Östemperlenmiş küresel grafitli dökme demirlerin aşınma davranışı
The wear behaviour of austempered ductile iron
- Tez No: 178855
- Danışmanlar: PROF.DR. AHMET AKDEMİR
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Teknik Eğitim, Engineering Sciences, Technical Education
- Anahtar Kelimeler: Asınma, Kuru sürtünme, Östemperleme, Küresel grafitli dökme demir, Aşınma, Küresel grafitli dökme demirler, Ostemperleme, Wear, Dry wear, Austempering, Ductile iron, Dry friction, Nodular graphite cast irons
- Yıl: 2007
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Östemperlenmis küresel grafitli dökme demirler mükemmel dayanım, süneklilik, asınma direnci gibi mekanik özelliklere sahip oldukları için is makinelerinde ve ulasım ekipmanlarında krank saftı, disli gibi artan sayıda mühendislik uygulamaları için kullanılmaktadır. Bu çalısmada, GGG 40 ferritik küresel grafitli dökme demirin asınma direncini iyilestirmek amacıyla farklı sıcaklıklarda östemperleme ısıl islemi yapıldı. Östemperlenmis ve döküm haldeki numunelerin asınma deneyleri, 2000 m kayma mesafesinde, 1.54 m/s sabit kayma hızında, farklı yüklerde, kuru sürtünme kosulları altında pin-disk deney setinde gerçeklestirildi. Asınma deneylerinde, döküm haldeki ve östemperlenmis numunelerin yüzey pürüzlülükleri, agırlık kayıpları ve sürtünme katsayıları ölçüldü. Asınma izleri optik mikroskop altında incelendi. Sonuç olarak; östemperleme ısıl isleminin küresel grafitli dökme demirin asınma direncini, çekme ve akma dayanımını artırdıgı tespit edildi. Mikro yapının östemperleme sıcaklıgına önemli derecede baglı oldugu, östemperleme sıcaklıgının yükselmesi ile asınma direncinin azaldıgı tespit edildi.
Özet (Çeviri)
Austempered ductile iron (ADI) has extremely good mechanical properties such as excellent fatigue and tension strength, high toughness, good wear resistance. Because of these properties, ADI has become increasingly important for the manufacturing of components of machines such as gear, crankshafts. In this work, Ductile cast iron was austempered at two different temperatures to improve of the wear resistance. The wear tests of samples from austempered and as cast irons were carried out by means of a pin on disc tester under dry atmospheric condition, 2000 m sliding distance, different normal loads, at 1,54 m/s sliding speed. Samples from austempered and as cast irons of coefficient of friction, surface roughness and weight losses were determined in the wear tests. The worn surfaces were investigated by using optic microscope. As the results of this work, It was found that the austempering heat treatment increased the wear resistance, tensile and yield strength of ductile cast iron. It was shown that austempering temperatures have an important influence on the microstructure and increasing of austempering temperature cause decreasing of wear resistance
Benzer Tezler
- Östemperlenmiş küresel grafitli dökme demirlerin aşınma davranışlarının incelenmesi
Wear behaviour of austempered ductile iron
ALİ ASLAN
Yüksek Lisans
Türkçe
2002
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. YUSUF ŞAHİN
- GGG 50 ve GGG 80 sınıfı küresel grafitli dökme demirlerin abrasiv aşınma davranışına ostemperleme işleminin etkisi
The influence of a austempering process on the abrasive wear properties of GGG 50 and GGG 80 grade ductile irons
MEHMET UMUT KÖKDEN
Yüksek Lisans
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Östemperlenmiş küresel grafitli dökme demirlerin aşınma davranışlarının geliştirilmesi
The improvement of wear behavior of austempered ductile irons
MELİK ÇETİN
- Östemperlenmiş küresel grafitli dökme demirlerin aşınma özellikleri
Wear behaviour of a ustempered ductile irons
ALİ S. TAHERY
- Küresel grafitli dökme demirlerin aşınma davranışları
Wear behaviours of ductile irons
ÖZGÜR ÇELİK
Yüksek Lisans
Türkçe
2001
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI