Ekstrüzyonla tam yoğunlaştırılmış püskürtme şekillendirme alüminyumun mekanik özelliklerinin deneysel olarak araştırılması
Experimental investigation of mechanical properties of spray formed aluminium consolidated by extrusion
- Tez No: 180406
- Danışmanlar: YRD. DOÇ. DR. İBRAHİM USLAN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Püskürtme şekillendirme, Ekstrüzyon, Mekanik özellikler, Spray forming, Extrusion, Mechanical propertiesPage Number : 56Adviser : Assist. Prof. Dr. brahim USLAN
- Yıl: 2006
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Toz metalurjisi tekniklerinden biri olan Püskürtme Şekillendirme (PŞ) ile,gözenek miktarı az, tane boyutu küçük ve yüksek mukavemetli parçalarüretilmektedir. Ekstrüzyon ise toz metal parçalarda gözenek kapatmak içinuygulanan en iyi tekniklerden biridir. Bu çalışmada aluminyumdan PŞ yöntemikullanılarak üretilen parçalar, ekstrüzyon ile tam yoğunluğa çıkarılmışlardır.PŞ işlemleri, 90-140 mm püskürtme mesafelerinde ve 5-10 bar gazatomizasyonu basınçlarında gerçekleştirilmiştir. PŞ parçalar tornalanarak 20mm çapında silindirler haline getirildikten sonra ekstrüze edilerek, 6 mmçapında çubuklar elde edilmiştir. Ekstrüze çubuklardan hazırlanan numunelereçekme testleri uygulanmıştır. Çekme testleri sonucunda ekstrüze edilmiş PŞparçaların çekme mukavemetlerinin, ekstrüze edilmiş döküm parçalara göre%10'a varan bir iyileşme gösterdiği belirlenmiştir. Ayrıca, gaz atomizasyonu vePŞ değişkenleri ile ekstrüzyon işleminin mikroyapıya etkileri ve kırılmayüzeyleri, optik ve elektron mikroskop çalışmaları yapılarak incelenmiştir.Bilim Kodu : 914.1.092
Özet (Çeviri)
Spray forming (SF) is one of the powder metallurgy techniques by which thematerials having high strength, less porosity and fine grains are produced. Onthe other hand extrusion is one of the best techniques of closing pores of metalparts. In this study spray formed ingot aluminium parts were extruded andreached full density. SF experiments were performed at distances between 90-140 mm and atomisation pressure between 5-10 bars. After machining of sprayformed preforms to cylindrical parts having 20 mm in diameter, they wereextruded to rods 6 mm in diameter. Tensile tests were applied to specimensproduced by extrusion. According to results of the tensile tests, nearly 10%improvement was observed on strength of the extruded spray formed parts incomparison to extruded as-cast parts. Furthermore, effects of the gasatomisation parameter and SF variables and the extrusion to microstructureand fracture surfaces were investigated by optical and electron microscopestudies.Science Code : 914.1.092
Benzer Tezler
- Alaşımlı alüminyum boruların MIG kaynak yöntemiyle kaynağına kaynak parametrelerinin etkisi
Effects of welding parameters to MIG ark welding of alloyed alumium tubes
ALİ UFUK NOYAN
Yüksek Lisans
Türkçe
2003
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI
- Effects of twin serew compounding conditions on the mechanical properties of nylon-6 glass fiber composites
Çift burgulu ekst-under çalışma şartlarının cam elyaf takviyeli naylon-6 karma malzemesinin mekanik özelliklerine etkisi
MURAT CANSEVER
Yüksek Lisans
İngilizce
1999
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ÜLKÜ YILMAZER
- Değişik ekstrüzyon yöntemiyle işlenmiş tam yağlı soyanın Bıldırcınların performansı üzerindeki etkileri
The effect of full-fat soybean that processed with the method of different extrusion on quails
EBRU DENİZ ÖZIŞIK
- Ekstüriziyon yöntemi ile elde edilen tam yağlı soyanın (Fulfat soya) broyler performansına etkileri
Başlık çevirisi yok
ŞERAFETTİN KAYA