wires drawn from electrolytic copper rods produced by southwire continuous rod production system
CANDAN AYHAN
Yüksek Lisans
Türkçe
2002
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI