Nikel esaslı inconel 718 süper alaşımının işlenebilirliğinin incelenmesi
The review on machinability of inconel 718 nicel base super alloy
- Tez No: 196410
- Danışmanlar: PROF. DR. MUAMMER NALBANT
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Teknik Eğitim, Mechanical Engineering, Technical Education
- Anahtar Kelimeler: Süper alaşımlar, Inconel 718, kesme kuvvetleri, Takım ömrüdeneyleri, Yanak aşınması, şlenebilirlik, Super Alloys, Inconel 718, Cuttıng forces, Tool Life, FlankWear, Carbide Insert.Paper number : 207Adviser : Prof. Dr. Muammer NALBANT
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ŞLENEB L RL Ğ N N NCELENMES(Doktora Tezi)ABDULLAH ALTINGAZ ÜN VERS TESFEN B L MLER ENST TÜSÜKasım 2005ÖZETBu çalışmada, Inconel 718'in işlenmesi esnasında kesme parametrelerininkarbür ve seramik kesici takımlar için takım ömrü, kesme kuvvetleri ve yüzeypürüzlülüğü üzerindeki etkileri analiz edilerek, grafik ve resimlerleaçıklanmıştır. Silikon nitrit esaslı seramik, whisker takviyeli alüminyum oksitesaslı seramik, CVD kaplamalı sementit karbür ve kaplamasız tungsten karbürtakım kullanılarak soğutma sıvısı ortamında CNC torna tezgahında talaşkaldırılmıştır. Kesici takım üzerinde oluşan aşınmalar, kesme kuvvetleri veyüzey pürüzlülükleri ölçülmüş ve takım ömrü için yanak aşınması, bir kriterolarak ele alınmıştır. Kaplamalı karbürlerde yanak aşınması, plastikdeformasyon ve çentik, kaplamasız karbürlerde yanak aşınması ve çentik,seramik SNGN uçlarda krater ve yanak aşınması, seramik RNGN uçlarda iseyanak aşınması ve çentik aşınması daha fazla görülmüştür. Takım ömrü içinyanak aşınma alanı genişliği esas alınmıştır.2 mm'lik sabit talaş derinliği, 0.20 mm/rev.'lik sabit ilerlemede yanak aşınmaalanı genişliği, yüzey kalitesi ve asıl kesme kuvveti yönünden nconel 718' inSECO 883 RCMM kaplamasız karbür uç ile V = 45 m/min.'lik kesme hızındaelde edilen optimum değerleri sırasıyla Vbb = 0.08 mm, Ra = 0.45 µm ve FC =1149 N, KYON 4300 SNGN whisker takviyeli Al2O3+SiCw seramik uç ile V =150 m/min.'lik kesme hızında ise sırasıyla, Vbb= 0.13 mm, Ra = 1.22 µm ve FC =852 N olarak bulunmuştur.Bilim Kodu : 728
Özet (Çeviri)
THE REV EW ON MACHINABILITY OF INCONEL 718 NICEL BASESUPER ALLOY(Ph. D. Thesis)ABDULLAH ALTINGAZ UNIVERSITYINSTITUTE OF SCIENCE AND TECHNOLOGYNowember 2005ABSTRACTIn this study, analysis of tool life, cutting forces and surface roughness for themachining of Inconel 718 with carbide and ceramic cutting tools was carried outand the results were shown graphically. Metal cutting process is done withcutting floods by using Silicon nitrite based ceramic, aluminium okside basedwhisker reinforced ceramic, CVD coated cementid carbide and uncoatedtungsten carbide cutting tools in CNC machine Tool. Assuming flank wear as acriter; tool wear, cutting forces and surface roughness were measured. Flankwear, plastic deformation and notch for coated carbides; Flank wear and notchfor uncoated carbides; crater and flank wear for SNGN inserts, Flank wear andnotch wear for seramic RNG inserts were seen. Width of flank wear area wasconsidered as a main case for the tool life.Optimum values of width of flank wear area, surface roughness and maincutting force for Inconel 718 were found to be Vbb = 0.08 mm, Ra = 0.45 µm veFC = 1149 N, respectively, in 2 mm constant depth of cut, 0.20 mm/rev constantfeed rate, V = 45 m/min cutting speed and by using uncoated SECO 883RCMM carbide insert. The optimum values were found to be Vbb= 0.13 mm,Ra = 1.22 µm and FC = 852 N by using 4300 SNGN whisker reinforced cuttingtool at the cutting speed of 150 m/min.Science code : 728
Benzer Tezler
- İnconel 718 alaşımının işlenebilirliğinin kesme kuvvetleri ve yüzey pürüzlülüğü açısından değerlendirilmesi
Investigation of cutting force and surface roghness on the machinability of inconel 718 super alloy
ADNAN TAŞLIYAN
Yüksek Lisans
Türkçe
2003
Makine MühendisliğiZonguldak Karaelmas ÜniversitesiMakine Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. MUSTAFA ACARER
- Nikel esaslı süperalaşımların talaşlı işlenmesi için sialon esaslı kompozit malzemelerin geliştirilmesi
Improvement of sialon based composite materials for machining of nickel based superalloys
ALİ ÇELİK
Yüksek Lisans
Türkçe
2006
Seramik MühendisliğiAnadolu ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALPAGUT KARA
- Elektron bombardıman kaynaklı Fe-Ni esaslı inconel 718'in ısı tesiri altındaki bölgesindeki mikroçatlakların incelenmesi
Research of microfissuring in heat affected zone of welded Fe-Ni based superalloys inconel 718
MELİH CEMAL KUŞHAN
Doktora
Türkçe
1996
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF.DR. MACİT YAMAN
- Bilgisayar yardımıyla süper alaşım malzeme verileri ve tasarım kriterleri kütüphanesi oluşturulması
Başlık çevirisi yok
M.ÇAĞLAYAN TAŞÇIOĞLU
Yüksek Lisans
Türkçe
1998
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET DEMİRKOL
- Yüksek nikel alaşımlı malzemelerin vakum ortamında sert lehimlenmesine işlem parametrelerinin özelliklere etkisinin incelenmesi
The Investigation of brazing cycle, overlap distance and joint clearance parameters effect to mechanical properties for high nickel alloys during brazing under vacuum
HASAN KURŞUNGÖZ
Doktora
Türkçe
1996
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF.DR. ORHAN KOMAÇ