Sfaleritin asidik potasyum dikromatlı (K2Cr2O7) ortamda çözündürülmesi

Dissolution of sphalerite in acidic potassium dichromate (K2Cr2O7) medium

PDF İndir

  1. Tez No: 178285
  2. Yazar: İSMAİL DEDEMLİ
  3. Danışmanlar: DOÇ. DR. SALİH AYDOĞAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Maden Mühendisliği ve Madencilik, Mining Engineering and Mining
  6. Anahtar Kelimeler: Sfalerit, potasyum dikromat, sülfürik asit, liç, liç kinetiği, Sphalerite, potassium dichromate, sulphuric acid, leaching, leaching kinetics
  7. Yıl: 2008
  8. Dil: Türkçe
  9. Üniversite: Selçuk Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu tezde Sivas-Koyulhisar yöresinde bulunan Cu-Pb-Zn kompleks cevherinden flotasyon yoluyla zenginleştirilmiş sfalerit konsantresinin, sülfürik asitli ortamda potasyum dikromat etkisinde liç şartları araştırılmıştır. Araştırmalarda; karıştırma hızı (200-600 rpm), liç sıcaklığı (50-95 0C), sülfirik asit derişimi (0,5 ? 4 M), potasyumdikromat derişimi (0,01-0,15 M) ve tane boyutunun (-212 +106, -106 +75, -75 +45, -45 +38 ve -38 µm) sfaleritten çinko çözünmesine olan etkisi incelenmiştir.Elde edilen sonuçlara göre çinko çözünme hızı; karıştırma hızı, liç sıcaklığı, sülfürik asit ve potasyum dikromat derişimi arttıkça artmaktadır, tane boyutu büyüdükçede azalmaktadır. 400 rpm karıştırıcı hızında, 70 0C sıcaklığında, 2 M H2SO4 derişiminde, 0,1 M K2Cr2O7 derişiminde ve -75 + 45 µm tane boyutunda 150 dakika yapılan liç çalışması sonucu % 99,25 Zn çözünme değerine ulaşılmıştır.Çözünme mekanizmasının belirlenmesi amacıyla elde edilen çözünme değerlerine küçülen çekirdek modelleri uygulanmış ve çözünme hızının mineral yüzeyinde meydana gelen kimyasal reaksiyonla kontrol edildiği belirlenmiştir. Buradan hareketle aktivasyon enerjisi 56,21 kj/mol olarak hesaplanmıştır. Çözünme hızının H2SO4 ve K2Cr2O7 derişimlerine bağımlılığı ise sırasıyla 0,49 ([H2SO4]0,49) ve 0,28 ([K2Cr2O7]0,28) olarak belirlenmiştir.

Özet (Çeviri)

In this thesis, the leaching conditions of sphalerite (ZnS) concentrate enriched through flotation of Sivas-Koyulhisar Cu-Pb-Zn complex ore in sulphuric acid medium under effect of potassium dichromate were investigated. Effects of stirring speed in the range of 200 - 600 rpm, sulphuric acid concentration in the range of 0.5 ? 4.0 M, potassium dichromate concentration in the range of 0.01 - 0.15 M, leaching temperature in the range of 50 - 95°C, particle size fractions of -212 +106, -106 +75, -75 +45, -45 +38 and -38 µm on zinc dissolution were investigated.According to the obtained results, it was determined that the zinc dissolution rate increased with increasing stirring speed, temperature, sulphuric acid and potassium dichromate concentrations. On the other hand, it decreased with increasing particle size. The zinc dissolution of % 99,25 was obtained with following conditions: leaching time of 150 minutes, stirring speed of 400 rpm, sulphuric acid concentration of 2 M, potassium dichromate concentration of 0,1 M, leaching temperature of 70 °C, particle size of -75 + 45 µm.In order to determine the dissolution mechanism, shrinking core models were applied to the obtained dissolution values and it was determined that dissolution rate was controlled by the chemical reaction occurred on mineral surface. Activationenergy was calculated as 56.21 kJ/mol. Dependence of dissolution rate to H2SO4 and K2Cr2O7 concentrations was found as 0.49 ([H2SO4]0.49) and 0.28 ([K2Cr2O7]0.28) , respectively.

Benzer Tezler

  1. Tez No

    134158

    Koyulhisar sfalerit konsantresinin asidik ferrik klorürlü ortamda liçing şartlarının belirlenmesi

    Determination of leaching conditions of Koyulhisar sphalerite concentrate in acidic ferric chloride medium

    ALİ ARAS

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Maden Mühendisliği ve MadencilikSelçuk Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. SALİH AYDOĞAN

  2. Tez No

    139230

    Midi Zn-Pb yatağının jeolojik, mineralojik, jeokimyasal ve kökensel incelemesi (Karamustafa/Gümüşhane, Kuzeydoğu-Türkiye) KD Türkiye

    Geologic, mineralogic, geochemical and genetic studies of Midi (Karamustafa/Gümüşhane) Zn-Pb deposit, Northeast Turkey

    ABDURRAHMAN LERMİ

    Doktora

    Türkçe

    Türkçe

    2003

    Jeoloji MühendisliğiKaradeniz Teknik Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    PROF. DR. NECATİ TÜYSÜZ

  3. Tez No

    172127

    Oksit-sülfür karışımlı Pb-Zn cevherlerinin flotasyon artıklarından hidrometalurjik yöntemlerle çinko kazanılması

    Recovery of zinc from lead-zinc flotation tailings of mixed oxide-sulfide Pb-Zn ores by hydrometallurgical processes

    YILDIZ AYKAÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    Maden Mühendisliği ve Madencilikİstanbul Teknik Üniversitesi

    PROF.DR. FATMA ARSLAN

  4. Tez No

    96739

    Akoluk (Ulubay-Ordu) epitermal altın cevherleşmesinin jeolojisi, mineralojisi, hidrotermal alterasyon ve jeokimyasal özellikleri açısından incelenmesi

    Başlık çevirisi yok

    GÜLTEN YAYLALI

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Jeoloji MühendisliğiKaradeniz Teknik Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    DOÇ. DR. NECATİ TÜYSÜZ

  5. Tez No

    170974

    Istala ve Köstere (Torul-Gümüşhane) madenlerinin mineralojik ve dokusal özellikleri

    Mineralogical and textural properties of Istala and Köstere mines (Torul-Gümüşhane)

    YILMAZ DEMİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    Jeoloji MühendisliğiKaradeniz Teknik Üniversitesi

    Jeoloji Mühendisliği Ana Bilim Dalı

    PROF.DR. BURHAN SADIKLAR

Geri Dön