Cu ve Co katkılanmış MgB2 süperiletkenlerinin incelenmesi
Investigation of Cu and Co-doped MgB2 superconductors
- Tez No: 197064
- Danışmanlar: DOÇ.DR. AYHAN GÜLDESTE
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: MgB2 süperiletkenler, termoelektrik güç, termal iletkenlik, katıhalreaksiyon yöntemi, MgB2 superconductors, thermoelectric power, thermal conductivity, solid-state reaction method
- Yıl: 2006
- Dil: Türkçe
- Üniversite: Erciyes Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
iiiCu VE Co KATKILANMIŞ MgB2 SÜPERİLETKENLERİN İNCELENMESİİsmail DEMİRELErciyes Üniversitesi, Fen Bilimleri EnstitüsüYüksek Lisans Tezi, Mart 2006Tez Danışmanı: Doç. Dr. Ayhan GÜLDESTEÖZET(MgB2)1-xCux (x=0.0, 0.1 , 0.2 , 0.3 , 0.4 , 0.5) ve (MgB2)1-xCox (x=0.0, 0.1, 0,3, 0,5)süperiletken sistemleri katıhal reaksiyon tekniği ile hazırlanmıştır. Hazırlanannumunelerin yapısal özellikleri X-ışını toz kırınımı (XRD) tekniği ve taramalı elektronmikroskobu (SEM) ile incelenmiştir. Her iki sisteminde XRD analizi, MgB2 sistemineCu ve Co'ın eklenmesinin sırası ile MgCu2, MgB24, MgO ve MgB4, MgCo2O safsızlıkfazları ile çok fazlı bir oluşuma neden olduğunu gösterdi. Cu ve Co konsantrasyonuarttığında bu safsızlık fazlarının pik şiddeti artmaktadır. Ayrıca MgB2 içerisinde Cu veCo'ın herhangi bir kaydedilebilir çözünmesi gözlenmemiştir.Cu ve Co eklenmesiyle elektriksel özellikler büyük ölçüde etkilenmiştir. Numunelerindirencinin sıcaklık bağımlılığı Tc'ye kadar bir metalik davranış gösterdi. MgB2 içindekiCu ve Co konsantrasyonu artırıldığında, Tc ve Tc(0) değerlerinin azaldığı bulundu.Süperiletkenlik faz geçişi x=0.3 yukarısındaki Cu konsantrasyonu ve Co'ın x=0.5numunesi için tamamen kayboldu. MgB2 içerisinde Cu ve Co ilavesi ile geçişin daha dagenişlediği, saf MgB2 (x=0) için süperiletkenlik geçişlerinin keskin olduğu gözlenmiştir.Uygulanan magnetik alanın artışı ile bu geçiş daha da genişler. Termoelektrik güç S(T)değerinin bütün numuneler için pozitif bulunması hole tipi iletimin baskın olduğunugöstermektedir. Termal iletkenliğin (κ) büyüklüğü Cu ve Co konsantrasyonuartırıldığında aşağı doğru bastırıldı ve HTc sistemlerde genellikle gözlenen, Tc'ye yakınsıcaklıklarda κ(T)'nin keskin yükselişi gözlenmedi.
Özet (Çeviri)
ivINVESTIGATION OF Cu AND Co-DOPED MgB2 SUPERCONDUCTORSİsmail DEMİRELErciyes University, Graduate School of Natural and Applied SciencesM. Sc. Thesis, March 2006Thesis Supervisor: Assoc. Prof. Ayhan GÜLDESTEABSTRACTThe (MgB2)1-xCux (x=0.0, 0.1 , 0.2 , 0.3 , 0.4 , 0.5) and (MgB2)1-xCox (x=0.0, 0.1, 0,3,0,5) superconducting system were prepared by a solid-state reaction technique. Thestructural properties of prepared samples were investigated by X-Ray powderdiffraction (XRD) technique and Scanning Electron Microscopy (SEM). The XRDanalysis of both systems showed that the addition of Cu and Co into the MgB2 systemcaused a multiphase formation with impurity phases mainly MgCu2, MgB24, MgO andMgB4, MgCo2O respectively. The peak intensity of these impurity phases increasedwhen Cu and Co concentration increased. It was also not observed any detectablesolution of Cu and Co in MgB2.The electrical properties were considerably effected by addition of Cu and Co. Thetemperature dependence of resistivity of the samples showed a metallic behavior downto Tc. It was found that the Tc and Tc(0) values decreased when Cu and Co concentrationwas increased in MgB2. The superconducting phase transition completely disappearedfor the Cu concentration above x=0.3 and for the x=0.5 sample of Co. Thesuperconducting transition was obtained to be sharp for pure MgB2 (x=0) where on thetransition become broader with increasing Cu and Co addition into the MgB2. Thetransition becomes also broader with increasing the applied magnetic field. Thethermoelectric power, S(T), value was obtained to be positive for all the samples,indicating that the hole-type conducting is dominant. The magnitude of Thermalconductivity, κ, was suppressed when the Cu and Co concentration was increased andsharp rising of κ(T) at temperatures close to Tc which is often appeared in the HTcsystems was not observed.
Benzer Tezler
- Bazı manyetik malzemelerde (Cu-Co, Ti1-xCoxO2 ince filmler ve mikroteller) dev manyeto empedans incelemeleri
Giant magneto impedance investigations of some magnetic materials (Cu-Co, Ti1-xCoxO2 thin films and microwires)
FİKRET YILDIZ
Doktora
Türkçe
2004
Fizik ve Fizik MühendisliğiGebze Yüksek Teknoloji EnstitüsüFizik Ana Bilim Dalı
Y.DOÇ.DR. BULAT RAMEEV
- Değişik metal katkılanmış lityum içerme bileşiklerinin sentezi karakterizasyonu ve doldurulabilir lityum piller
Synthesis and characterization of various metal doped lithium insertion compounds and rechargeable lithium batteries
ELMAS ÖZKAN
- Elektrokimyasal depolama yoluyla elde edilen CuCo ve Cu-Co-Ni alaşım filmlerinin yapısal ve magnetorezistans özellikleri
The characterizations of structural and magnetoresistance properties of CuCo and Cu-Co-Ni alloys obtained by electrochemical deposition
İSMAİL HAKKI KARAHAN
Doktora
Türkçe
2002
Fizik ve Fizik MühendisliğiAtatürk ÜniversitesiOrtaöğretim Fen ve Matematik Alanlar Eğitimi Ana Bilim Dalı
PROF.DR. Ö. FARUK BAKKALOĞLU
- Tek çekirdekli, iki çekirdekli, üç çekirdekli, dört çekirdekli ve çok çekirdekli geçiş metalleri komplekslerinin x-ışınları kristal yapı araştırmaları
Crystal structure determination of mononuclear, dinuclear, trinuclear, tetranuclear and polynuclear transition metal complexes by x-ray diffraction techniques
CENGİZ ARICI
Doktora
Türkçe
2003
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
PROF. DR. DİNÇER ÜLKÜ
- Magnetoresistance effect CuAgCo allo films
CuAgCo alaşım filmlerinde magnetoresistans etkisi
PINAR CAN
Yüksek Lisans
İngilizce
2005
Fizik ve Fizik MühendisliğiGaziantep ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
PROF. DR. ÖMER FARUK BAKKALOĞLU