Alüminyum döküm alaşımlarına Al5Ti1B ile tane inceltme işlemi uygulanması
Grain refining of aluminium foundry alloys using Al5Ti1B
- Tez No: 196612
- Danışmanlar: DOÇ. DR. FERHAT GÜL
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Teknik Eğitim, Metallurgical Engineering, Technical Education
- Anahtar Kelimeler: Al5Ti1B, Al-Si Alaşımları, Tane nceltme, DökümSıcaklığı ve Kalıp Sıcaklığı, Al5Ti1B, Al-Si Alloys, Grain Refinement, PouringTemperature and Mold TemperaturePage Number : 107Adviser : Doç. Dr. Ferhat GÜL
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ALÜM NYUM DÖKÜM ALAŞIMLARINA Al5Ti1B LE TANE NCELTMEŞLEM UYGULANMASI(Yüksek Lisans Tezi)Fatih BAYPINARGAZ ÜN VERS TESFEN B L MLER ENST TÜSÜAralık 2005ÖZETyi döküm karakteristikleri ve mekanik özellikleri, düşük çekme, yüksekkorozyon dirençi nedeni ile Al-Si alaşımları otomobil, elektrik ve havacılıkendüstrisinde yaygın olarak kullanılmaktadır. Alüminyum alaşımlarının taneinceltilmesi Al-Ti veya Al-Ti-B'a dayalı master alaşımların ilavesi ilegerçekleştirilir. Bunlar mukavemeti, sünekliği, homojenliği, katılaşma sırasındabeslemeyi geliştirmek için kullanılır. Tane inceltme sırasında elde edilen taneboyutu, tane incelticinin tipi ve miktarı, döküm sıcaklığı, kalıp sıcaklığı gibiparametrelere bağlıdır. Bu tezde Al7Si döküm alaşımlarının mekanik özellikleriüzerinde bu parametrelerin etkisi araştırılmıştır. Tane inceltme işlemi Al5Ti1Bmaster alaşımı ilavesi ile gerçekleştirilmiştir. Döküm sıcaklıkları 730,750 ve770ºC olarak seçilmiştir. Sıvı alüminyumun tane inceltmesi için %0,15 ve %0,2°olmak üzere iki farklı titanyum içeriği kullanılmıştır. Katılaşmadan sonranumunelerin yarısına T6 ısıl işlemi uygulanmıştır. Tane inceltme ve ısıl işlem ilemekanik özelliklerde önemli gelişmeler elde edilmiştir. Deneysel sonuçlaroptimum proses parametrelerini 770ºC döküm sıcaklığı, 250ºC kalıp sıcaklığı ve° °%0,2 titanyum içeriği olduğu göstermektedir.Bilim Kodu : 710.3.011
Özet (Çeviri)
GRAIN REFINING OF ALUMINIUM FOUNDRY ALLOYS USING AL5Ti1B(M.Sc. Thesis)Fatih BAYPINARGAZ UNIVERSITYINSTITUTE OF SCIENCE AND TECHNOLOGYDecember 2005ABSTRACTAl-Si alloys are widely used in automobile, electrical, aircraft industries due totheir good casting characteristics and mechanical properties, low shrinkage,high corrosion resistance. Grain refinement of aluminum alloys is usuallyachieved by an addition of master alloys based on Al-Ti or Al-Ti-B, It is used toimprove mechanical strength, ductility, homogeneity, feeding duringsolidification. The grain size obtained during grain refinement depends onnumber of parameters such as type and level of grain refiner, pouringtemperature, mould temperature. In this thesis, the effects of these parameterson the mechanical properties of Al%7 Si foundry alloys were investigated.Grain refinement was achieved by adding Al5Ti1B master alloy. The pouringtemperatures were selected as 730, 750 and 770 ËC. Two different level of 0,15and 0,2 Ti were used for grain refinement of molten aluminum. Aftersolidification, the half of specimens were applied T6 heat treatment. Significantimprovements in mechanical properties have been obtained with grain refiningand heat treatment. Experimental results show that optimum processparameters are the pouring temperature of 770 ºC, mould temperature 250 ºCand 0,2 % Ti content.Science Code : 710.3.011
Benzer Tezler
- Alüminyum tane incelticilerin toz metalurjisi ile üretimi ve döküm performansının incelenmesi
Production of aluminum grain refiners by powder metallurgy and investigation of casting performance
RAMAZAN CAN
Yüksek Lisans
Türkçe
2022
Metalurji MühendisliğiZonguldak Bülent Ecevit ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NAZIM KUNDURACI
PROF. DR. SÜLEYMAN CAN KURNAZ
- 7075 alumınyum alaşımına tane ınceltme ıslemının mekanık ozellıklerıne etkısı
Effect of grain refining process on 7075 aluminum alloy on mechanical properties
ADNAN KAHVECİ
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiZonguldak Bülent Ecevit ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. NAZIM KUNDURACI
PROF. DR. SÜLEYMAN CAN KURNAZ
- Al-4,5Cu döküm alaşımında tane inceltme işleminin etkisinin zamanla değişiminin incelenmesi
Investigation of effect of grain refinement change in time for Al-4,5Cu alloys
ZİYA TANYEL
Yüksek Lisans
Türkçe
2014
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ. DR. NEŞET AKAR
- A713 alaşımının döküm ve karakterizasyonu
Casting and characterization of A713 alloy
YEŞİM BAŞTÜRK
Yüksek Lisans
Türkçe
2019
Metalurji MühendisliğiKocaeli ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUZAFFER ZEREN
- Çift merdaneli sürekli levha döküm yöntemi ile üretilmiş AA 3003 alüminyum alaşımı levhalarda proses parametrelerinin özelliklere etkisi
Influence of process parameters on the properties of AA 3003 aluminium alloy sheets produced by continuous twin roll sheet casting method
FATİH BÜYÜKAKKAŞ