Silis dumanı katkılı bimsbetonların özellikleri
Properties of silica fume added pumice-concrete
- Tez No: 165923
- Danışmanlar: Y.DOÇ.DR. OSMAN ŞİMŞEK
- Tez Türü: Doktora
- Konular: Teknik Eğitim, İnşaat Mühendisliği, Technical Education, Civil Engineering
- Anahtar Kelimeler: Bimsbeton, Aderans dayanımı, Donatı korozyonu, Yüksek sıcaklık etkisi, Pumice-concrete, Bond strength, Reinforcement corrosion, High temperature effect Page Number : 164 Adviser : Assist. Prof. Dr. Osman ŞİMŞEK
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Yapı Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
SİLİS DUMANI KATKILI BIMSBETONLARIN ÖZELLİKLERİ (Doktora Tezi) Emre SANCAK GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Ocak 2005 ÖZET Doğal bîr hafif agrega olan bims agregasının, Türkiye'de geniş rezervleri bulunmaktadır. Bu çalışmada, bims agregası ile üretilen taşıyıcı bimsbeton (BB) ve normal yoğun agrega ile üretilen normal betonların (NB) karşılaştırmalı olarak: 1) betonların, içerisindeki donatıyı korozyona karşı koruma etkinliği, 2) donatı - beton kenetlenme (aderans) özellikleri ve 3) yüksek ısıya (20 °C, 100 °C, 400 °C, 800 °C, 1000 °C) maruz kaldıktan sonraki bazı fiziksel ve mekanik özellikleri araştırılmıştır. Bu amaçla, 12 farklı beton karışımı hazırlanmıştır. Silis Dumanı (SD), mineral katkı olarak % 0, % 5 ve % 10 oranlarında çimento ile ağırlıkça yer değiştirilerek kullanılmıştır. Süper akışkanlaştırıcı (SA) katkı ise betona, çimento ağırlığının % 2'si oranında katılmıştır. Sonuç olarak; BB'ların birim ağırlıktan, NB'lara göre % 23 daha düşüktür. Basınç dayanımları, SD veya SA katkıya bağlı olarak, NB'ların % 48'î ile % 65'i arasında değişen değerler almıştır. BB'larda ve NB'larda, SD ve SA katkının birlikte kullanılması ile donatı - beton aderansı artmaktadır. NB ve BB'lar, 20 °C, 100 °C ve 400 °C sıcaklıklara maruz bırakıldıklarında, NB'ların daha dayanıklı oldukları görülmüştür. Yan-hücre potansiyel verilerine göre NaCI çözeltisinde, 17 ıslatma- kurutma çevrimine maruz kalan, % 10 SD - % 2 SA'lı BB ve NB'lar, en olumlu sonucu vermişlerdir (sırasıyla; -511,2 ve -485,8). BB ve NB'larda, % 10 SD - % 2 SA'nın birlikte kullanılması durumunda, 0-10 mmderinlikte klorür miktarı sırasıyla; % 2,24 ve % 1,76 olmuştur. Donatı ağırlığında en az kayıp, % 10 SD - % 2 SA'lı BB ve NB'larda elde edilmiştir (sırası ile % 0,87 ve % 0,85). NB ve BB'larda, SD'nın tek başına kullanımı île karbonatlaşma derinliği artmıştır. En düşük karbonatlaşma derinliğini % 5 SD - % 2 SA'lı BB ve NB'lar sağlamışlardır (sırası ile 1,40 ve 1,61 mm). Bilim Kodu : 714
Özet (Çeviri)
Ill PROPERTIES OF SILICA FUME ADDED PUMICE-CONCRETE (PhD. Thesis) Emre SANCAK GAZI UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY January 2005 ABSTRACT Large deposits of Pumice, a natural lightweight aggregate, are found in Turkey. In this study, the following properties of structural concrete produced by Pumice and normal-weight aggregate are investigated: 1) the ability to protect the embedded reinforcement against corrosion, 2) the bond strength between concrete and reinforcement, and 3) compressive strength and weight loss of Concrete with Pumice Aggregate (PAC) and Normal-weight Aggregate (NAC) after being exposed to high temperatures (20, 100, 400, 800, 1000 degrees C). To achieve these objectives, 12 different types of concrete mixtures were produced. In producing the NAC and PAC mixtures, a mineral additive, Silica Fume (SF), was used to replace the Portland cement in the ratios of 0 %, 5 % and 10 % by weight. The remaining six types of mixtures were obtained by adding Super Plasticizers (SP) to the above mixtures in the ratio of 2 % by weight. In conclusion; unit weight of PAC was 23 % lower than that of NAC. When compared to NAC, compressive strength reductions in PAC were observed to change between 48 % and 65 %. Use of SF and SP together, increased the bonding between concrete and the reinforcement in both PAC and NAC. When exposed to the temperatures of 20 °C, 100 °C and 400 °C, NAC performed better thanIV the PAC. PAC containing 10 % SF- 2 % SP, exposed to 17 cycles of wetting-drying in 7 % NaCI solution, gave the most suitable results (- 511,2 and -485,8 mV respectively) according to the half -cell potential data. The use of 10 % SF- 2 % SP together in PAC and NAC, amount of C\" ion became 2,24 % and 1,76 % respectively at a depth of 0-10 mm. The minimum loss of reinforcement weight was obtained by the addition of 10 % SF- 2 % SP to PAC and NAC, which was determined as 0,87 % and 0,85 %, respectively. When SF is used alone in NAC and PAC, carbonation depth increased. The minimum carbonation depth was obtained by the addition of 5 % SF and 2 % SP to PAC and NAC, which was determined as 1,40 mm and 1,61 mm, respectively. Science Code : 714
Benzer Tezler
- Silis dumanı katkılı betonarme elemanlara klorür etkisinin hızlandırılmış korozyon deneyi ile araştırılması
Başlık çevirisi yok
NABİ YÜZER
Doktora
Türkçe
1998
İnşaat MühendisliğiYıldız Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. FEVZİYE AKÖZ
- Bentonit uçucu kül ve silis dumanı katkılı çimento enjeksiyonu uygulanan granüler zeminlerde serbest basınç mukavemetinin incelenmesi
Investigation of unconfined compressive strength of cement injection blended with bentonite fly ash and silica fume to granular soils
GÖKHAN GÜNGÖRMÜŞ
Yüksek Lisans
Türkçe
2003
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ÖZCAN TAN
- Uçucu kül ve silis dumanı katkılı yol betonlarının dayanım ve dayanıklılık özelliklerinin araştırılması
Investigation of strength and durability characteristics of cement concrete pavements with fly ash and silica fume
ENGİN YENER
Yüksek Lisans
Türkçe
2004
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
Y.DOÇ.DR. SİNAN HINISLIOĞLU
- Silis dumanlı betonların mikro yapısının incelenmesi
Micro structural analysis of concrete with silica fume
MEHMET CANBAZ
Yüksek Lisans
Türkçe
2001
İnşaat MühendisliğiEskişehir Osmangazi Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. İLKER BEKİR TOPÇU
- Korozif etkiler altında yüksek fırın cürufu ve silis dumanı katkılı yüksek dayanımlı betonların mekanik özellikleri ve dayanıklılığı
Mechanical properties and durability of high strength concrete made up of blast furnace slag and silica fume under the corrosive effect
İBRAHİM TÜRKMEN
Doktora
Türkçe
2002
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. RÜSTEM GÜL