Fe-%30Ni-%XMo alaşımlarında atermal ve izotermal martensitik faz dönüşümlerinin fiziksel özelliklerinin incelenmesi
Physical properties of athermal and isothermal martensitic phase transformations in Fe-%30 Ni-%XMo alloys
- Tez No: 196779
- Danışmanlar: PROF.DR. TAHSİN NURİ DURLU
- Tez Türü: Doktora
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Austenite, Martensite, Martensitik Dönüşümler, εαâ²Martensite, Atermal Martensite, İzotermal Martensite, Manyetik Alınganlık, Mössbauer Spektrometresi, DSC, TEM, SEM.ii, Austenite, Martensite, Martensitic Transformation, εMartensite, αⲠMartensite, Athermal Martensite, Isothermal Martensite, Magnetic Susceptibility, Mössbauer Spectroscopy, DSC, TEM, SEM.iv
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZETFe-%30Ni-%XMo ALAŞIMLARINDA ATERMAL VE İZOTERMALMARTENSİTİK FAZ DÖNÜŞÜMLERİNİN FİZİKSEL ÖZELLİKLERİNİNİNCELENMESİYAŞAR, ErdemKırıkkale ÜniversitesiFen Bilimleri EnstitüsüFizik Anabilim Dalı, Doktora TeziDanışman : Prof. Dr. Tahsin Nuri DurluTEMMUZ 2005, 117 sayfaFe-%30Ni-%XMo (x=0.8, 1.8, 2.6, 3.6 ve 5) alaşımında gözlenenatermal ve izotermal özellikli martensitik faz dönüşümlerinin morfolojik,kristallografik ve manyetik özellikleri çeşitli fiziksel yöntemler kullanılarakaraştırılmıştır. Fe-%30Ni-%XMo alaşımlarında austenite fazdan martensitefaza geçiş Mo elementinin oranına bağlı olarak hem atermal hem deizotermal özellik göstermekte olup, izotermal martensitik fazın ilk oluşumu vezaman içerisinde büyümesi, oluşum esnasında Taramalı ElektronMikroskobu(SEM) ve Geçirmeli Elektron Mikroskobu(TEM) kullanılarakincelenmiştir. Austenite fazı içerisinde atermal ve izotermal olarak oluşanmartensite fazı arasında Kurdjumov-Sachs türü kristalografik dönmeibağıntısının var olduğu ve habit düzleminin {252}γ olduğu bulundu. Fe-α â² (bcc) martensite yapı ile ε (hcp)%30Ni-%XMo alaşımında gözlenenmartensite yapının Mo oranına bağlı olarak bu alaşımda oluşabileceği ilk defabu çalışmada ortaya konuldu. Oluşan ε türü martensite yapı ile austenite yapıarasında Shoji-Nishiyama türü dönme bağıntısı bulunduğu ve habitdüzleminin {111}γ olduğu sonucuna varılmıştır.Fe-%30Ni-%XMo alaşımında kristallografik faz dönüşümlerine eşlikeden bir manyetik faz geçişinin olup olmadığı AC manyetik alınganlık yöntemiile araştırılmış olup, bu malzeme için paramanyetik fazdan antiferromanyetikfaza geçiş görülmüş ve Ms sıcaklıkları bulunmuştur. Ayrıca Mössbauerspektrometresi yöntemi kullanılarak, austenite faz içerisinde oluşan atermalmartensite fazın hacim yüzdeleri bulunmuş ve austenite fazın paramanyetik,martensite fazın antiferromanyetik fazda olduğu açığa çıkarılmıştır. DSCsistemi ile alaşımın (Fe-%30Ni-%XMo, X=0.8, 1.8, 2.6) martensite başlamasıcaklığı (Ms), austenite başlama sıcaklığı (As) ve austenite bitiş sıcaklığı (Af)belirlenmiştir.
Özet (Çeviri)
ABSTRACTPHYSICAL PROPERTIES OF ATHERMAL AND ISOTHERMALMARTENSITIC PHASE TRANSFORMATIONS IN Fe-%30 Ni-%XMoALLOYSYAŞAR, ErdemKırıkkale UniversityGraduate School of Natural and Applied SciencesDepartment of Physics, Ph.D. ThesisSupervisor : Prof. Dr. Tahsin Nuri DurluJULY 2005, 117 pagesIn this study, morphologic, thermal, magnetic and crystallographicproperties of the Fe-%30Ni-%XMo (X=0.8, 1.8, 2.6, 3.6, 5) alloy, in whichathermal and isothermal phase transformations have been investigated usingvarious physical characterisation methods. In Fe-%30Ni-%XMo alloy, thetransformation of austenite phase to martensite shows both athermal andisothermal characteristics depend on the rate of Mo element. Isothermalcharacteristic formation and growth process were investigated using variousmicroscopical methods such as Scanning Electron Microscopy (SEM) andTransmission Electron Microscopy (TEM). Identical studies were also carriedout for athermal and isothermal phase transformations. It was found that thehabit plane of athermal and isothermal martensitic phase is parallel to planeiii{252}γ of austenite phase, similar to which was defined by Kurdjumov-Sachscrystallographic orientation relationships. Original results in this study, ε(hcp)martensite and α â² (bcc) martensite were observed in Fe-%30Ni-%XMo alloy.Habit plane is parallel to plane {111}γ of austenite phase similar to which wasdefined by Shoji-Nishiyama orientation relationship in Fe-%30Ni-%5Mo.An AC magnetic susceptibility method was employed in order toinvestigate a possible contribution of magnetic transiton to martensitic phasetransformations. Mössbauer spectroscopy was used to determine volumefraction of athermal martensite formed in austenite phase. As a result, unlikeaustenite, which has paramagnetic, martensitic phase showedantiferromagnetic behaviour. Finally, DSC was used to determine martenitestart temperature (Ms), austenite start temperature (As) and austenite finishtemperatures (Af) in Fe-%30Ni-%XMo (X=0.8, 1.8, 2.6) alloy.
Benzer Tezler
- Fe-%30Ni-%1Pd ve Fe-%30Ni-%1Pd-%1Mo alaşımlarının fiziksel özelliklerinin incelenmesi
The investigation of pyhsical properties of Fe-30%Ni-1%Pd and Fe-30%Ni-1%Pd-1%Mo alloys
GÖKÇEN DİKİCİ
Doktora
Türkçe
2009
Fizik ve Fizik MühendisliğiKırıkkale ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. SAFFET NEZİR
- Bazı kobalt esaslı alaşımlarda mikroyapı ve faz analizi
Microstructure and phase analysis in some cobalt-base alloys
ALEV OSMA
- High temperature wear performance of alloyed and carbide reinforced stellite 12 coatings
Alaşımlandırılmış ve karbür takviyeli stellite 12 kaplamaların yüksek sıcaklıkta aşınma davranışı
AMIR MOTALLEBZADEH
Doktora
İngilizce
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
DOÇ. DR. ERDEM ATAR
- Kendiliğinden ilerleyen yüksek sıcaklık sentezi yöntemi ile yeni ve özel alaşımların üretimi ve geliştirilmesi
Investigation of new and noble alloys productions by self-propagating high-temperature synthesis method
MURAT ALKAN
Doktora
Türkçe
2014
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
DOÇ. DR. CEVAT BORA DERİN
- Kokil ve kum kalıba döküm yöntemleriyle üretilen yüksek kromlu beyaz dökme demirlerin x-ışınları ve taramalı elektron mikroskobu çalışmalarıyla karakterize edilmesi
Characterization of high chromium white cast irons which were produced by permanent mold casting and sand casting methods by x-rays and scanning electron microscope
AKIN ODABAŞI
Yüksek Lisans
Türkçe
2004
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF.DR. NİYAZİ ERUSLU