Galvanizli çeliklerin nokta kaynağında kaplama kalınlığının kaynak dikişine ve elektrod ömrüne etkisinin araştırılması
An investigation on the effect of coating thickness on the weld nugget and electrode life in the spot welding of galvanized steels
- Tez No: 168574
- Danışmanlar: Y.DOÇ.DR. FÜSUN MÜFTÜOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Galvanizli çelik, nokta kaynağı, kaplama kalınlığı, kaynak dikişi, elektrod ömrü, Galvanized steel, spot welding, coating thickness, nugget, electrode life
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Zonguldak Karaelmas Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Yüksek Lisans Tezi GALVANİZLİ ÇELİKLERİN NOKTA KAYNAĞINDA KAPLAMA KALINLIĞININ KAYNAK DİKİŞİNE VE ELEKTROD ÖMRÜNE ETKİSİNİN ARAŞTIRILMASI Tuna KESKİNEL Zonguldak Karaelmas Üniversitesi Fen Bilimleri Enstitüsü Makine Mühendisliği Anabilim Dalı Tez Danışmanı: Yrd. Doç. Dr. Füsun MÜFTÜOĞLU Mayıs 2005, 150 sayfa Hafif ve korozyon direnci yüksek taşıtların üretiminde sıcak daldırma ile galvaniz kaplanmış ve elektrogalvaniz kaplanmış çeliklerin kullanımı giderek artmaktadır. Genellikle 5 mm' den ince parçaların birleştirilmesi için, kaplama kalınlığı 450 gr/m2'ye (65 um kalınlık) kadar kaplamalarda nokta kaynağı başarı ile uygulanmaktadır. Bu tez çalışmasında, kaplama kalınlıklarının kaynak dikişine ve elektrod ömrüne etkilerini araştırmak için kaplamasız, 100 gr/m2, 180 gr/m2 ve 275 gr/m2 kaplama kalınlıkları olan ve kimyasal kompozisyonu aynı, 1.5 mm kalınlıktaki saclar, sabit kaynak parametreleri kullanılarak nokta kaynağı yapılmıştır.Her 50 kaynak sonunda bir koparma testi numunesi hazırlanmış olup kaynak dikiş çapları ölçülmüştür. Minimum kabul edilebilir dikiş çapı olan 3Vt değerinde kaynaklar sonlandırılmıştır. Sonuç olarak kaplama kalınlığı arttıkça kaynak dikişi dayanımının ve elektrod ömrünün mÖZET (devam ediyor) azaldığı tespit edilmiştir.
Özet (Çeviri)
ABSTRACT M.Sc. Thesis AN INVESTIGATION ON THE EFFECT OF COATING THICKNESS ON THE WELD NUGGET AND ELECTRODE LIFE IN THE SPOT WELDING OF GALVANIZED STEELS Tuna KESKINEL Zonguldak Karaelmas University Graduate School of Natural and Applied Sciences Department of Mechanical Engineering Thesis Advisor: Asst. Prof. Füsun MÜFTÜO?LU May 2005, 150 pages The usege of hot dip galvanized and electrogalvanized steels in the manufacturing of vehicles with a superior corrosion resistance have been increasing. Generally, for joining steel sheets that are up to 5mm in thickness, the resistance spot welding has been successfully applied for welding steel sheets that have coating thickness of less than 450 gr/m2 (65 um thickness). In this thesis, to investigate the effect of coating thickness on the weld nugget and electrode life; 1.5 mm thickness of uncoated and galvanized steel sheets with a similar chemical compositions and different coating thicknesses (100 gr/m2, 180 gr/m2, and 275 gr/m2) have been welded with resistance spot welding using constant welding parameters. After fifty welds, a shear tests specimen have been prepared and the weld nugget diameters have been measured. This experiment has been ended when the electrode diameter has been reached a minimum acceptable value of 3Vt. vABSTRACT (continue) Consequently, it is determined that as the coating thickness increased the weld nugget strength and electrode life decreased.
Benzer Tezler
- Farklı çeliklerin elektirik direnç nokta kaynağında temas dirençlerinin bağlantının dayanımı üzerine etkisi
Başlık çevirisi yok
HALUK GAZİOĞLU
Yüksek Lisans
Türkçe
1993
Makine MühendisliğiTrakya ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. VURAL CEYHUN
- Galvanizli kromatlı mikro alaşımlı çeliklerin elektrik direnç nokta kaynağında uygun hasar modunun tespiti
Damage mode determination of electric resistance spot welding of galvanized and chrominated micro alloyed steel sheets
SALİM ASLANLAR
Doktora
Türkçe
1999
Makine MühendisliğiSakarya ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. AHMET OĞUR
- Galvanizli çelik saçların karbonlu ve ferritik paslanmaz çelikler ile nokta kaynağında kaynak parametrelerinin kaynak davranışına ve bağlantının dayanımına etkisi
The Effect of welding parameters on welding behaviour and tensile-shear strength of joints in resistance spot welding of galvanized steel sheets with carbon steel and ferritic chromium stainless stell sheets
MURAT VURAL
- Kaplı çeliklerin özellikleri
Properties of coated steels
YÜKSEL BİLİR
Yüksek Lisans
Türkçe
2004
Metalurji MühendisliğiMarmara ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF.DR. İRFAN YÜKLER
- Galvenizli çelik saçların ark kaynaklı bağlantılarının mekanik ve korozyon davranışlarının incelenmesi
Investigation of mechenical and corrosion behaviour of arc welded joints on galvanized steel sheets
C. BURAK ÖREN
Yüksek Lisans
Türkçe
1999
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. KUTSAL TÜLBENTÇİ