Metaller arası bileşik MgSi takviyeli AZ91/Mg2Si kompozit malzemenin geliştirilmesi
The development of inter-metalic compound Mg2Si reinforced AZ91/Mg2Si compositive material
- Tez No: 196729
- Danışmanlar: PROF. DR. BURHANETTİN İNEM
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: In-situ, Mg2Si, Kompozit, Mikroyap0 ve MekanikÖzellikler, In-situ, Mg2Si, Composite, Microstructure andMechanical Properties
- Yıl: 2006
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
iiiMETALLER ARASI B LE K Mg2Si TAKV YELAZ91/Mg2Si KOMPOZ T MALZEMEN N GEL T R LMES(Yüksek Lisans Tezi)Ayhan DEM RGAZ ÜN VERS TESFEN B L MLER ENST TÜSÜOcak 2006ÖZETBu çal01mada, AZ91/Mg2Si in-situ kompozit malzemede Mg2Si faz0n0nmodifikasyonu üzerine kalsiyumun ve farkl0 üretim 1artlar0n0n etkisiara1t0r0lm01t0r. Dü1ük yo=unlu=a, yüksek sertlik ve elastik modülüne sahip inceve poligonal Mg2Si faz0 kompozit malzemenin mekanik özelliklerinigeli1tirmektedir. Bu nedenle Mg2Si faz0n0n morfolojisi, kalsiyum ilavesi ve/veyakat0la1ma davran010n0n kontrolü ile Çin harfi 1eklinden küçük poligonal 1ekledönü1türülmektedir. In-situ AZ91/Mg2Si kompozit malzeme s0v0 kar01t0rmayöntemi ile üretilmi1tir. Ala10m s0v0s0 haz0rland0ktan sonra kalsiyum ve dahasonra silisyum s0v0ya 670 ºC'de ilave edilmi1 ve 720 ºC'de dökümtamamlanm01t0r. Numunelerden baz0lar0, mikroyap0 ve Mg2Si faz0n0ninceltilmesi amac0yla farkl0 1artlarda üretilmi1tir. Mikroyap0 numuneleri%2'lik nital da=lay0c0s0 ile da=lanm01t0r. Mekanik test için ise test çubuklar0 vesertlik numuneleri haz0rlanm01t0r. Sonuç olarak Mg2Si faz0 nispeten poligonal1ekle dönü1türülmü1 ve böylelikle kompozitin mekanik özelliklerigeli1tirilmi1tir.Bilim Kodu : 710
Özet (Çeviri)
ivTHE DEVELOPMENT OF INTER-METALIC COMPOUND Mg2SiREINFORCED AZ91/Mg2Si COMPOSITE MATERIAL(M.Sc. Thesis)Ayhan DEMIRGAZI UNIVERSITYINSTUTE OF SCIENCE AND TECHNOLOGYJanuary 2006ABSTRACTIn this study, effect of calcium and different production conditions onmodification of Mg2Si in AZ91/Mg2Si in-situ magnesium composite wasinvestigated. Fine and polygonal Mg2Si having low density, high hardness andelastic modulus improves mechanical properties of the composites. Thereforethe morphology of Mg2Si has been changed from the Chinese script to smallpoliygonal shape through addition of calcium and/or controlling thesolidification behaivour. In-situ AZ91/Mg2Si composite was produced by meltstirring method. After preparation of the alloy, calcium and then silicon wereintroduced into the melt at 670 ºC and then cast into a special die at 720 ºC.Some of the specimens were produced in different production conditions tomodifiy the microstructure and Mg2Si. Specimens for optical microscopy andscanning electron microscopy (SEM) were etched with a solution of 2 vol. %nitric acid + ethyl alcohol. Furthermore tensile testing bars and hardnessspecimens were prepared for mechanical tests. As a result, Mg2Si was changedto relatively polygonal type, and thus mechanical properties of composite wasimproved.Sicence Code : 710
Benzer Tezler
- Alkil ftalodinitril türevlerinin sentezi ve ftalosiyaninlerinin hazırlanması
Synthesis of the alkylphthalodinitrile derivatives and phthalocyanines
HATİCE AKIN DİNÇER
Doktora
Türkçe
2005
Kimyaİstanbul Teknik ÜniversitesiDOÇ.DR. ESİN HAMURYUDAN
PROF.DR. MAKBULE BURKUT KOÇAK
- Şişe kapağı üretiminde kullanılan 8011 alüminyum alaşımının üretim süreci parametrelerinin mekanik özelliklere etkisi
Başlık çevirisi yok
ÖMER MURAT ACARŞEKİ
- Metallerarası fazların çökelme sıcaklıklarının difüzyon kaynağı üzerindeki etkilerinin araştırılması
Investigation of the precipitation temperatures of intermetallic phases on diffusion bonding
SERMİN OZAN
Doktora
Türkçe
2000
Eğitim ve ÖğretimFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
DOÇ.DR. NURİ ORHAN
- Adsorplanmış ve polimer-bağlanmış kelatlayıcı bileşikler yardımıyla ağır metal deriştirilmesi
Preconcentration of heavy metals by the aid of adsorbed and polymer-bonded chelating materials
SEMA DEMİRCİ
- Difüzyon kaynaklı TiAl-TiAl alaşımlarının içyapı ve mekanik özelliklerinin incelenmesi
Investigation into microstructure and mechanical properties of diffusion bonded TiAl-TiAl alloys
GÜVEN İPEKOĞLU
Yüksek Lisans
Türkçe
2003
Makine MühendisliğiMustafa Kemal ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. GÜREL ÇAM