Polyester reçinenin bitüm ve bitümlü sıcak karışımlar üzerindeki etkilerinin araştırılması
Investigation of the effects of polyester resin on the bitumen and bitumen hot-mixes
- Tez No: 169307
- Danışmanlar: Y.DOÇ.DR. PERVİZ AHMEDZADE
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Polyester Reçine, Marshall Stabilite, İndirekt Çekme Sertlik Modülü, Statik Yüklemeli Sünme Sertliği, Fraas Kırılma Noktası, Polyester Resin, Marshall Stability, Indirekt Tensile Stiffness Modulus, Static Loading Creep Stiffness, Fraas Breaking Point. XI
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Yüksek Lisans Tezi POLYESTER REÇİNENİN BITUM VE BITUMLU SICAK KARIŞIMLAR ÜZERİNDEKİ ETKİLERİNİN ARAŞTIRILMASI Mehmet YILMAZ Fırat Üniversitesi Fen Bilimleri Enstitüsü İnşaat Mühendisliği Ana Bilim Dalı 2005, Sayfa :57 Bu çalışmada, katkı maddesi olarak kullanılan polyester reçinenin (PR) bitüm ve bitümlü sıcak karışımlar üzerindeki etkileri araştırılmıştır. AC 75/100 bitümü ve çeşitli oranlarda polyester reçine kullanılarak elde edilen karışımlar üzerinde bağlayıcı deneyleri yapılmıştır. Penetrasyon deneyi sonuçlarından, AC 100/150 bitümü ile aynı kıvamda bir bağlayıcının % 0,75 oranında PR kullanılmasıyla elde edildiği belirlenmiştir. AC 75/100, AC 100/150, AC 75/100 + % 0,75 PR bağlayıcıları kullanılan numunelerin Marshall karışım dizaynına göre optimum bağlayıcı içerikleri bulunmuştur. Optimum bağlayıcı içeriklerinde yapılan karışım numuneleri üzerinde Marshall Stabilite, indirekt çekme sertlik modülü ve statik yüklemeli sünme sertliği deneyleri yapılmıştır. Sonuç olarak AC 75/100 + % 0,75 PR katkılı bağlayıcının, karışımın stabilitesini ve indirekt çekme sertlik modülünü arttırdığı, statik yüklemeli sünme sertliğini ise azalttığı tespit edilmiştir.
Özet (Çeviri)
ABSTRACT Master Thesis INVESTİGETİON OF THE EFFECTS OF POLYESTER RESÎN ON THE BITUMEN AND BITUMEN HOT - MIXES Mehmet YILMAZ Fırat University Graduate School of Natural and Applied Science Department of Civil Engineering 2005, Page :57 In this study, polyester resin (PR) that used like additional material was investigated effects on bitumen and bitumen hot - mixes. Binder tests were done on mixes that obtained AC 75/100 and various proportion polyester resin. From obtained penetration values, AC 100/150 bitumen same class a binder was supplied from mixes that used AC 75/100 bitumen and % 0,75 ratio PR. Samples' optimum binder content that used AC 75/100, AC 100/150, AC 75/100 + % 0,75 ratio PR binders were determined according to Marshall mix design. Marshall stability, indirect tensile stiffness modulus and static loading creep stiffness tests were done on the mix samples that had optimum bitumen content. Test results have shown that AC 75/100 + % 0,75 ratio PR binder was increased Marshall stability and indirekt tensile stiffness modulus and it was reduced static loading creep stiffness.
Benzer Tezler
- Polyester esaslı elektrostatik toz boyalarda yeni bir sertleştiricinin kullanılma koşullarının incelenmesi
Examination of the conditions of use of a new hardener in polyester based thermosetting powder loatings
ÖZER ÖZALP
- İsoftalik ve tereftalik asitli modifiye doymamış polyesterlerin sentezi, stirenle kopolimerizasyonu ve karakterizasyonu
Synthesis of isophtalic and terephtalic modified unsaturated polyester resins, copolimerisation with styrene and characterisation
BİLGEHAN TUBA KAYA
- Toz plastik kaplama maddelerinin eldesi
Başlık çevirisi yok
GÜLBEYİ DURSUN
Yüksek Lisans
Türkçe
1988
Kimya MühendisliğiHacettepe ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. OKTAY BEŞKARDEŞ
- Effect of process variables on the molgg filling time in resin transfer molding
Reçine enjeksiyon kalıplama yönteminde kalıp dolum süresi üzerine bir inceleme
AYÇA ERTEKİN
Yüksek Lisans
İngilizce
1998
Polimer Bilim ve TeknolojisiOrta Doğu Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. TAYFUR ÖZTÜRK